7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
Dostupné formuláře: plate, tube, bar / rod, wire
Běžné typy povah: F, H112, O, T6, T651, T7451, T77, T7751
Podpora zpracování: CNC obrábění, laserové řezání, TIG/MIG svařování, eloxování, leštění, práškové lakování
Dokumenty týkající se kvality: Protokol o zkoušce z materiálu (MTC) s každou objednávkou
7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
Dostupné stavy: F, O, T6, T651, T7451, H112
| Temperament | Tloušťka (mm) | Šířka (mm) | Délka (mm) |
|---|---|---|---|
| F, O, T6, T651, T7451, H112 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (řezání na míru) |
Dostupné stavy: T77, T7751
| Temperament | Vnější průměr (mm) | Tloušťka stěny (mm) | Délka (mm) |
|---|---|---|---|
| T77, T7751 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Dostupné stavy: T77, T7751
| Temperament | Průměr (mm) | Délka (mm) |
|---|---|---|
| T77, T7751 | 3 – 300 | 500 – 12000 |
Dostupné stavy: T77, T7751
| Průměr (mm) | Hmotnost svitku | Tolerance |
|---|---|---|
| 0.8 – 30 | Min. 50 kg | ± 0,02 mm |
7055 aluminum (EN AW-7055, AlZn8MgCuZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Prvek | Procento (%) |
|---|---|
| Si | 0,10 max |
| Fe | 0,15 max |
| Cu | 2.0 - 2.6 |
| Mn | 0,05 max |
| Mg | 1.8 - 2.3 |
| Cr | 0,04 max. |
| Zn | 7.6 - 8.4 |
| Ti | 0,06 max |
| Zr | 0.08 - 0.25 |
| Ostatní (každý) | 0.05 |
| Ostatní (celkem) | 0.15 |
| Al | Bilance |
| Temperament | Pevnost v tahu (MPa) | Mez kluzu (MPa) | Prodloužení (%) | Pevnost ve smyku (MPa) |
|---|---|---|---|---|
| T7751 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
| T6 / T651 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
Values are typical for the T7751 / T6 tempers. Composition was corrected to AA 7055 limits (see audit report) and must be confirmed with the mill certificate.
Exceeds 7050 and 7075 in compression and fatigue.
Holds up under cyclic load in thick sections.
Overaging balances strength and corrosion.
Supplied as machined or formed parts.
Linsy CNC-machines and laser-cuts 7055, then anodizes or paints for corrosion protection. Welding is not recommended.
Společnost Linsy je dodavatel hliníku se sídlem v Shenzhenu s více než 20 lety zkušeností. Náš systém kvality je certifikován podle ISO 9001, ISO 14001 a ISO 45001. Každá objednávka je odeslána s certifikátem z válcovny (MTC). Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání. Typická dodací lhůta na zakázku je 10–60 dní v závislosti na stavu, rozměru a množství.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
Yes. 7055 is among the strongest commercial 7xxx alloys, with higher compression and fatigue strength, especially in thick sections.
T7751 offers the best balance of strength and stress-corrosion resistance.
No, it is not a welding grade; design as machined or formed parts.
Každá objednávka je odeslána s MTC a zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Zakázkové objednávky hliníku se obvykle odesílají za 10–60 dní v závislosti na slitině, stavu, rozměru a množství. Skladové nebo standardní rozměry mohou být rychlejší – zeptejte se našeho týmu.
Ano. Každá objednávka obsahuje MTC. Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Ano. Poskytujeme CNC obrábění, laserové řezání, svařování, eloxování, leštění a práškové lakování, takže díly mohou být dodány v blíže k hotovému tvaru.
Zašlete svou slitinu, stav, rozměry, množství a požadovanou normu. Náš tým potvrdí dostupnost, dodací lhůtu a cenu.
Výhody Linsy
Společnost Linsy Aluminium je předním dodavatelem výrobků pro zpracování hliníku, které slouží různým průmyslovým odvětvím včetně leteckého průmyslu, všeobecného strojírenství, automobilového průmyslu, lodního průmyslu, stavby lodí a dalších specializovaných průmyslových aplikací.
Zavázali jsme se dodržovat nejvyšší standardy kvality a odpovědnosti vůči životnímu prostředí, což dokazují naše certifikáty: ISO 9001:2008， ISO 14001:2004 a SGS.