7475 is a high-strength 7xxx alloy engineered specifically for superior toughness and fracture resistance, even in thicker sections. Commonly supplied in T761 temper for aircraft fuselage and wing skins, it is the preferred choice for critical structures where both strength and durability matter. Linsy supplies 7475 sheet, plate, bar and tube with full MTC documentation.
Доступные формы: sheet / plate / bar / tube / wire
Распространенные типы характера: T761 / T7351
Поддержка обработки: CNC machining, saw cutting, anodizing
Документы по качеству: Отчет MTC с каждым заказом
7475 is a high-strength 7xxx alloy engineered specifically for superior toughness and fracture resistance, even in thicker sections. Commonly supplied in T761 temper for aircraft fuselage and wing skins, it is the preferred choice for critical structures where both strength and durability matter. Linsy supplies 7475 sheet, plate, bar and tube with full MTC documentation. Its high zinc content gives an outstanding strength-to-toughness combination, making it a staple for aircraft skins and bulkheads.
| Толщина (мм) | Ширина (мм) | Длина (мм) | Темпер |
|---|---|---|---|
| 0.5 – 150 | 500 – 2500 | up to 12,000 | T761, T7351 |
| Custom sizes on request | — | — | — |
| Bar Dia. / Tube OD (mm) | Wire (mm) | Длина (мм) | Темпер |
|---|---|---|---|
| 3 – 300 (bar) / 6 – 300 (tube) | 0.8 – 30 | up to 12,000 | T761, T7351 |
| Custom sizes on request | — | — | — |
7475 is supplied to AMS and ASTM references where applicable (e.g., AMS 4202 for T761 plate). EN AW designation: EN AW-7475. Confirm exact spec with our team.
| Элемент | Содержание (%) |
|---|---|
| Si | 0.10 макс. |
| Fe | 0,12 макс. |
| Cu | 1.2 – 1.9 |
| Mn | 0,06 макс. |
| Mg | 1.9 – 2.6 |
| Cr | 0.18 – 0.25 |
| Zn | 5.2 – 6.2 |
| Ti | 0,06 макс. |
| Другие (каждый) | 0,05 макс. |
| Прочие (всего) | 0,15 макс. |
| Эл | Баланс |
Typical T761 values (converted from source KSI): tensile ≈ 524 MPa (76 ksi), yield ≈ 441 MPa (64 ksi), elongation ≈ 12%, shear ≈ 317 MPa (46 ksi). Confirm against the MTC for your form and thickness.
| Темпер | Темпер | Предел прочности при растяжении (МПа) | Предел текучести (МПа) | Elong. (%) |
|---|---|---|---|---|
| T761 | ≈ 524 | ≈ 441 | ≈ 12 | |
| T7351 | ≈ 510 | ≈ 425 | ≈ 12 |
T761 — peak combination of strength and toughness for skins and structural plate. T7351 — improved stress-corrosion resistance. Both are overaged; not weld-friendly.
Among the toughest 7xxx grades for thick sections.
Suited to cyclic-load aircraft skins.
Not recommended for fusion welding.
Aircraft fuselage and wing skins, high-toughness structural parts, bulkheads, critical military components, aerospace fasteners.
CNC machining and saw cutting supported; anodizing with sealant advised for corrosion service.
Every order ships with an MTC. SGS third-party test reports available on request. Linsy holds ISO 9001, ISO 14001 and ISO 45001.
Linsy Aluminum is a Shenzhen-based supplier with 20+ years of experience across the 1000–8000 series. We supply 7475 sheet, plate, bar and tube with MTC per order and support custom sizes. Typical custom lead time is 10–60 days.
Internal Linsy blog links for 7475 are being added as articles are published.
What tempers does 7475 come in?
T761 and T7351.
7475 vs 7075?
7475 offers higher toughness/fracture resistance; 7075 higher peak strength.
Lead time?
10–60 days for custom sizes.
MTC provided?
Yes, with every order.
Custom sizes?
Yes.
Standards?
AMS, ASTM, GB/T, EN on request.
Преимущества Linsy
Linsy Aluminum - ведущий поставщик продукции для обработки алюминия, обслуживающий различные отрасли промышленности, включая аэрокосмическую, общее машиностроение, автомобильную, морскую, судостроительную и другие специализированные промышленные приложения.
Мы стремимся поддерживать самые высокие стандарты качества и экологической ответственности, о чем свидетельствуют наши сертификаты: ISO 9001:2008, ISO 14001:2004 и SGS.