7475 is a high-strength 7xxx alloy engineered specifically for superior toughness and fracture resistance, even in thicker sections. Commonly supplied in T761 temper for aircraft fuselage and wing skins, it is the preferred choice for critical structures where both strength and durability matter. Linsy supplies 7475 sheet, plate, bar and tube with full MTC documentation.
Formulários disponíveis: sheet / plate / bar / tube / wire
Temperamentos comuns: T761 / T7351
Suporte ao processamento: Usinagem CNC, corte com serra, anodização
Documentos de qualidade: Relatório MTC em cada pedido
7475 is a high-strength 7xxx alloy engineered specifically for superior toughness and fracture resistance, even in thicker sections. Commonly supplied in T761 temper for aircraft fuselage and wing skins, it is the preferred choice for critical structures where both strength and durability matter. Linsy supplies 7475 sheet, plate, bar and tube with full MTC documentation. Its high zinc content gives an outstanding strength-to-toughness combination, making it a staple for aircraft skins and bulkheads.
| Espessura (mm) | Largura (mm) | Comprimento (mm) | Temperamento |
|---|---|---|---|
| 0.5 – 150 | 500 – 2500 | até 12.000 | T761, T7351 |
| Dimensões personalizadas sob consulta | — | — | — |
| Bar Dia. / Tube OD (mm) | Wire (mm) | Comprimento (mm) | Temperamento |
|---|---|---|---|
| 3 – 300 (barra) / 6 – 300 (tubo) | 0.8 – 30 | até 12.000 | T761, T7351 |
| Dimensões personalizadas sob consulta | — | — | — |
7475 is supplied to AMS and ASTM references where applicable (e.g., AMS 4202 for T761 plate). EN AW designation: EN AW-7475. Confirm exact spec with our team.
| Elemento | Conteúdo (%) |
|---|---|
| Si | 0,10 máximo |
| Fe | 0,12 máximo |
| Cu | 1.2 – 1.9 |
| Mn | 0,06 máximo |
| Mg | 1.9 – 2.6 |
| Cr | 0.18 – 0.25 |
| Zn | 5.2 – 6.2 |
| Ti | 0,06 máximo |
| Outros (cada) | 0,05 máximo |
| Outros (total) | 0,15 máximo |
| Al | Equilíbrio |
Typical T761 values (converted from source KSI): tensile ≈ 524 MPa (76 ksi), yield ≈ 441 MPa (64 ksi), elongation ≈ 12%, shear ≈ 317 MPa (46 ksi). Confirm against the MTC for your form and thickness.
| Temperamento | Temperamento | Tração (MPa) | Limite de Escoamento (MPa) | Along. (%) |
|---|---|---|---|---|
| T761 | ≈ 524 | ≈ 441 | ≈ 12 | |
| T7351 | ≈ 510 | ≈ 425 | ≈ 12 |
T761 — peak combination of strength and toughness for skins and structural plate. T7351 — improved stress-corrosion resistance. Both are overaged; not weld-friendly.
Among the toughest 7xxx grades for thick sections.
Suited to cyclic-load aircraft skins.
Não recomendado para soldagem por fusão.
Aircraft fuselage and wing skins, high-toughness structural parts, bulkheads, critical military components, aerospace fasteners.
CNC machining and saw cutting supported; anodizing with sealant advised for corrosion service.
Cada pedido é enviado com um MTC. Relatórios de teste de terceiros SGS disponíveis mediante solicitação. A Linsy possui certificações ISO 9001, ISO 14001 e ISO 45001.
Linsy Aluminum is a Shenzhen-based supplier with 20+ years of experience across the 1000–8000 series. We supply 7475 sheet, plate, bar and tube with MTC per order and support custom sizes. Typical custom lead time is 10–60 days.
Internal Linsy blog links for 7475 are being added as articles are published.
What tempers does 7475 come in?
T761 and T7351.
7475 vs 7075?
7475 offers higher toughness/fracture resistance; 7075 higher peak strength.
Lead time?
10 a 60 dias para dimensões personalizadas.
O MTC é fornecido?
Sim, com cada pedido.
Dimensões personalizadas?
Yes.
Normas?
AMS, ASTM, GB/T, EN on request.
Vantagens da Linsy
A Linsy Aluminum é uma fornecedora líder de produtos de processamento de alumínio, atendendo a diversos setores, incluindo aeroespacial, engenharia geral, automotivo, marítimo, construção naval e outras aplicações industriais especializadas.
Temos o compromisso de manter os mais altos padrões de qualidade e responsabilidade ambiental, conforme demonstrado por nossas certificações: ISO 9001:2008， ISO 14001:2004 e SGS.