{"id":8918,"date":"2025-07-19T06:50:22","date_gmt":"2025-07-19T06:50:22","guid":{"rendered":"https:\/\/premiumalu.com\/?post_type=product&p=8918"},"modified":"2026-07-08T15:01:14","modified_gmt":"2026-07-08T15:01:14","slug":"aleacion-de-aluminio-5657","status":"publish","type":"product","link":"https:\/\/premiumalu.com\/es\/producto\/aleacion-de-aluminio-5657\/","title":{"rendered":"5657 Aleaci\u00f3n de aluminio"},"content":{"rendered":"

What Is 5657 Aluminum?<\/h2>\n

5657 is a non-heat-treatable 5xxx alloy with about 1 percent magnesium, developed for high-quality anodized surfaces. It provides an excellent anodizing response, good corrosion resistance, and moderate strength, and is widely used for decorative and architectural finishes.<\/p>\n

Available 5657 Aluminum Products<\/h2>\n

Linsy supplies 5657 mainly as sheet and coil for anodized decorative finishes, with bar and profiles available on request. The tempers most commonly supplied are O, H25, H28, and H38<\/strong>. Las dimensiones a continuaci\u00f3n son rangos t\u00edpicos; otros tama\u00f1os pueden consultarse bajo solicitud.<\/p>\n

Chapa y Bobina<\/h3>\n

5657 is supplied primarily as thin-gauge sheet and coil in thicknesses from 0.3 mm to 4 mm, widths up to 2000 mm, and lengths up to 6000 mm or cut to size.<\/p>\n

Placa<\/h3>\n

Thick plate is not a standard 5657 product; thin rolled coil and sheet are the typical forms. Other gauges can be discussed on request.<\/p>\n

Barra (Redonda, Plana, Cuadrada)<\/h3>\n

Round, flat, and square bars can be produced in diameters or side lengths from 6 mm to 200 mm, normally in O or H25.<\/p>\n

Tubo y Tuber\u00eda<\/h3>\n

5657 tube can be supplied in outer diameters from 6 mm to 200 mm with wall thicknesses from 0.5 mm to 20 mm, usually in O or H25 temper.<\/p>\n

Perfil Extruido<\/h3>\n

Extruded and drawn profiles for trim are available on request.<\/p>\n

Especificaciones y denominaciones equivalentes<\/h2>\n

5657 is identified by the following common standards and designations.<\/p>\n\n\n\n\n\n\n\n
Est\u00e1ndar<\/th>\nDenominaci\u00f3n<\/th>\n<\/tr>\n<\/thead>\n
AA<\/td>\n5657<\/td>\n<\/tr>\n
UNS<\/td>\nA95657<\/td>\n<\/tr>\n
EN AW<\/td>\nEN AW-AlMg1<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Composici\u00f3n qu\u00edmica<\/h2>\n

The typical composition of 5657 aluminum is listed below in weight percent, with aluminum as the balance.<\/p>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
Elemento<\/th>\nComposici\u00f3n (%)<\/th>\n<\/tr>\n<\/thead>\n
Silicio (Si)<\/td>\n0,25 m\u00e1x.<\/td>\n<\/tr>\n
Hierro (Fe)<\/td>\n0.40 m\u00e1x.<\/td>\n<\/tr>\n
Cobre (Cu)<\/td>\n0,10 m\u00e1x.<\/td>\n<\/tr>\n
Manganeso (Mn)<\/td>\n0.15 – 0.35<\/td>\n<\/tr>\n
Magnesio (Mg)<\/td>\n0,8 \u2013 1,2<\/td>\n<\/tr>\n
Cromo (Cr)<\/td>\n0,05 m\u00e1x.<\/td>\n<\/tr>\n
Zinc (Zn)<\/td>\n0,10 m\u00e1x.<\/td>\n<\/tr>\n
Titanio (Ti)<\/td>\n0.03 max<\/td>\n<\/tr>\n
Otros cada uno<\/td>\n0.05<\/td>\n<\/tr>\n
Otros total<\/td>\n0.15<\/td>\n<\/tr>\n
Aluminio (Al)<\/td>\nSaldo<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Propiedades mec\u00e1nicas seg\u00fan el estado de templado<\/h2>\n

Los valores a continuaci\u00f3n son t\u00edpicos para productos laminados y extruidos y deben confirmarse con el certificado de prueba del molino para el temple y espesor espec\u00edficos solicitados.<\/p>\n\n\n\n\n\n\n\n\n
Temple<\/th>\nResistencia a la tracci\u00f3n (MPa)<\/th>\nL\u00edmite el\u00e1stico (MPa)<\/th>\nAlargamiento (%)<\/th>\n<\/tr>\n<\/thead>\n
O<\/td>\n115 – 160<\/td>\n45 min<\/td>\n18<\/td>\n<\/tr>\n
H25<\/td>\n180 – 220<\/td>\n150 min<\/td>\n8<\/td>\n<\/tr>\n
H28<\/td>\n215 – 260<\/td>\n180 min<\/td>\n5<\/td>\n<\/tr>\n
H38<\/td>\n230 – 270<\/td>\n200 min<\/td>\n4<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Gu\u00eda para la selecci\u00f3n del temple<\/h2>\n

Choose O or H25 for bright decorative trim that is formed before anodizing; H28 and H38 give higher strength for anodized parts that are not heavily formed.<\/p>\n

Caracter\u00edsticas principales<\/h2>\n

Anodizing response<\/h3>\n

5657 is valued for a clear, consistent, and attractive anodized finish, its main selection reason.<\/p>\n

Resistencia a la corrosi\u00f3n<\/h3>\n

Corrosion behavior is good for interior and architectural exposure.<\/p>\n

Formabilidad<\/h3>\n

In O and H25 tempers it forms and bends well for panels and trim.<\/p>\n

Fuerza<\/h3>\n

Strength is moderate; the grade is chosen for appearance more than load capacity.<\/p>\n

Aplicaciones<\/h2>\n