7150 is a high-strength, heat-treatable 7xxx alloy primarily alloyed with zinc, copper and magnesium. It is engineered for aerospace structures, offering a strong balance of strength, fatigue resistance and fracture toughness. Linsy supplies 7150 plate, bar and tube in T6, T651 and T7751 tempers with full MTC documentation.
이용 가능한 양식: plate / sheet / bar / tube
흔히 나타나는 기질: O / T6 / T651 / T7751
처리 지원: CNC machining, saw cutting, anodizing
품질 관련 문서: 모든 주문 시 MTC 보고서 제공
7150 is a high-strength, heat-treatable 7xxx alloy primarily alloyed with zinc, copper and magnesium. It is engineered for aerospace structures, offering a strong balance of strength, fatigue resistance and fracture toughness. Linsy supplies 7150 plate, bar and tube in T6, T651 and T7751 tempers with full MTC documentation. While not quite as strong as 7055, 7150 provides an excellent combination of properties for demanding aircraft structural components such as wing and fuselage parts.
| 두께(mm) | 너비(mm) | 길이(mm) | 성질 |
|---|---|---|---|
| 6 – 150 | 500 – 2500 | up to 12,000 | O, T6, T651, T7751 |
| Custom sizes on request | — | — | — |
| Bar Dia. (mm) / Tube OD (mm) | 길이(mm) | 성질 |
|---|---|---|
| 3 – 300 (bar) / 6 – 300 (tube) | up to 12,000 | O, T6, T651, T7751 |
| Custom sizes on request | — | — |
7150 is supplied to ASTM B221 / AMS standards where applicable. EN AW designation: EN AW-7150. (Confirm exact spec with our team for your application.)
| 요소 | 콘텐츠(%) |
|---|---|
| Si | 0.40 최대 |
| Fe | 0.50 최대 |
| Cu | 2.0 - 2.6 |
| Mn | 0.30 최대 |
| Mg | 1.9 – 2.6 |
| Cr | 최대 0.04 |
| Zn | 5.7 – 6.7 |
| Ti | 최대 0.06 |
| Zr | 0.08 – 0.15 |
| 기타(각) | 최대 0.05 |
| 기타(합계) | 최대 0.15 |
| Al | 잔액 |
Typical T7x values: tensile 540–570 MPa, yield 420–520 MPa, elongation 11–13%, shear 150–340 MPa. Values vary by product form and thickness — confirm against the MTC.
| 성질 | 성질 | 인장 강도 (MPa) | 항복 강도 (MPa) | Elong. (%) |
|---|---|---|---|---|
| T651 | 540 – 570 | 420 – 520 | 11 – 13 | |
| T7751 | 540 – 570 | 420 – 520 | 11 – 13 |
T651 — high strength with stress relief for machining. T7751 — optimized toughness and corrosion resistance for aerospace structures. 7150 is not weld-friendly; use mechanical joining.
Strong 7xxx grade balanced for fatigue-critical parts.
Suited to cyclic-load aircraft structures.
Not recommended for fusion welding.
Aircraft wing and fuselage structures, gears and shafts, high-stress automotive and aerospace components.
CNC machining and saw cutting supported; anodizing available. 7150 work-hardens — use rigid tooling and coolant.
Every order ships with an MTC. SGS third-party test reports available on request. Linsy holds ISO 9001, ISO 14001 and ISO 45001.
Linsy Aluminum is a Shenzhen-based supplier with 20+ years of experience across the 1000–8000 series. We supply 7150 plate, bar and tube with MTC per order and support custom sizes. Typical custom lead time is 10–60 days.
Internal Linsy blog links for 7150 are being added as articles are published. For 7xxx selection, see our 7075 guides in the meantime.
What tempers does 7150 come in?
O, T6, T651 and T7751.
Is 7150 weldable?
Fusion welding is generally not recommended.
What lead time?
10–60 days for custom sizes.
MTC provided?
Yes, with every order.
Custom sizes?
Yes, plate/bar/tube cut to spec.
Standards?
ASTM B221, AMS, GB/T, EN on request.