7022 aluminum is a high-strength Zn-Mg-Cu alloy in the 7xxx series, combining zinc, magnesium, and copper for elevated strength and good machinability. It is often chosen for tooling, mold making, and high-stress machined components where dimensional stability after machining matters. Linsy supplies 7022 in sheet, plate, and bar with mill test certificates on every order. Note: mechanical values below should be confirmed against the mill certificate before release.
Dostupné formuláře: sheet / plate, bar / rod
Běžné typy povah: T6, T651
Podpora zpracování: CNC obrábění, laserové řezání, TIG/MIG svařování, eloxování, leštění, práškové lakování
Dokumenty týkající se kvality: Protokol o zkoušce z materiálu (MTC) s každou objednávkou
7022 aluminum is a high-strength Zn-Mg-Cu alloy in the 7xxx series, combining zinc, magnesium, and copper for elevated strength and good machinability. It is often chosen for tooling, mold making, and high-stress machined components where dimensional stability after machining matters. Linsy supplies 7022 in sheet, plate, and bar with mill test certificates on every order. Note: mechanical values below should be confirmed against the mill certificate before release.
Dostupné stavy: T6, T651
| Temperament | Tloušťka (mm) | Šířka (mm) | Délka (mm) |
|---|---|---|---|
| T6, T651 | 0.5 – 150 | 500 – 2600 | 500 – 16000 (řezání na míru) |
Dostupné stavy: T6, T651
| Temperament | Průměr (mm) | Délka (mm) |
|---|---|---|
| T6, T651 | 3 – 300 | 500 – 12000 |
7022 aluminum (EN AW-7022, AlZn4.5Mg1) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Prvek | Procento (%) |
|---|---|
| Si | max 0,50 |
| Fe | max 0,50 |
| Cu | 0.50 – 1.0 |
| Mn | 0.10 – 0.40 |
| Mg | 2.6 – 3.7 |
| Cr | 0.10 – 0.30 |
| Zn | 4.3 – 5.2 |
| Ti | max 0,20 |
| Ostatní (každý) | 0.05 |
| Ostatní (celkem) | 0.15 |
| Al | Bilance |
| Temperament | Pevnost v tahu (MPa) | Mez kluzu (MPa) | Prodloužení (%) | Pevnost ve smyku (MPa) |
|---|---|---|---|---|
| T6 | ~ 480 – 540* | ~ 420 – 480* | 8 – 12* | — |
| T651 | ~ 480 – 540* | ~ 420 – 480* | 8 – 12* | — |
Values are typical for the indicated condition. An em dash (—) means the value was not available in the source data; confirm with the mill certificate. Asterisked values are estimates pending verification — see the audit report.
Among the stronger medium-zinc 7xxx grades, close to 7075 in the T6 condition.
Holds tight tolerances and a clean finish in high-speed milling.
T651 minimizes distortion after removal of stock.
Generally considered non-weldable; design as a machined part, not a welded assembly.
Linsy machines 7022 on CNC centers for molds and precision parts and laser-cuts plate. It is not recommended for welding; for corrosion protection use anodizing or painting. Stress-relieving (T651) is advised for finished machined parts.
Společnost Linsy je dodavatel hliníku se sídlem v Shenzhenu s více než 20 lety zkušeností. Náš systém kvality je certifikován podle ISO 9001, ISO 14001 a ISO 45001. Každá objednávka je odeslána s certifikátem z válcovny (MTC). Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání. Typická dodací lhůta na zakázku je 10–60 dní v závislosti na stavu, rozměru a množství.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection and welding 7000-series alloys. (Internal links to be connected to published Linsy blog articles.)
Generally no. 7022 is supplied for machined and formed parts rather than welded assemblies; choose 7020 or 7021 if welding is required.
Tooling, injection molds, and high-stress machined components where strength and stability after machining are critical.
The source data for this page was incomplete and partly copied from another grade. The values shown are typical estimates and must be verified against the mill certificate before use.
Každá objednávka je odeslána s MTC a zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Zakázkové objednávky hliníku se obvykle odesílají za 10–60 dní v závislosti na slitině, stavu, rozměru a množství. Skladové nebo standardní rozměry mohou být rychlejší – zeptejte se našeho týmu.
Ano. Každá objednávka obsahuje MTC. Zkušební protokoly třetí strany SGS jsou k dispozici na vyžádání.
Ano. Poskytujeme CNC obrábění, laserové řezání, svařování, eloxování, leštění a práškové lakování, takže díly mohou být dodány v blíže k hotovému tvaru.
Zašlete svou slitinu, stav, rozměry, množství a požadovanou normu. Náš tým potvrdí dostupnost, dodací lhůtu a cenu.
Výhody Linsy
Společnost Linsy Aluminium je předním dodavatelem výrobků pro zpracování hliníku, které slouží různým průmyslovým odvětvím včetně leteckého průmyslu, všeobecného strojírenství, automobilového průmyslu, lodního průmyslu, stavby lodí a dalších specializovaných průmyslových aplikací.
Zavázali jsme se dodržovat nejvyšší standardy kvality a odpovědnosti vůči životnímu prostředí, což dokazují naše certifikáty: ISO 9001:2008， ISO 14001:2004 a SGS.