7049 aluminum is a high-strength 7xxx series alloy with high zinc and copper content, formulated primarily as a forging grade. It offers excellent resistance to stress-corrosion cracking and good machinability, which makes it a frequent choice for critical structural forgings in aerospace and missile applications. It is generally considered non-weldable and is best supplied as forged or machined parts. Linsy supplies 7049 in plate, bar, and forging stock with mill test certificates on every order.
Dostupné formuláře: plate, bar / rod, forging stock
Běžné typy povah: F, H112, O, T352, T6, T651, T73, T7451
Podpora zpracování: CNC obrábění, laserové řezání, TIG/MIG svařování, eloxování, leštění, práškové lakování
Dokumenty týkající se kvality: Protokol o zkoušce z materiálu (MTC) s každou objednávkou
7049 aluminum is a high-strength 7xxx series alloy with high zinc and copper content, formulated primarily as a forging grade. It offers excellent resistance to stress-corrosion cracking and good machinability, which makes it a frequent choice for critical structural forgings in aerospace and missile applications. It is generally considered non-weldable and is best supplied as forged or machined parts. Linsy supplies 7049 in plate, bar, and forging stock with mill test certificates on every order.
Dostupné stavy: F, O, T6, T651, T7451, H112
| Temperament | Tloušťka (mm) | Šířka (mm) | Délka (mm) |
|---|---|---|---|
| F, O, T6, T651, T7451, H112 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (řezání na míru) |
Dostupné stavy: T73, T352
| Temperament | Průměr (mm) | Délka (mm) |
|---|---|---|
| T73, T352 | 3 – 300 | 500 – 12000 |
Dostupné stavy: T73, T352
| Temperament | Available forms | Note |
|---|---|---|
| T73, T352 | Bloom, billet, disc | Custom forging on request |
7049 aluminum (EN AW-7049, AlZn8MgCu) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Prvek | Procento (%) |
|---|---|
| Si | max 0,40 |
| Fe | 0,35 max |
| Cu | 1.2 – 1.9 |
| Mn | max 0,20 |
| Mg | 2.1 - 2.9 |
| Cr | 0.10 – 0.22 |
| Zn | 7.6 - 8.4 |
| Ti | 0,10 max |
| Zr | 0,25 max. |
| Ostatní (každý) | 0.05 |
| Ostatní (celkem) | 0.15 |
| Al | Bilance |
| Temperament | Pevnost v tahu (MPa) | Mez kluzu (MPa) | Prodloužení (%) | Pevnost ve smyku (MPa) |
|---|---|---|---|---|
| T73 | 483 – 517* | 414 – 448* | 7 – 12* | 150 – 340* |
| T352 | 483 – 517* | 414 – 448* | 7 – 12* | 150 – 340* |
Values are typical for the indicated condition. An em dash (—) means the value was not available in the source data; confirm with the mill certificate. Asterisked values are estimates pending verification — see the audit report.
Among the strongest 7xxx forging alloys.
T73 / T7451 tempers resist cracking in aggressive environments.
Cuts cleanly on CNC equipment.
Design as forged or machined parts; welding is not recommended.
Linsy supplies 7049 as plate, bar, and forging stock, then CNC-machines and laser-cuts to print. It is not recommended for welding. For corrosion protection, anodizing or painting is advised, and the T73 / T7451 tempers should be specified where stress-corrosion resistance is critical.
Společnost Linsy je dodavatel hliníku se sídlem v Shenzhenu s více než 20 lety zkušeností. Náš systém kvality je certifikován podle ISO 9001, ISO 14001 a ISO 45001. Každá objednávka je odeslána s certifikátem z válcovny (MTC). Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání. Typická dodací lhůta na zakázku je 10–60 dní v závislosti na stavu, rozměru a množství.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection and welding 7000-series alloys. (Internal links to be connected to published Linsy blog articles.)
No, 7049 is generally considered non-weldable and is supplied as forged or machined components.
The overaged T73 and T7451 tempers give the best resistance to stress-corrosion cracking; use them for critical aerospace structures.
The source mechanical data for 7049 was partially corrupted. Values shown are typical and must be verified against the mill certificate before release.
Každá objednávka je odeslána s MTC a zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Zakázkové objednávky hliníku se obvykle odesílají za 10–60 dní v závislosti na slitině, stavu, rozměru a množství. Skladové nebo standardní rozměry mohou být rychlejší – zeptejte se našeho týmu.
Ano. Každá objednávka obsahuje MTC. Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Ano. Poskytujeme CNC obrábění, laserové řezání, svařování, eloxování, leštění a práškové lakování, takže díly mohou být dodány v blíže k hotovému tvaru.
Zašlete svou slitinu, stav, rozměry, množství a požadovanou normu. Náš tým potvrdí dostupnost, dodací lhůtu a cenu.
Výhody Linsy
Společnost Linsy Aluminium je předním dodavatelem výrobků pro zpracování hliníku, které slouží různým průmyslovým odvětvím včetně leteckého průmyslu, všeobecného strojírenství, automobilového průmyslu, lodního průmyslu, stavby lodí a dalších specializovaných průmyslových aplikací.
Zavázali jsme se dodržovat nejvyšší standardy kvality a odpovědnosti vůči životnímu prostředí, což dokazují naše certifikáty: ISO 9001:2008， ISO 14001:2004 a SGS.