{"id":8751,"date":"2025-06-02T03:54:02","date_gmt":"2025-06-02T03:54:02","guid":{"rendered":"https:\/\/premiumalu.com\/6065-aluminum-essential-guide-for-engineers\/"},"modified":"2026-10-08T08:00:06","modified_gmt":"2026-10-08T08:00:06","slug":"6065-hlinikova-zakladni-prirucka-pro-inzenyry","status":"publish","type":"post","link":"https:\/\/premiumalu.com\/cs\/6065-aluminum-essential-guide-for-engineers\/","title":{"rendered":"Hlin\u00edk 6065: Z\u00e1kladn\u00ed p\u0159\u00edru\u010dka pro in\u017een\u00fdry"},"content":{"rendered":"

6065 je specifikov\u00e1na pro jednu v\u011bc: l\u00e1m\u00e1n\u00ed t\u0159\u00edsky. Jde o chemii 6061 s p\u0159\u00eddavkem bismutu \u2014 nikoli o vysokopevnostn\u00ed jakost \u2014 a m\u00e1lokdy se objev\u00ed, dokud ji nejmenuje v\u00fdkres nebo o ni nepo\u017e\u00e1d\u00e1 obr\u00e1b\u011b\u010d. \u010c\u00edst ji jako vysokopevnostn\u00ed leteckou jakost je chyba, kter\u00e1 vede ke \u0161patn\u00e9 specifikaci.<\/p>\n\n\n\n

Bismut m\u011bn\u00ed to, jak se slitina obr\u00e1b\u00ed, nikoli jakou dosahuje pevnost: extrudovan\u00fd v\u00fdrobek v obou jakostech m\u00e1 stejn\u00e9 minimum T6 podle EN 755-2.<\/p>\n\n\n\n

\"6065-01-cover\"<\/figure>\n\n\n\n

Co je hlin\u00edk 6065?<\/h2>\n\n\n\n

6065 je tepeln\u011b zpracovateln\u00e1 slitina hlin\u00edk-ho\u0159\u010d\u00edk-k\u0159em\u00edk ze skupiny 6xxx. Je registrov\u00e1na jako AA\/UNS 6065 (A96065) a jako EN AW-6065 (AlMg1Bi1Si) a zpev\u0148uje se stejn\u00fdm zp\u016fsobem jako 6061 \u2014 precipitac\u00ed Mg\u2082Si b\u011bhem precipita\u010dn\u00edho vytvrzov\u00e1n\u00ed.<\/p>\n\n\n\n

Bismut je to, co z n\u00ed \u010din\u00ed samostatnou jakost nam\u00edsto varianty 6061. 6065 obsahuje 0,50\u20131,50% Bi podle EN 573-3, p\u0159id\u00e1van\u00e9ho proto, aby se t\u0159\u00edska l\u00e1mala m\u00edsto zamot\u00e1v\u00e1n\u00ed. Odstra\u0148te bismut a zb\u00fdvaj\u00edc\u00ed mezn\u00ed hodnoty prvk\u016f se velmi p\u0159ibl\u00ed\u017e\u00ed hodnot\u00e1m 6061.<\/p>\n\n\n\n

Tento jedin\u00fd p\u0159\u00eddavek ur\u010duje \u00fa\u010del specifikace. Kdy\u017e v\u00fdkres jmenuje 6065, po\u017eadavek za t\u00edm je l\u00e1m\u00e1n\u00ed t\u0159\u00edsky a jakost povrchu po obr\u00e1b\u011bn\u00ed \u2014 nikoli vy\u0161\u0161\u00ed pevnostn\u00ed t\u0159\u00edda a nikoli sva\u0159itelnost.<\/p>\n\n\n\n

Chemick\u00e9 slo\u017een\u00ed 6065<\/h2>\n\n\n\n

N\u00ed\u017ee uveden\u00e9 mezn\u00ed hodnoty jsou registrovan\u00e9 hodnoty podle EN 573-3. Pokud nab\u00eddka uv\u00e1d\u00ed jin\u00fd rozsah, zeptejte se, z jak\u00e9 normy byl p\u0159evzat.<\/p>\n\n\n\n

