{"id":2923,"date":"2024-06-01T02:41:45","date_gmt":"2024-06-01T02:41:45","guid":{"rendered":"https:\/\/premiumalu.com\/?post_type=product&p=2923"},"modified":"2026-07-07T08:32:46","modified_gmt":"2026-07-07T08:32:46","slug":"liga-de-aluminio-2017","status":"publish","type":"product","link":"https:\/\/premiumalu.com\/pt\/produto\/liga-de-aluminio-2017\/","title":{"rendered":"Liga de alum\u00ednio 2017"},"content":{"rendered":"

What Is 2017 Aluminum?<\/h2>\n

2017 aluminum alloy (UNS A92017, EN AW-2017) is a copper-based, heat-treatable alloy in the 2xxx series. Its nominal composition \u2014 approximately 3.5\u20134.5% Cu, 0.4\u20131.0% Mn, 0.4\u20130.8% Mg, and 0.2\u20130.8% Si \u2014 gives it a combination of strength and machinability that makes it a practical choice for forged and machined structural parts.<\/p>\n

In the annealed (O) condition, 2017 exhibits good ductility for cold-forming operations such as riveting. After solution heat treatment and natural aging (T4), it develops tensile strength up to approximately 390 MPa \u2014 comparable to many higher-strength aerospace alloys, though with somewhat lower corrosion resistance than 2xxx alloys containing higher magnesium.<\/p>\n

2017 is the direct US equivalent of the Chinese 2A11 (GB\/T 3190) and Russian D1 alloy designations. It is sometimes referred to as AlCu4MgSi<\/strong> under the ISO designation system.<\/p>\n

Available 2017 Aluminum Products<\/h2>\n

Linsy Aluminum supplies 2017 alloy across a range of product forms and tempers. All products can be cut to custom dimensions; typical lead times for custom sizes are 10\u201360 days.<\/p>\n

2017 Aluminum Sheet & Plate<\/h3>\n\n\n\n\n\n
Formul\u00e1rio<\/th>\nTemperamento<\/th>\nEspessura (mm)<\/th>\nLargura (mm)<\/th>\nComprimento (mm)<\/th>\n<\/tr>\n
Folha<\/td>\nO, T3, T351, T4, T42, T451<\/td>\n0.3\u20136.0<\/td>\n500\u20132200<\/td>\n1000\u20136000<\/td>\n<\/tr>\n
Placa<\/td>\nO, T3, T351, T4, T42, T451<\/td>\n6.0\u2013200<\/td>\n500\u20132200<\/td>\n1000\u20136000<\/td>\n<\/tr>\n
Dimensions can be customized to project requirements<\/td>\n<\/tr>\n<\/table>\n

2017 Aluminum Bar<\/h3>\n\n\n\n\n\n\n
Formul\u00e1rio<\/th>\nTemperamento<\/th>\nDiameter \/ Thickness (mm)<\/th>\nComprimento (mm)<\/th>\n<\/tr>\n
Round bar<\/td>\nO, T3, T351, T4, T42, T451<\/td>\n3\u2013500<\/td>\n1000\u20136000<\/td>\n<\/tr>\n
Flat bar<\/td>\nO, T3, T351, T4, T42, T451<\/td>\n3\u2013200 (thickness)<\/td>\n1000\u20136000<\/td>\n<\/tr>\n
Square bar<\/td>\nO, T3, T351, T4, T42, T451<\/td>\n3\u2013200<\/td>\n1000\u20136000<\/td>\n<\/tr>\n
Dimensions can be customized to project requirements<\/td>\n<\/tr>\n<\/table>\n

2017 Aluminum Tube<\/h3>\n\n\n\n\n\n
Formul\u00e1rio<\/th>\nTemperamento<\/th>\nDi\u00e2metro externo (mm)<\/th>\nDi\u00e2metro interno (mm)<\/th>\nComprimento (mm)<\/th>\n<\/tr>\n
Round tube<\/td>\nO, T3, T351, T4, T42, T451<\/td>\n6\u2013350<\/td>\n4\u2013320<\/td>\n1000\u20136000<\/td>\n<\/tr>\n
Square tube<\/td>\nO, T3, T351, T4, T42, T451<\/td>\n10\u2013200 (side)<\/td>\n\u2014<\/td>\n1000\u20136000<\/td>\n<\/tr>\n
Dimensions can be customized to project requirements<\/td>\n<\/tr>\n<\/table>\n

