7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
Dostupné formuláře: plate, tube, bar / rod
Běžné typy povah: T73510, T73511, T74, T7451, T7452
Podpora zpracování: CNC obrábění, laserové řezání, TIG/MIG svařování, eloxování, leštění, práškové lakování
Dokumenty týkající se kvality: Protokol o zkoušce z materiálu (MTC) s každou objednávkou
7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
Dostupné stavy: T73510, T73511, T74, T7451, T7452
| Temperament | Tloušťka (mm) | Šířka (mm) | Délka (mm) |
|---|---|---|---|
| T73510, T73511, T74, T7451, T7452 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (řezání na míru) |
Dostupné stavy: T73510, T73511, T7451, T7452
| Temperament | Vnější průměr (mm) | Tloušťka stěny (mm) | Délka (mm) |
|---|---|---|---|
| T73510, T73511, T7451, T7452 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Dostupné stavy: T73510, T73511, T7451, T7452
| Temperament | Průměr (mm) | Délka (mm) |
|---|---|---|
| T73510, T73511, T7451, T7452 | 3 – 300 | 500 – 12000 |
7050 aluminum (EN AW-7050, AlZn6CuMgZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Prvek | Procento (%) |
|---|---|
| Si | 0,12 max |
| Fe | 0,15 max |
| Cu | 2.0 - 2.6 |
| Mn | 0,10 max |
| Mg | 1.9 – 2.6 |
| Cr | 0,04 max. |
| Zn | 5.6 – 6.7 |
| Ti | 0,06 max |
| Zr | 0.08 – 0.15 |
| Ostatní (každý) | 0.05 |
| Ostatní (celkem) | 0.15 |
| Al | Bilance |
| Temperament | Pevnost v tahu (MPa) | Mez kluzu (MPa) | Prodloužení (%) | Pevnost ve smyku (MPa) |
|---|---|---|---|---|
| T7451 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
| T73510 / T73511 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
Values are typical for the overaged T7451 / T7351x tempers; confirm exact figures with the mill certificate.
Less quench-sensitive than 7075, so plate stays strong through its depth.
Overaged tempers resist cracking in aggressive service.
Precipitation hardening delivers the specified strength.
Generally supplied as a machined or formed part, not a welded assembly.
Linsy CNC-machines and laser-cuts 7050, then anodizes or paints for corrosion protection. Welding is not recommended; design parts as machined or formed components.
Společnost Linsy je dodavatel hliníku se sídlem v Shenzhenu s více než 20 lety zkušeností. Náš systém kvality je certifikován podle ISO 9001, ISO 14001 a ISO 45001. Každá objednávka je odeslána s certifikátem z válcovny (MTC). Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání. Typická dodací lhůta na zakázku je 10–60 dní v závislosti na stavu, rozměru a množství.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
7050 is less sensitive to quench rate, so it keeps strength better in thick plate, and its overaged tempers resist stress corrosion far better than 7075-T6.
T7451 is the standard for aerospace plate where corrosion resistance matters; T73510/T73511 for extruded sections.
No, it is not a welding grade. Plan for machined or bonded assemblies.
Každá objednávka je odeslána s MTC a zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Zakázkové objednávky hliníku se obvykle odesílají za 10–60 dní v závislosti na slitině, stavu, rozměru a množství. Skladové nebo standardní rozměry mohou být rychlejší – zeptejte se našeho týmu.
Ano. Každá objednávka obsahuje MTC. Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Ano. Poskytujeme CNC obrábění, laserové řezání, svařování, eloxování, leštění a práškové lakování, takže díly mohou být dodány v blíže k hotovému tvaru.
Zašlete svou slitinu, stav, rozměry, množství a požadovanou normu. Náš tým potvrdí dostupnost, dodací lhůtu a cenu.
Výhody Linsy
Společnost Linsy Aluminium je předním dodavatelem výrobků pro zpracování hliníku, které slouží různým průmyslovým odvětvím včetně leteckého průmyslu, všeobecného strojírenství, automobilového průmyslu, lodního průmyslu, stavby lodí a dalších specializovaných průmyslových aplikací.
Zavázali jsme se dodržovat nejvyšší standardy kvality a odpovědnosti vůči životnímu prostředí, což dokazují naše certifikáty: ISO 9001:2008， ISO 14001:2004 a SGS.