Prvek<\/td>Hmotnost %<\/td><\/tr>
K\u0159em\u00edk (Si)<\/td>0.40 \u2013 0.80<\/td><\/tr>
\u017delezo (Fe)<\/td>0,70 max.<\/td><\/tr>
M\u011b\u010f (Cu)<\/td>0.15 \u2013 0.40<\/td><\/tr>
Mangan (Mn)<\/td>0,15 max<\/td><\/tr>
Ho\u0159\u010d\u00edk (Mg)<\/td>0.80 \u2013 1.20<\/td><\/tr>
Chrom (Cr)<\/td>0,15 max<\/td><\/tr>
Zinek (Zn)<\/td>0,25 max.<\/td><\/tr>
Bismut (Bi)<\/strong><\/td>0.50 \u2013 1.50<\/strong><\/td><\/tr>
Titan (Ti)<\/td>0,10 max<\/td><\/tr>
Zirkonium (Zr)<\/strong><\/td>0,15 max<\/strong><\/td><\/tr>
Olovo (Pb)<\/strong><\/td>0,05 max<\/strong><\/td><\/tr>
Ostatn\u00ed, ka\u017ed\u00fd \/ celkem<\/td>0.05 \/ 0.15<\/td><\/tr>
Hlin\u00edk (Al)<\/td>Zbytek<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n

T\u0159i \u0159\u00e1dky zaji\u0161\u0165uj\u00ed odli\u0161en\u00ed od 6061. Bismut p\u0159i 0,50\u20131,50% nem\u00e1 v 6061 prot\u011bj\u0161ek, zirkonium do 0,15% rovn\u011b\u017e chyb\u00ed a chrom je omezen na 0,15% nam\u00edsto 0,04\u20130,35% u 6061. Bismut je \u0159\u00e1dek, kter\u00fd je t\u0159eba hledat na certifik\u00e1tu \u2014 tavba bez n\u011bj nen\u00ed 6065.<\/p>\n\n\n\n

\u0158\u00e1dek hlin\u00edku je zbytek, nikoli pevn\u00fd rozsah.<\/p>\n\n\n\n

Pokud certifik\u00e1t uv\u00e1d\u00ed z\u016fstatkov\u00e9 hodnoty, kter\u00e9 spadaj\u00ed mimo va\u0161i specifikaci, zeptejte se, proti jak\u00e9 norm\u011b byl list vystaven.<\/p>\n\n\n\n

Olovo je to, co odli\u0161uje 6065 od ostatn\u00edch olovnat\u00fdch voln\u011b obrobiteln\u00fdch jakost\u00ed 6xxx \u2014 mimo jin\u00e9 6262 a 6012. P\u0159i maximu 0,05% z\u016fst\u00e1v\u00e1 olovo stopov\u00fdm prvkem, nikoli leguj\u00edc\u00edm p\u0159\u00eddavkem.<\/p>\n\n\n\n

Mechanick\u00e9 vlastnosti podle zp\u016fsobu temperov\u00e1n\u00ed<\/h2>\n\n\n\n

6065 se objedn\u00e1v\u00e1 hlavn\u011b ve stavu O a T6. EN 755-2 ji tabeluje spolu s ostatn\u00edmi extrudovan\u00fdmi jakostmi 6xxx a ta\u017een\u00fd v\u00fdrobek za studena je pokryt EN 754-2.<\/p>\n\n\n\n

