7150 is a high-strength, heat-treatable 7xxx alloy primarily alloyed with zinc, copper and magnesium. It is engineered for aerospace structures, offering a strong balance of strength, fatigue resistance and fracture toughness. Linsy supplies 7150 plate, bar and tube in T6, T651 and T7751 tempers with full MTC documentation.
Доступные формы: plate / sheet / bar / tube
Распространенные типы характера: O / T6 / T651 / T7751
Поддержка обработки: CNC machining, saw cutting, anodizing
Документы по качеству: Отчет MTC с каждым заказом
7150 is a high-strength, heat-treatable 7xxx alloy primarily alloyed with zinc, copper and magnesium. It is engineered for aerospace structures, offering a strong balance of strength, fatigue resistance and fracture toughness. Linsy supplies 7150 plate, bar and tube in T6, T651 and T7751 tempers with full MTC documentation. While not quite as strong as 7055, 7150 provides an excellent combination of properties for demanding aircraft structural components such as wing and fuselage parts.
| Толщина (мм) | Ширина (мм) | Длина (мм) | Темпер |
|---|---|---|---|
| 6 – 150 | 500 – 2500 | up to 12,000 | O, T6, T651, T7751 |
| Custom sizes on request | — | — | — |
| Bar Dia. (mm) / Tube OD (mm) | Длина (мм) | Темпер |
|---|---|---|
| 3 – 300 (bar) / 6 – 300 (tube) | up to 12,000 | O, T6, T651, T7751 |
| Custom sizes on request | — | — |
7150 is supplied to ASTM B221 / AMS standards where applicable. EN AW designation: EN AW-7150. (Confirm exact spec with our team for your application.)
| Элемент | Содержание (%) |
|---|---|
| Si | 0,40 макс. |
| Fe | 0,50 макс. |
| Cu | 2.0 - 2.6 |
| Mn | 0,30 макс. |
| Mg | 1.9 – 2.6 |
| Cr | 0,04 макс. |
| Zn | 5.7 – 6.7 |
| Ti | 0,06 макс. |
| Zr | 0.08 – 0.15 |
| Другие (каждый) | 0,05 макс. |
| Прочие (всего) | 0,15 макс. |
| Эл | Баланс |
Typical T7x values: tensile 540–570 MPa, yield 420–520 MPa, elongation 11–13%, shear 150–340 MPa. Values vary by product form and thickness — confirm against the MTC.
| Темпер | Темпер | Предел прочности при растяжении (МПа) | Предел текучести (МПа) | Elong. (%) |
|---|---|---|---|---|
| T651 | 540 – 570 | 420 – 520 | 11 – 13 | |
| T7751 | 540 – 570 | 420 – 520 | 11 – 13 |
T651 — high strength with stress relief for machining. T7751 — optimized toughness and corrosion resistance for aerospace structures. 7150 is not weld-friendly; use mechanical joining.
Strong 7xxx grade balanced for fatigue-critical parts.
Suited to cyclic-load aircraft structures.
Not recommended for fusion welding.
Aircraft wing and fuselage structures, gears and shafts, high-stress automotive and aerospace components.
CNC machining and saw cutting supported; anodizing available. 7150 work-hardens — use rigid tooling and coolant.
Every order ships with an MTC. SGS third-party test reports available on request. Linsy holds ISO 9001, ISO 14001 and ISO 45001.
Linsy Aluminum is a Shenzhen-based supplier with 20+ years of experience across the 1000–8000 series. We supply 7150 plate, bar and tube with MTC per order and support custom sizes. Typical custom lead time is 10–60 days.
Internal Linsy blog links for 7150 are being added as articles are published. For 7xxx selection, see our 7075 guides in the meantime.
What tempers does 7150 come in?
O, T6, T651 and T7751.
Is 7150 weldable?
Fusion welding is generally not recommended.
What lead time?
10–60 days for custom sizes.
MTC provided?
Yes, with every order.
Custom sizes?
Yes, plate/bar/tube cut to spec.
Standards?
ASTM B221, AMS, GB/T, EN on request.