8009 is a powder-metallurgy-derived dispersion-strengthened alloy whose strength comes from a uniform dispersion of thermally stable Al–Fe–Si–V intermetallics. Unlike 2xxx\/7xxx alloys, its strength does not collapse at moderately high service temperatures, making it attractive for aerospace and engine-adjacent structural parts. It is not a lithium-bearing alloy; its chemistry is iron–silicon–vanadium based.<\/p>\n
Typische productiebereiken worden hieronder vermeld; aangepaste afmetingen zijn op aanvraag verkrijgbaar.<\/p>\n
| Formulier<\/th>\n | Temper<\/th>\n | Afmeting<\/th>\n | Bereik<\/th>\n | Opmerking<\/th>\n<\/tr>\n<\/thead>\n | ||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Plaat & Coil<\/td>\n | O, T6, T8<\/td>\n | Dikte<\/td>\n | 0.5 – 100 mm<\/td>\n | Custom widths\/lengths<\/td>\n<\/tr>\n | ||||||||||||||||||||||||||||||||||||||||||||
| Plaat<\/td>\n | O, T6, T8<\/td>\n | Dikte<\/td>\n | 6 \u2013 150 mm<\/td>\n | Quarto<\/td>\n<\/tr>\n | ||||||||||||||||||||||||||||||||||||||||||||
| Ronde Staaf<\/td>\n | O, T6, T8<\/td>\n | Diameter<\/td>\n | 6 – 300 mm<\/td>\n | Op maat gezaagd<\/td>\n<\/tr>\n | ||||||||||||||||||||||||||||||||||||||||||||
| Buis<\/td>\n | O, T6, T8<\/td>\n | Buitendiameter<\/td>\n | 10 – 300 mm<\/td>\n | Wall 1 – 30 mm<\/td>\n<\/tr>\n | ||||||||||||||||||||||||||||||||||||||||||||
| Draad<\/td>\n | O, T6, T8<\/td>\n | Diameter<\/td>\n | 0,8 \u2013 30 mm<\/td>\n | Coil weight ≥ 50 kg<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n8009 Specifications & Equivalent Designations<\/h2>\nChemical Composition of 8009 Aluminum<\/h2>\n
|
The dispersed intermetallics resist coarsening, so strength holds up better than age-hardened alloys at elevated temperature.<\/p>\n
Good fatigue performance supports rotating and cyclic-load aerospace components.<\/p>\n
Generally good corrosion resistance; welding is possible but reduces the dispersion-strengthened benefit — confirm with engineering for critical parts.<\/p>\n
8009 machines comparably to other high-strength aluminum grades. Because its strength derives from dispersion rather than precipitation, prolonged exposure above roughly 200–250°C should be reviewed with engineering. Standard anodizing and polishing are applicable.<\/p>\n
Elke zending gaat vergezeld van een MTC-rapport met details over chemische samenstelling en mechanische testresultaten. Inspectie door derden en SGS-testrapporten kunnen op aanvraag worden geregeld. Inkomende en uitgaande inspectie omvat afmetingen, oppervlakteconditie en mechanische eigenschappen.<\/p>\n
Linsy heeft een productiebasis in Shenzhen met meer dan 20 jaar ervaring in aluminiumproductie en levert legeringen uit de 1000\u20138000-serie aan wereldwijde B2B-kopers. Wij ondersteunen aangepaste afmetingen, uitvoeringen en verwerking voor zowel prototype- als productievolumes.<\/p>\n
Technische handleidingen en specificatiereferenties ondersteunen de selectie van legeringen en het ontwerp. De onderstaande externe links zijn bedoeld als achtergrondinformatie en dienen v\u00f3\u00f3r publicatie te worden vervangen door eigen inhoud van Linsy (v\u00f3\u00f3r gebruik verifi\u00ebren).<\/p>\n