Temperament<\/td>Forma a \u0159\u00edd\u00edc\u00ed norma<\/td>Mez pevnosti Rm min<\/td>Smluvn\u00ed mez Rp0.2 min<\/td>Ta\u017enost A min<\/td>Ta\u017enost A50 min<\/td><\/tr>
O<\/td>\u017d\u00edhan\u00fd \u2014 \u017e\u00e1dn\u00e9 tabelovan\u00e9 minimum<\/td>\u2014<\/td>\u2014<\/td>\u2014<\/td>\u2014<\/td><\/tr>
T6<\/td>Extrudovan\u00e9 ty\u010de, pruty, trubky a profily \u2014 EN 755-2<\/td>260 MPa<\/td>240 MPa<\/td>10%<\/td>8%<\/td><\/tr>
T6<\/td>Ta\u017een\u00e9 ty\u010de, pruty a trubky za studena \u2014 EN 754-2<\/td>290 MPa<\/td>240 MPa<\/td>10%<\/td>8%<\/td><\/tr>
T8<\/td>Ta\u017een\u00e9 za studena \u2014 EN 754-2<\/td>345 MPa<\/td>315 MPa<\/td>4%<\/td>3%<\/td><\/tr>
T9<\/td>Ta\u017een\u00e9 za studena \u2014 EN 754-2<\/td>360 MPa<\/td>330 MPa<\/td>4%<\/td>3%<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n

Hodnota, podle n\u00ed\u017e je t\u0159eba navrhovat, je 260 MPa mez pevnosti a 240 MPa smluvn\u00ed mez pro extrudovan\u00fd v\u00fdrobek podle EN 755-2. Jsou to stejn\u00e1 minima, p\u0159i nich\u017e je tabelov\u00e1na 6061, tak\u017ee p\u0159echod z 6061 na 6065 nep\u0159in\u00e1\u0161\u00ed pevnost. Vy\u0161\u0161\u00ed \u010d\u00edsla T8 a T9 poch\u00e1zej\u00ed ze zpevn\u011bn\u00ed za studena podle EN 754-2, nikoli ze slitiny.<\/p>\n\n\n\n

Tlou\u0161\u0165ka pr\u016f\u0159ezu tyto mezn\u00ed hodnoty posouv\u00e1 a EN 755-2 je tabeluje podle tlou\u0161\u0165ky st\u011bny \u2014 siln\u00fd prut a tenk\u00fd profil nemaj\u00ed stejn\u00fd \u0159\u00e1dek normy. Uve\u010fte rozhoduj\u00edc\u00ed tlou\u0161\u0165ku v popt\u00e1vce a potvrd\u00edme hodnoty pro tuto tlou\u0161\u0165ku, m\u00edsto abychom citovali hlavn\u00ed \u010d\u00edslo.<\/p>\n\n\n\n

Stav O je \u017e\u00edhan\u00fd stav s maxim\u00e1ln\u00ed tva\u0159itelnost\u00ed, dod\u00e1van\u00fd s vlastnostmi deklarovan\u00fdmi na hutn\u00edm certifik\u00e1tu, nikoli stanoven\u00fdmi publikovan\u00fdm minimem. Pokud je d\u00edl p\u0159ed nasazen\u00edm do provozn\u00edho zat\u00ed\u017een\u00ed oh\u00fdb\u00e1n nebo tv\u00e1\u0159en, tv\u00e1\u0159\u00ed se ve stavu O a tepeln\u011b se zpracov\u00e1v\u00e1 a\u017e pot\u00e9; tv\u00e1\u0159en\u00ed po vytvrzen\u00ed je omezen\u00e9.<\/p>\n\n\n\n

Obrobitelnost: Co bismut p\u0159in\u00e1\u0161\u00ed<\/h2>\n\n\n\n
\"6065-04-machined-parts\"<\/figure>\n\n\n\n

Bismut hlin\u00edk nezpev\u0148uje. V tavenin\u011b vytv\u00e1\u0159\u00ed diskr\u00e9tn\u00ed n\u00edzko taviteln\u00e9 \u010d\u00e1stice a tyto \u010d\u00e1stice l\u00e1mou t\u0159\u00edsku p\u0159i pr\u016fchodu n\u00e1stroje, tak\u017ee odpad odch\u00e1z\u00ed kr\u00e1tk\u00fd, m\u00edsto aby se vinul kolem n\u00e1stroje a obrobku.<\/p>\n\n\n\n