2017 Aluminum Wire<\/h3>\n\n\n\n\n
Temperamento<\/th>\nDi\u00e2metro (mm)<\/th>\nMin. Weight\/Coil<\/th>\nToler\u00e2ncia<\/th>\n<\/tr>\n
O, T3, T4, T351<\/td>\n0.8\u201312<\/td>\n50 kg<\/td>\n\u00b10,02 mm<\/td>\n<\/tr>\n
Dimensions can be customized to project requirements<\/td>\n<\/tr>\n<\/table>\n

Specifications & Equivalent Designations<\/h2>\n\n\n\n\n\n\n\n\n
Especifica\u00e7\u00e3o<\/th>\nDesigna\u00e7\u00e3o<\/th>\n<\/tr>\n
UNS<\/td>\nA92017<\/td>\n<\/tr>\n
PT<\/td>\nEN AW-2017<\/td>\n<\/tr>\n
ISO (AlCu4MgSi)<\/td>\n2017<\/td>\n<\/tr>\n
Chinese (GB\/T 3190)<\/td>\n2A11<\/td>\n<\/tr>\n
Russian (GOST)<\/td>\nD1<\/td>\n<\/tr>\n
AA (US)<\/td>\n2017<\/td>\n<\/tr>\n<\/table>\n

Composi\u00e7\u00e3o qu\u00edmica<\/h2>\n

Per ASTM B209 \/ EN 573-3, the nominal composition of 2017 aluminum alloy:<\/p>\n\n\n\n\n\n\n\n\n\n\n\n\n\n
Elemento<\/th>\nConte\u00fado (%)<\/th>\n<\/tr>\n
Si<\/td>\n0.20\u20130.80<\/td>\n<\/tr>\n
Fe<\/td>\n0.70 max<\/td>\n<\/tr>\n
Cu<\/td>\n3.50\u20134.50<\/td>\n<\/tr>\n
Mn<\/td>\n0.40\u20131.00<\/td>\n<\/tr>\n
Mg<\/td>\n0.40\u20130.80<\/td>\n<\/tr>\n
Cr<\/td>\n0,10 m\u00e1ximo<\/td>\n<\/tr>\n
Zn<\/td>\n0,25 m\u00e1ximo<\/td>\n<\/tr>\n
Ti<\/td>\n0,15 m\u00e1ximo<\/td>\n<\/tr>\n
Others, each<\/td>\n0,05 m\u00e1ximo<\/td>\n<\/tr>\n
Others, total<\/td>\n0,15 m\u00e1ximo<\/td>\n<\/tr>\n
Al<\/td>\nEquil\u00edbrio<\/td>\n<\/tr>\n<\/table>\n

Mechanical Properties by Temper<\/h2>\n

Typical mechanical properties for 2017 aluminum alloy in common tempers (values are approximate and vary with product form and thickness; verify against mill certificates for specific orders):<\/p>\n\n\n\n\n\n\n\n\n
Temperamento<\/th>\nUTS (MPa)<\/th>\nYield (MPa)<\/th>\nElongation A50 (%)<\/th>\nUso t\u00edpico<\/th>\n<\/tr>\n
O<\/td>\n\u2264220<\/td>\n\u2264110<\/td>\n18\u201322<\/td>\nCold forming, riveting<\/td>\n<\/tr>\n
T3<\/td>\n380\u2013390<\/td>\n220\u2013245<\/td>\n12\u201315<\/td>\nAerospace rivets, fasteners<\/td>\n<\/tr>\n
T4<\/td>\n380\u2013390<\/td>\n220\u2013245<\/td>\n12\u201315<\/td>\nStructural parts, machined components<\/td>\n<\/tr>\n
T351<\/td>\n370\u2013390<\/td>\n220\u2013245<\/td>\n12\u201315<\/td>\nStress-relieved plate\/bar for precision machining<\/td>\n<\/tr>\n
T42<\/td>\n370\u2013390<\/td>\n215\u2013240<\/td>\n12\u201315<\/td>\nUser-solution-treated from O temper<\/td>\n<\/tr>\n
T451<\/td>\n370\u2013390<\/td>\n215\u2013240<\/td>\n12\u201315<\/td>\nStress-relieved, user heat-treated<\/td>\n<\/tr>\n<\/table>\n

Temper Selection Guide<\/h2>\n

Choosing the right temper for 2017 depends on the balance between formability and strength your application demands:<\/p>\n