6201 aluminum alloy is a heat-treatable 6xxx series conductor grade combining good electrical conductivity with moderate strength and resistance to stress-corrosion cracking. Linsy supplies 6201 as wire, rod, and bar in T4, T6, and T81 tempers for busbars, conductor rails, and overhead line hardware. Custom sizes, cutting, and MTC documentation are available with every order.
Dostupné formuláře: wire / rod / bar / sheet / coil / tube
Běžné typy povah: T4 / T6 / T81
Podpora zpracování: cutting / drawing / CNC machining / custom length
Dokumenty týkající se kvality: Protokol o zkoušce z materiálu (MTC) s každou objednávkou
6201 aluminum is a heat-treatable 6xxx series alloy developed for electrical conductor applications. With a silicon-magnesium composition and moderate strength, it combines good electrical conductivity with resistance to stress-corrosion cracking. It is most commonly supplied in the T81 temper for busbars, conductor rails, and overhead line hardware where a balance of conductivity and mechanical strength is required.
6201 is primarily an electrical conductor alloy, most often supplied as wire and rod for busbar and overhead line use. The following forms and size ranges are typical; custom dimensions can be negotiated.
| Formulář | Size Range | Temperament |
| Wire (coil) | 0.8 – 30 mm diameter | T81, T6 |
| Drawn rod | 6 – 60 mm diameter | T81, T6 |
| Formulář | Size Range | Temperament |
| Round / square bar | 6 – 300 mm diameter | T81, T6, T4 |
| Formulář | Size Range | Temperament |
| Sheet / coil | 0.5 – 10 mm thickness, 500 – 2600 mm width | T6, T4 |
Extruded tube and profile in T6 temper are available on request; typical outside diameters range from 6 to 300 mm. Length is normally up to 12,000 mm and can be cut to order.
| Systém | Označení |
| AA (USA) | 6201 |
| EN AW | EN AW-6201 |
| UNS | A96201 |
| ISO | AlMg0.7Si |
| Běžné stavy | T4, T6, T81 |
| Prvek | Obsah (%) |
| Křemík (Si) | 0.50 – 0.90 |
| Železo (Fe) | max 0,50 |
| Měď (Cu) | 0,10 max |
| Mangan (Mn) | 0.03 max |
| Hořčík (Mg) | 0.60 – 0.90 |
| Zinek (Zn) | 0,10 max |
| Titan (Ti) | 0.03 max |
| Ostatní (každý) | 0,05 max |
| Ostatní (celkem) | 0,15 max |
| Hliník (Al) | Zbytek |
Values below are typical AA reference figures for 6201 and should be confirmed against Linsy mill test data before specification.
| Temperament | Pevnost v tahu (MPa) | Mez kluzu (MPa) | Prodloužení (%) | Pevnost ve smyku (MPa) |
| T4 | 200 | 120 | 15 | — |
| T6 | 300 | 260 | 10 | — |
| T81 | 310 | 275 | 8 | 193 |
| Temperament | Kdy použít |
| T4 | Solution heat-treated and naturally aged; higher ductility for forming before final use. |
| T6 | Solution heat-treated and artificially aged; higher strength for general structural conductors. |
| T81 | Solution heat-treated, cold-worked, and artificially aged; the standard temper for 6201 busbar and conductor wire offering the best strength-to-conductivity balance. |
6201 offers good conductivity (approximately 53% IACS in the T81 temper), making it suitable for power transmission and distribution components.
Compared with pure aluminum conductor grades, 6201 provides significantly higher strength while retaining good corrosion resistance and resistance to stress-corrosion cracking.
The alloy is typically used in the as-supplied temper; welding is uncommon for electrical conductors, and mechanical connections (bolting, crimping) are preferred.
6201 wire and rod are supplied in the drawn or extruded condition. Cutting, bending, and punching are standard fabrication steps. Anodizing is not typical for electrical conductor use; consult our team before specifying a surface finish on conductive parts.
Every 6201 order ships with a Mill Test Certificate (EN 10204 3.1 MTC) covering composition and mechanical properties. SGS or third-party inspection can be arranged on request.
Comparison guides between conductor grades (for example 6101 vs 6201) and general aluminum selection notes can be linked to this page. Blog resources are being consolidated and will be added before launch.
No. Both are electrical conductor alloys, but 6201 has a higher magnesium range and is typically used in the T81 temper for busbar, while 6101 is more common for wire and strand.
In the T81 temper, 6201 typically reaches about 53% IACS. Confirm exact values from the MTC for your specific lot.
Standardní skladové rozměry jsou obvykle odeslány do 10–60 dnů v závislosti na temperu, množství a případném zakázkovém zpracování. Přesný harmonogram potvrďte s naším obchodním týmem při vyžádání cenové nabídky.
Ano. Řežeme na délku, pílíme a CNC obrábíme podle výkresu a na vyžádání můžeme zajistit specifické tempery. Uveďte požadované rozměry a tolerance v poptávce.
Hutní certifikát (MTC) je přiložen ke každé objednávce. V případě potřeby lze zajistit inspekční zprávy SGS nebo jiné třetí strany.
Mezi běžné možnosti patří povrch z válcovny, eloxování a leštění. Konkrétní povrchové úpravy by měly být dohodnuty ve fázi cenové nabídky.
Výhody Linsy
Společnost Linsy Aluminium je předním dodavatelem výrobků pro zpracování hliníku, které slouží různým průmyslovým odvětvím včetně leteckého průmyslu, všeobecného strojírenství, automobilového průmyslu, lodního průmyslu, stavby lodí a dalších specializovaných průmyslových aplikací.
Zavázali jsme se dodržovat nejvyšší standardy kvality a odpovědnosti vůči životnímu prostředí, což dokazují naše certifikáty: ISO 9001:2008， ISO 14001:2004 a SGS.