Na jednoduch\u00e9m d\u00edlu se tento rozd\u00edl sotva projev\u00ed. U dlouhodob\u011b b\u011b\u017e\u00edc\u00ed zak\u00e1zky, hlubok\u00e9 kapsy nebo p\u0159\u00edsn\u00e9ho po\u017eadavku na jakost povrchu se projev\u00ed jako \u017eivotnost n\u00e1stroje, m\u00edra zmetkovitosti a \u010das obsluhy str\u00e1ven\u00fd odstra\u0148ov\u00e1n\u00edm t\u0159\u00edsky. To je cel\u00fd obchodn\u00ed d\u016fvod pro p\u0159echod d\u00edlu z 6061 na 6065.<\/p>\n\n\n\n

V\u016f\u010di 6262 je rozhoduj\u00edc\u00edm \u0159\u00e1dkem olovo. 6262 pou\u017e\u00edv\u00e1 0,4\u20130,7% olova vedle sv\u00e9ho bismutu; 6065 dr\u017e\u00ed olovo na maximu 0,05%. Pokud kone\u010dn\u00fd v\u00fdrobek nebo specifikace z\u00e1kazn\u00edka omezuje obsah olova, tento jedin\u00fd \u0159\u00e1dek rozhoduje o tom, kter\u00e1 ze dvou jakost\u00ed je pou\u017eiteln\u00e1.<\/p>\n\n\n\n

Obr\u00e1b\u011bc\u00ed p\u0159\u00ednos n\u00e1le\u017e\u00ed vytvrzen\u00fdm stav\u016fm. Ve stavu O je slitina m\u011bkk\u00e1 a ta\u017en\u00e1, co\u017e je pro l\u00e1m\u00e1n\u00ed t\u0159\u00edsky nespr\u00e1vn\u00fd stav \u2014 O je stav pro tv\u00e1\u0159en\u00ed a obr\u00e1b\u011bn\u00ed obvykle prob\u00edh\u00e1 po vytvrzen\u00ed.<\/p>\n\n\n\n

Sva\u0159ov\u00e1n\u00ed, tv\u00e1\u0159en\u00ed a povrchov\u00e9 \u00fapravy<\/h2>\n\n\n\n

6065 je jakost pro obr\u00e1b\u011bn\u00ed, nikoli pro sva\u0159ov\u00e1n\u00ed. Tyt\u00e9\u017e \u010d\u00e1stice bismutu, kter\u00e9 l\u00e1mou t\u0159\u00edsku, vstupuj\u00ed tak\u00e9 do svarov\u00e9 l\u00e1zn\u011b a voln\u011b obrobiteln\u00e9 jakosti 6xxx se sva\u0159uj\u00ed \u0161patn\u011b. Postup kvalifikovan\u00fd na 6061 se nep\u0159en\u00e1\u0161\u00ed a u spoje 6065 nelze p\u0159edpokl\u00e1dat, \u017ee dos\u00e1hne vlastnost\u00ed z\u00e1kladn\u00edho materi\u00e1lu.<\/p>\n\n\n\n

Pokud konstrukce vy\u017eaduje jak obr\u00e1b\u011bn\u00fd detail, tak sva\u0159ovanou strukturu, obvykl\u00e9 rozd\u011blen\u00ed je 6061 nebo 5083 pro sva\u0159ovan\u00e9 \u010dleny. Pokud mus\u00ed b\u00fdt d\u00edl z 6065 sva\u0159ov\u00e1n, kvalifikujte postup na skute\u010dn\u011b dod\u00e1van\u00e9 slitin\u011b a stavu, m\u00edsto abyste roz\u0161i\u0159ovali st\u00e1vaj\u00edc\u00ed postup.<\/p>\n\n\n\n

