7475 is a high-strength 7xxx alloy engineered specifically for superior toughness and fracture resistance, even in thicker sections. Commonly supplied in T761 temper for aircraft fuselage and wing skins, it is the preferred choice for critical structures where both strength and durability matter. Linsy supplies 7475 sheet, plate, bar and tube with full MTC documentation.
Formularios disponibles: sheet / plate / bar / tube / wire
Temperamentos habituales: T761 / T7351
Asistencia técnica: CNC machining, saw cutting, anodizing
Documentos de calidad: Informe MTC con cada pedido
7475 is a high-strength 7xxx alloy engineered specifically for superior toughness and fracture resistance, even in thicker sections. Commonly supplied in T761 temper for aircraft fuselage and wing skins, it is the preferred choice for critical structures where both strength and durability matter. Linsy supplies 7475 sheet, plate, bar and tube with full MTC documentation. Its high zinc content gives an outstanding strength-to-toughness combination, making it a staple for aircraft skins and bulkheads.
| Espesor (mm) | Anchura (mm) | Longitud (mm) | Temple |
|---|---|---|---|
| 0.5 – 150 | 500 – 2500 | up to 12,000 | T761, T7351 |
| Custom sizes on request | — | — | — |
| Bar Dia. / Tube OD (mm) | Wire (mm) | Longitud (mm) | Temple |
|---|---|---|---|
| 3 – 300 (bar) / 6 – 300 (tube) | 0.8 – 30 | up to 12,000 | T761, T7351 |
| Custom sizes on request | — | — | — |
7475 is supplied to AMS and ASTM references where applicable (e.g., AMS 4202 for T761 plate). EN AW designation: EN AW-7475. Confirm exact spec with our team.
| Elemento | Contenido (%) |
|---|---|
| Si | 0,10 máx. |
| Fe | 0,12 máx. |
| Cu | 1.2 – 1.9 |
| Mn | 0,06 máx. |
| Mg | 1.9 – 2.6 |
| Cr | 0.18 – 0.25 |
| Zn | 5.2 – 6.2 |
| Ti | 0,06 máx. |
| Otros (cada uno) | 0,05 máx. |
| Otros (total) | 0,15 máx. |
| Al | Saldo |
Typical T761 values (converted from source KSI): tensile ≈ 524 MPa (76 ksi), yield ≈ 441 MPa (64 ksi), elongation ≈ 12%, shear ≈ 317 MPa (46 ksi). Confirm against the MTC for your form and thickness.
| Temple | Temple | Tracción (MPa) | Límite elástico (MPa) | Elong. (%) |
|---|---|---|---|---|
| T761 | ≈ 524 | ≈ 441 | ≈ 12 | |
| T7351 | ≈ 510 | ≈ 425 | ≈ 12 |
T761 — peak combination of strength and toughness for skins and structural plate. T7351 — improved stress-corrosion resistance. Both are overaged; not weld-friendly.
Among the toughest 7xxx grades for thick sections.
Suited to cyclic-load aircraft skins.
Not recommended for fusion welding.
Aircraft fuselage and wing skins, high-toughness structural parts, bulkheads, critical military components, aerospace fasteners.
CNC machining and saw cutting supported; anodizing with sealant advised for corrosion service.
Every order ships with an MTC. SGS third-party test reports available on request. Linsy holds ISO 9001, ISO 14001 and ISO 45001.
Linsy Aluminum is a Shenzhen-based supplier with 20+ years of experience across the 1000–8000 series. We supply 7475 sheet, plate, bar and tube with MTC per order and support custom sizes. Typical custom lead time is 10–60 days.
Internal Linsy blog links for 7475 are being added as articles are published.
What tempers does 7475 come in?
T761 and T7351.
7475 vs 7075?
7475 offers higher toughness/fracture resistance; 7075 higher peak strength.
Lead time?
10–60 days for custom sizes.
MTC provided?
Yes, with every order.
Custom sizes?
Yes.
Standards?
AMS, ASTM, GB/T, EN on request.