{"id":7803,"date":"2025-02-09T06:48:34","date_gmt":"2025-02-09T06:48:34","guid":{"rendered":"https:\/\/premiumalu.com\/?post_type=product&p=7803"},"modified":"2026-07-08T15:01:11","modified_gmt":"2026-07-08T15:01:11","slug":"liga-de-aluminio-5454","status":"publish","type":"product","link":"https:\/\/premiumalu.com\/pt\/produto\/liga-de-aluminio-5454\/","title":{"rendered":"Liga de alum\u00ednio 5454"},"content":{"rendered":"

What Is 5454 Aluminum?<\/h2>\n

5454 is a non-heat-treatable 5xxx alloy containing about 2.7 percent magnesium with manganese. It offers higher strength than 3003 or 5052 while keeping very good corrosion resistance, including resistance to stress corrosion cracking. These traits make it a common choice for welded pressure equipment and marine structures.<\/p>\n

Available 5454 Aluminum Products<\/h2>\n

Linsy supplies 5454 in sheet, plate, bar, tube, and extruded profiles. The tempers most commonly supplied are O, H32, H34, H111, and H112<\/strong>. Dimensions below are typical ranges; other sizes can be discussed on request.<\/p>\n

Sheet and Coil<\/h3>\n

5454 sheet and coil are supplied in thicknesses from 0.5 mm to 6 mm, widths up to 2600 mm, and lengths up to 6000 mm or cut to size.<\/p>\n

Placa<\/h3>\n

5454 plate is available from 6 mm up to 80 mm thick, with standard widths up to 3000 mm, commonly in H112 or H32.<\/p>\n

Bar (Round, Flat, Square)<\/h3>\n

Round, flat, and square bars are produced in diameters or side lengths from 6 mm to 300 mm, typically in H111, H112, or O.<\/p>\n

Tube and Pipe<\/h3>\n

5454 tube and pipe are supplied in outer diameters from 6 mm to 400 mm with wall thicknesses from 0.5 mm to 40 mm, in O, H32, H34, H111, or H112.<\/p>\n

Extruded Profile<\/h3>\n

Extruded angles, channels, and custom profiles are available on request, usually in H111 or H112 temper.<\/p>\n

Specifications & Equivalent Designations<\/h2>\n

5454 is identified by the following common standards and designations.<\/p>\n\n\n\n\n\n\n\n
Padr\u00e3o<\/th>\nDesigna\u00e7\u00e3o<\/th>\n<\/tr>\n<\/thead>\n
AA<\/td>\n5454<\/td>\n<\/tr>\n
UNS<\/td>\nA95454<\/td>\n<\/tr>\n
EN AW<\/td>\nEN AW-AlMg3Mn<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Composi\u00e7\u00e3o qu\u00edmica<\/h2>\n

The typical composition of 5454 aluminum is listed below in weight percent, with aluminum as the balance.<\/p>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
Elemento<\/th>\nComposi\u00e7\u00e3o (%)<\/th>\n<\/tr>\n<\/thead>\n
Sil\u00edcio (Si)<\/td>\n0,25 m\u00e1ximo<\/td>\n<\/tr>\n
Ferro (Fe)<\/td>\n0.40 max<\/td>\n<\/tr>\n
Cobre (Cu)<\/td>\n0,10 m\u00e1ximo<\/td>\n<\/tr>\n
Mangan\u00eas (Mn)<\/td>\n0.50 – 1.00<\/td>\n<\/tr>\n
Magn\u00e9sio (Mg)<\/td>\n2.4 – 3.0<\/td>\n<\/tr>\n
Cromo (Cr)<\/td>\n0.05 – 0.20<\/td>\n<\/tr>\n
Zinco (Zn)<\/td>\n0,25 m\u00e1ximo<\/td>\n<\/tr>\n
Tit\u00e2nio (Ti)<\/td>\n0.20 max<\/td>\n<\/tr>\n
Others each<\/td>\n0.05<\/td>\n<\/tr>\n
Others total<\/td>\n0.15<\/td>\n<\/tr>\n
Alum\u00ednio (Al)<\/td>\nEquil\u00edbrio<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Propriedades Mec\u00e2nicas por T\u00eampera<\/h2>\n

The values below are typical for rolled and extruded products and should be confirmed against the mill test certificate for the specific temper and thickness ordered.<\/p>\n\n\n\n\n\n\n\n\n\n
Temperamento<\/th>\nResist\u00eancia \u00e0 tra\u00e7\u00e3o (MPa)<\/th>\nResist\u00eancia ao escoamento (MPa)<\/th>\nAlongamento (%)<\/th>\n<\/tr>\n<\/thead>\n
O<\/td>\n215 – 260<\/td>\n85 min<\/td>\n18<\/td>\n<\/tr>\n
H32<\/td>\n250 – 300<\/td>\n180 min<\/td>\n10<\/td>\n<\/tr>\n
H34<\/td>\n270 – 320<\/td>\n215 min<\/td>\n8<\/td>\n<\/tr>\n
H111<\/td>\n215 min<\/td>\n130 min<\/td>\n14<\/td>\n<\/tr>\n
H112<\/td>\n215 min<\/td>\n130 min<\/td>\n12<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Temper Selection Guide<\/h2>\n

Use H32 or H34 for formed and welded parts that need moderate strength. H111 and H112 are suited to structural and pressure components, while O provides the best formability for deep drawing or bending.<\/p>\n

Principais caracter\u00edsticas<\/h2>\n

Resist\u00eancia \u00e0 corros\u00e3o<\/h3>\n

5454 resists seawater and many chemicals well and is not prone to stress corrosion cracking in normal service.<\/p>\n

Soldabilidade<\/h3>\n

It welds readily with MIG and TIG using 5xxx fillers, with little loss of corrosion resistance in the weld zone.<\/p>\n

For\u00e7a<\/h3>\n

It is stronger than the common 3xxx and 5xxx general-purpose grades, making it useful where 5052 is marginally too weak.<\/p>\n

Formabilidade<\/h3>\n

In O and H32 tempers it forms and bends well for tanks and panels.<\/p>\n

Aplicativos<\/h2>\n