Tv\u00e1\u0159en\u00ed je ve stavu O p\u0159\u00edmo\u010dar\u00e9, co\u017e \u010din\u00ed \u017e\u00edhan\u00fd polotovar b\u011b\u017en\u00fdm vstupem pro d\u00edly oh\u00fdban\u00e9 p\u0159ed vytvrzen\u00edm. Eloxov\u00e1n\u00ed i le\u0161t\u011bn\u00ed jsou u 6065 podporov\u00e1ny; p\u0159ed uvoln\u011bn\u00edm d\u00edlu potvr\u010fte t\u0159\u00eddu povrchov\u00e9 \u00fapravy a p\u0159\u00edpadn\u00fd po\u017eadavek na shodu barev proti vzorku.<\/p>\n\n\n\n

Jak si 6065 stoj\u00ed ve srovn\u00e1n\u00ed s 6061<\/h2>\n\n\n\n
\"6065-03-6061-comparison\"<\/figure>\n\n\n\n
Majetek<\/td>EN AW-6065<\/td>EN AW-6061<\/td><\/tr>
Registrovan\u00fd n\u00e1zev<\/td>AlMg1Bi1Si<\/td>AlMg1SiCu<\/td><\/tr>
Bismut<\/td>0.50 \u2013 1.50%<\/td>nen\u00ed p\u0159\u00edtomen<\/td><\/tr>
Zirkonium<\/td>0,15% max<\/td>nen\u00ed p\u0159\u00edtomen<\/td><\/tr>
Chrom<\/td>0,15% max<\/td>0.04 \u2013 0.35%<\/td><\/tr>
Minimum T6, extrudov\u00e1no (EN 755-2)<\/td>Rm \u2265 260 MPa, Rp0.2 \u2265 240 MPa<\/td>Rm \u2265 260 MPa, Rp0.2 \u2265 240 MPa<\/td><\/tr>
Chov\u00e1n\u00ed p\u0159i obr\u00e1b\u011bn\u00ed<\/td>Voln\u011b obrobiteln\u00e9; bismut l\u00e1me t\u0159\u00edsku<\/td>Obecn\u00e9 obr\u00e1b\u011bn\u00ed<\/td><\/tr>
Sva\u0159ov\u00e1n\u00ed<\/td>Nen\u00ed jakost pro sva\u0159ov\u00e1n\u00ed<\/td>Snadno sva\u0159iteln\u00e9<\/td><\/tr>
Co rozhoduje o volb\u011b<\/td>\u0158\u00edzen\u00ed t\u0159\u00edsky a jakost povrchu po obr\u00e1b\u011bn\u00ed<\/td>Dostupnost, sva\u0159itelnost, cena<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n

Zvolte 6065 pouze tehdy, kdy\u017e je \u0159\u00edzen\u00ed t\u0159\u00edsky nebo jakost povrchu \u00fazk\u00fdm m\u00edstem.<\/p>\n\n\n\n

Pokud se ve v\u00fdrobn\u00edm postupu objev\u00ed sva\u0159ov\u00e1n\u00ed, z\u016fsta\u0148te u 6061<\/a>. Pokud je sou\u010d\u00e1st\u00ed obr\u00e1b\u011bn\u00fd detail uvnit\u0159 sva\u0159ovan\u00e9ho celku, rozd\u011blte oboj\u00ed: 6061 pro sva\u0159ovan\u00e9 prvky, 6065 pro d\u00edly \u0159ezan\u00e9 z pln\u00e9ho materi\u00e1lu.<\/p>\n\n\n\n

Ani jedna z t\u011bchto jakost\u00ed nen\u00ed n\u00e1mo\u0159n\u00ed slitinou v tom smyslu, \u017ee 5083<\/a> nebo 5052 jsou. Pro trval\u00e9 pono\u0159en\u00ed nebo silnou expozici chlorid\u016fm z\u016fst\u00e1vaj\u00ed jakosti 5xxx bezpe\u010dn\u011bj\u0161\u00edm v\u00fdchoz\u00edm bodem.<\/p>\n\n\n\n

Kde se 6065 pou\u017e\u00edv\u00e1<\/h2>\n\n\n\n