{"id":9037,"date":"2025-09-01T01:57:32","date_gmt":"2025-09-01T01:57:32","guid":{"rendered":"https:\/\/premiumalu.com\/?post_type=product&p=9037"},"modified":"2026-07-08T15:01:14","modified_gmt":"2026-07-08T15:01:14","slug":"aluminiowy-pret-kwadratowy-6063","status":"publish","type":"product","link":"https:\/\/premiumalu.com\/pl\/produkt\/aluminiowy-pret-kwadratowy-6063\/","title":{"rendered":"Aluminiowy pr\u0119t kwadratowy 6063-T5\/T52\/T6"},"content":{"rendered":"

What Is 6063 Aluminum Square Bar?<\/h2>\n

6063 aluminum square bar is a medium-strength, heat-treatable extruded profile often called architectural aluminum. It combines a smooth, anodize-friendly surface with good corrosion resistance and straightforward machinability, which makes it a common choice for visible structural parts such as frames, trims, and fittings. Linsy supplies 6063 square bar in T5 and T6 tempers, cut to the lengths your project requires.<\/p>\n

Available 6063 Aluminum Products<\/h2>\n

Aluminiowy pr\u0119t kwadratowy 6063<\/h3>\n\n\n\n\n
Formularz<\/th>\nTemperament<\/th>\nSide (mm)<\/th>\nD\u0142ugo\u015b\u0107 (mm)<\/th>\n<\/tr>\n
Kwadratowy pasek<\/td>\nT5, T6<\/td>\n8 – 150<\/td>\n1000 – 6000 (custom cut)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Dimensions can be customized. Tell us the side length, temper, and required length and we will confirm feasibility and tolerance.<\/p>\n

Other 6063 Forms<\/h3>\n

Square bar is one of several 6063 shapes we supply. Related forms include 6063 square tube, flat bar, round bar, and round tube, each available in T5\/T6 with custom dimensions.<\/p>\n

Dane techniczne i odpowiedniki oznacze\u0144<\/h2>\n\n\n\n\n\n\n
Standard<\/th>\nOznaczenie<\/th>\n<\/tr>\n
AA \/ UNS<\/td>\n6063 \/ A96063<\/td>\n<\/tr>\n
PL<\/td>\nEN AW-6063 (AlMg0.5Si)<\/td>\n<\/tr>\n
Typowe stany<\/td>\nT5, T6 (also O, T4, T52)<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Sk\u0142ad chemiczny<\/h2>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
Element<\/th>\nSk\u0142ad (% wag.)<\/th>\n<\/tr>\n
Si<\/td>\n0.20 – 0.60<\/td>\n<\/tr>\n
Fe<\/td>\n0.35 max<\/td>\n<\/tr>\n
Cu<\/td>\n0,10 maks<\/td>\n<\/tr>\n
Mn<\/td>\n0,10 maks<\/td>\n<\/tr>\n
Mg<\/td>\n0.45 – 0.90<\/td>\n<\/tr>\n
Cr<\/td>\n0,10 maks<\/td>\n<\/tr>\n
Zn<\/td>\n0,10 maks<\/td>\n<\/tr>\n
Ti<\/td>\n0,10 maks<\/td>\n<\/tr>\n
Inni (ka\u017cdy)<\/td>\n0.05 max<\/td>\n<\/tr>\n
Inne (\u0142\u0105cznie)<\/td>\n0,15 maks<\/td>\n<\/tr>\n
Al<\/td>\nReszta<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

W\u0142a\u015bciwo\u015bci mechaniczne w zale\u017cno\u015bci od stanu utwardzenia<\/h2>\n

Values below are typical for 6063 and reflect standard AA reference ranges. Actual results vary with section thickness and temper.<\/p>\n\n\n\n\n\n\n\n\n
Temperament<\/th>\nWytrzyma\u0142o\u015b\u0107 na rozci\u0105ganie (MPa)<\/th>\nGranica plastyczno\u015bci (MPa)<\/th>\nWyd\u0142u\u017cenie (%, min.)<\/th>\n<\/tr>\n
O<\/td>\n90<\/td>\n55<\/td>\n25<\/td>\n<\/tr>\n
T4<\/td>\n150<\/td>\n90<\/td>\n20<\/td>\n<\/tr>\n
T5<\/td>\n185<\/td>\n145<\/td>\n12<\/td>\n<\/tr>\n
T52<\/td>\n185<\/td>\n130<\/td>\n12<\/td>\n<\/tr>\n
T6<\/td>\n240<\/td>\n215<\/td>\n12<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Przewodnik po doborze hartowania<\/h2>\n

T5<\/strong> is produced by cooling from extrusion and artificial aging; it offers good strength with efficient production and suits most architectural and decorative parts. T6<\/strong> is solution heat treated then aged, giving the highest strength in the 6063 range for structural or load-bearing use. Choose T6 when the design needs more margin, and T5 when surface finish and cost matter most.<\/p>\n

Kluczowe cechy charakterystyczne<\/h2>\n

Smooth Surface & Anodizing Response<\/h3>\n

6063 takes a clean, even anodized finish better than most structural alloys, which is why it is favored for exposed trim and framing.<\/p>\n

Odporno\u015b\u0107 na korozj\u0119<\/h3>\n

In typical atmospheric and mildly industrial environments 6063 resists corrosion well without additional coating.<\/p>\n

Podatno\u015b\u0107 do formowania i spawalno\u015b\u0107<\/h3>\n

The alloy bends and forms readily in softer tempers and welds with standard methods, though welded zones lose some local strength compared with the base temper.<\/p>\n

Zastosowania<\/h2>\n