5083-H32/H111/H116 铝板

What Is 5083 Aluminum Sheet?

5083 Aluminum Sheet is a non-heat-treatable aluminum-magnesium alloy (AlMg4.5Mn0.7) supplied by Linsy Aluminum. It is one of the strongest work-hardenable grades and is widely specified for marine, offshore, and cryogenic service because of its excellent resistance to seawater corrosion and its ability to retain strength after welding. Common tempers include O, H111, H112, H116, and H321.

Available 5083 Aluminum Products

5083 Sheet & Plate — Standard Sizes

厚度	0.5 – 150 mm
宽度	1000 – 3000 mm
长度	1000 – 6000 mm (custom)
常见状态	O, H111, H112, H116, H321, H32
标准	ASTM B209, EN 485, GB/T 3880

Dimensions can be customized to customer drawings. Share your required size and temper for a quote.

规格与等效牌号

标准	名称
AA / UNS	5083 / A95083
EN	EN AW-AlMg4.5Mn0.7
国际标准化组织	AlMg4.5Mn0.7
GB/T	5A05 (closest domestic grade)
JIS	A5083

化学成分

The composition below follows the AA 5083 specification (AlMg4.5Mn0.7). Values are typical ranges; the supplied MTC reports the actual analysis of your lot.

要素	百分比 %
Si	0.40（上限）
铁	0.40（上限）
铜	最大 0.10
锰	0.40 – 1.00
镁	4.00 – 4.90
Cr	0.05 – 0.25
锌	最大 0.25
Ti	0.15 最大值
其他（每项）	0.05 最大值
其他（共计）	0.15 最大值
Al	平衡

不同回火状态下的力学性能

Values below are typical room-temperature properties for 5083 sheet and plate. Actual results depend on temper and thickness and are reported on the MTC.

脾气	拉伸强度（兆帕）	屈服强度（兆帕）	伸长率 (%)	布氏硬度
O	275 – 350	110 – 145	16 – 21	~75
H111	275 – 350	≥175	16	~75
H112	≥275	≥125	≥12	~75
H116 / H321	305 – 385	≥215	≥10	~85
H32	305 – 345	≥215	≥12	~85

硬度选择指南

• O（退火状态）： maximum ductility and corrosion resistance; used where forming is required.
• H111 / H112: minor strain-hardened or as-fabricated; good general structural use.
• H116 / H321： strain-hardened and stabilized for marine plate and extrusions; the default choice for shipbuilding and offshore structures.
• H32: strain-hardened to half-hard; good for sheet requiring moderate strength and formability.

5083 is non-heat-treatable — tempers are produced by strain hardening and stabilization, not by solution heat treatment.

主要特点

卓越的耐腐蚀性

Resists seawater, brine, and many chemicals; widely used where long service life in marine environments is required.

高强度

One of the strongest non-heat-treatable aluminum alloys, with good strength-to-weight ratio.

焊接性

Excellent weldability with minimal loss of properties in the heat-affected zone.

Cryogenic Toughness

Retains toughness at low temperatures, suitable for LNG and cryogenic storage.

应用

• Shipbuilding and marine structures
• Pressure vessels
• 储存罐
• Offshore platform components
• Transport and cryogenic tanks

加工与表面处理说明

5083 welds well with conventional processes (TIG/MIG) and retains most of its strength in the weld zone. For welding filler, ER5183 or ER5356 wire is commonly used. The alloy has only moderate machinability compared with heat-treatable grades, and cutting tools should account for its gummy chip formation.

• Cutting: sawing, CNC machining, laser cutting
• Forming: good in O and soft tempers; springback increases with hardening
• Surface: mill finish standard; anodizing, polishing, powder coating, PVC film available
• Heat input during welding should be controlled to avoid softening of adjacent material

质量文件与检验

Every 5083 order ships with a material test certificate (MTC) that reports the actual chemical analysis and mechanical results for the supplied lot. Third-party SGS test reports are available on request. Standard mill inspections cover dimensional tolerance, surface condition, and tensile verification per the ordered specification.

• MTC (EN 10204 3.1 or equivalent) with every order
• Dimensional and visual inspection at shipment
• Optional ultrasonic or penetration testing for plate and heavy sections
• RoHS and REACH documentation available on request

Why Choose Linsy for 5083 Sheet

Linsy Aluminum is a Shenzhen-based aluminum manufacturer with over 20 years of production experience, supplying the 1000–8000 series across plate, bar, tube, wire, coil, profile, and block. For 5083 sheet, we support custom dimensions, small minimum order quantities, and short lead times.

• Typical custom lead time: 10–60 days depending on specification
• Processing support: CNC machining, cutting, bending, welding, anodizing, polishing, powder coating
• Certified to ISO 9001, ISO 14001, and ISO 45001
• Material test certificate provided with every order

相关资源

• 5083 铝材终极指南
• 5083 H321 铝材终极指南
• 如何选择 5083 铝板
• Marine Plate: 5052 vs 5083

5083 Aluminum Sheet FAQ

What is the maximum thickness for 5083 sheet?

Linsy supplies 5083 as sheet and plate from 0.5 mm up to 150 mm. Thicker plates are produced to order.

Which temper is best for marine plate?

H116 and H321 are the standard marine tempers for 5083 plate, offering stabilized strength and corrosion resistance.

Is 5083 sheet stress-corrosion resistant?

Yes. 5083 has good resistance to stress-corrosion cracking, an important property for marine and offshore structures.

常见订购问题解答

通常的交货周期是多久？

Custom 5083 orders are usually produced and shipped within 10–60 days, depending on temper, size, and quantity. Contact us with your drawing or specification for a firm schedule.

最小起订量是多少？

We support low minimum order quantities for standard tempers and common sizes. Non-standard dimensions are quoted case by case.

Do you provide a material certificate?

Yes. A material test certificate (MTC) is provided with every order, and third-party SGS test reports are available on request.

Which surface finishes are available?

Mill finish is standard. Anodizing, polishing, powder coating, and PVC film protection can be arranged.

Can you cut to size?

Yes. CNC cutting, sawing, and machining services are available so material arrives closer to your net shape.