{"id":8577,"date":"2025-04-14T15:05:30","date_gmt":"2025-04-14T15:05:30","guid":{"rendered":"https:\/\/premiumalu.com\/?post_type=product&p=8577"},"modified":"2026-07-08T15:01:17","modified_gmt":"2026-07-08T15:01:17","slug":"6065-aluminiumlegierung","status":"publish","type":"product","link":"https:\/\/premiumalu.com\/de\/produkt\/6065-aluminiumlegierung\/","title":{"rendered":"6065 Aluminium-Legierung"},"content":{"rendered":"

What Is 6065 Aluminum Alloy?<\/h2>\n

6065 aluminum is a heat-treatable 6000-series alloy built on the magnesium-silicon base with bismuth added for improved machinability. It balances moderate strength, corrosion resistance, and good chip control during machining, which suits structural and industrial components. Linsy supplies 6065 in O and T6 tempers across sheet, tube, bar, and wire.<\/p>\n

Available 6065 Aluminum Products<\/h2>\n

6065 Aluminum Sheet & Coil<\/h3>\n\n\n\n\n
Formular<\/th>\nTemperament<\/th>\nDicke (mm)<\/th>\nBreite (mm)<\/th>\nL\u00e4nge (mm)<\/th>\n<\/tr>\n
Sheet \/ Coil<\/td>\nO, T6<\/td>\n0.5 – 200<\/td>\n500 – 2600<\/td>\n500 – 12000<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

6065 Aluminum Tube<\/h3>\n\n\n\n\n
Formular<\/th>\nTemperament<\/th>\nAu\u00dfen (mm)<\/th>\nWand (mm)<\/th>\nL\u00e4nge (mm)<\/th>\n<\/tr>\n
Rohr<\/td>\nO, T6<\/td>\n6 – 400<\/td>\n0.5 – 40<\/td>\n1000 – 12000<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

6065 Aluminum Bar<\/h3>\n\n\n\n\n
Formular<\/th>\nTemperament<\/th>\nDurchmesser (mm)<\/th>\nL\u00e4nge (mm)<\/th>\n<\/tr>\n
Bar (round \/ square \/ flat)<\/td>\nO, T6<\/td>\n6 – 400<\/td>\n1000 – 12000<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

6065 Aluminum Wire<\/h3>\n\n\n\n\n
Formular<\/th>\nTemperament<\/th>\nDurchmesser (mm)<\/th>\nGewicht der Spule<\/th>\n<\/tr>\n
Wire \/ Rod<\/td>\nO, T6<\/td>\n0.8 – 30<\/td>\nmin 50 kg per coil<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Dimensions can be customized. Share your required form, temper, and size and we will confirm feasibility and tolerance.<\/p>\n

Technische Daten und gleichwertige Bezeichnungen<\/h2>\n\n\n\n\n\n\n
Standard<\/th>\nBezeichnung<\/th>\n<\/tr>\n
AA \/ UNS<\/td>\n6065 \/ A96065<\/td>\n<\/tr>\n
DE<\/td>\nEN AW-6065 (AlMg1Bi1Si)<\/td>\n<\/tr>\n
\u00dcbliche H\u00e4rtegrade<\/td>\nO, T6<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Chemische Zusammensetzung<\/h2>\n

Typical composition of 6065 is listed below. Bismuth is added to support machining; exact limits should be confirmed against the ordered specification.<\/p>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
Element<\/th>\nZusammensetzung (Gew.-%)<\/th>\n<\/tr>\n
Si<\/td>\n0.40 – 0.90<\/td>\n<\/tr>\n
Fe<\/td>\n0,70 max.<\/td>\n<\/tr>\n
Cu<\/td>\n0,15 \u2013 0,40<\/td>\n<\/tr>\n
Mn<\/td>\n0,15 max<\/td>\n<\/tr>\n
Mg<\/td>\n0,80 \u2013 1,20<\/td>\n<\/tr>\n
Cr<\/td>\n0,15 max<\/td>\n<\/tr>\n
Zn<\/td>\n0,25 max<\/td>\n<\/tr>\n
Bi<\/td>\n0.40 – 0.70 (typical)<\/td>\n<\/tr>\n
Ti<\/td>\n0,10 max<\/td>\n<\/tr>\n
Sonstige (jeweils)<\/td>\n0,05 max<\/td>\n<\/tr>\n
Sonstige (insgesamt)<\/td>\n0,15 max<\/td>\n<\/tr>\n
Al<\/td>\nRestbetrag<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Mechanische Eigenschaften je nach Temperierung<\/h2>\n

Values below are typical reference ranges; actual results vary with section thickness and temper. T6 figures are taken from the supplied specification, while O values are typical annealed references to be confirmed.<\/p>\n\n\n\n\n\n
Temperament<\/th>\nZugfestigkeit (MPa)<\/th>\nStreckgrenze (MPa)<\/th>\nBruchdehnung (%, min)<\/th>\n<\/tr>\n
O<\/td>\n~120<\/td>\n~70<\/td>\n~18<\/td>\n<\/tr>\n
T6<\/td>\n260 – 310<\/td>\n~240<\/td>\n10 – 11<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Shear strength for T6 is around 190 MPa.<\/p>\n

Leitfaden zur Auswahl der H\u00e4rtung<\/h2>\n

O<\/strong> (annealed) gives maximum formability and is chosen where the part is bent or formed before any service load. T6<\/strong> is the aged temper that delivers the strength and stability needed for structural and machined parts. Select T6 for load-bearing use and O where forming dominates.<\/p>\n

Wesentliche Merkmale<\/h2>\n

Balanced Strength & Machinability<\/h3>\n

6065 offers a useful strength level while the bismuth addition keeps chips manageable during machining.<\/p>\n

Korrosionsbest\u00e4ndigkeit<\/h3>\n

As a 6000-series alloy it resists corrosion well in normal atmospheric and industrial environments.<\/p>\n

Umformbarkeit und Schwei\u00dfbarkeit<\/h3>\n

In the O temper the alloy forms readily; it welds with standard methods, with some local softening in the heat-affected zone.<\/p>\n

Anwendungen<\/h2>\n