7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
Formularios disponibles: plate, tube, bar / rod
Temperamentos habituales: T73510, T73511, T74, T7451, T7452
Asistencia técnica: Mecanizado CNC, corte por láser, soldadura TIG/MIG, anodizado, pulido, recubrimiento en polvo
Documentos de calidad: Informe MTC con cada pedido
7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
Templetes disponibles: T73510, T73511, T74, T7451, T7452
| Temple | Espesor (mm) | Anchura (mm) | Longitud (mm) |
|---|---|---|---|
| T73510, T73511, T74, T7451, T7452 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (corte a medida) |
Templetes disponibles: T73510, T73511, T7451, T7452
| Temple | Diámetro exterior (mm) | Pared (mm) | Longitud (mm) |
|---|---|---|---|
| T73510, T73511, T7451, T7452 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Templetes disponibles: T73510, T73511, T7451, T7452
| Temple | Diámetro (mm) | Longitud (mm) |
|---|---|---|
| T73510, T73511, T7451, T7452 | 3 – 300 | 500 – 12000 |
7050 aluminum (EN AW-7050, AlZn6CuMgZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Elemento | Porcentaje (%) |
|---|---|
| Si | 0,12 máx. |
| Fe | 0,15 máx. |
| Cu | 2.0 - 2.6 |
| Mn | 0,10 máx. |
| Mg | 1.9 – 2.6 |
| Cr | 0,04 máx. |
| Zn | 5.6 – 6.7 |
| Ti | 0,06 máx. |
| Zr | 0.08 – 0.15 |
| Otros (cada uno) | 0.05 |
| Otros (total) | 0.15 |
| Al | Saldo |
| Temple | Resistencia a la tracción (MPa) | Límite elástico (MPa) | Alargamiento (%) | Resistencia al cizallamiento (MPa) |
|---|---|---|---|---|
| T7451 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
| T73510 / T73511 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
Values are typical for the overaged T7451 / T7351x tempers; confirm exact figures with the mill certificate.
Less quench-sensitive than 7075, so plate stays strong through its depth.
Overaged tempers resist cracking in aggressive service.
Precipitation hardening delivers the specified strength.
Generally supplied as a machined or formed part, not a welded assembly.
Linsy CNC-machines and laser-cuts 7050, then anodizes or paints for corrosion protection. Welding is not recommended; design parts as machined or formed components.
Linsy es un proveedor de aluminio con sede en Shenzhen con más de 20 años de experiencia. Nuestro sistema de calidad está certificado según ISO 9001, ISO 14001 e ISO 45001. Cada pedido se envía con un certificado de prueba de fábrica (MTC). Los informes de pruebas de terceros SGS están disponibles bajo solicitud. El plazo de entrega típico para pedidos personalizados es de 10 a 60 días, según el temple, tamaño y cantidad.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
7050 is less sensitive to quench rate, so it keeps strength better in thick plate, and its overaged tempers resist stress corrosion far better than 7075-T6.
T7451 is the standard for aerospace plate where corrosion resistance matters; T73510/T73511 for extruded sections.
No, it is not a welding grade. Plan for machined or bonded assemblies.
Cada pedido se envía con un MTC, y los informes de pruebas de terceros SGS están disponibles bajo solicitud.
Los pedidos personalizados de aluminio suelen enviarse en 10 a 60 días, según la aleación, temple, tamaño y cantidad. Las existencias o tamaños estándar pueden ser más rápidos — consulte a nuestro equipo.
Sí. Cada pedido incluye un MTC. Los informes de pruebas de terceros SGS están disponibles bajo solicitud.
Sí. Proporcionamos mecanizado CNC, corte por láser, soldadura, anodizado, pulido y recubrimiento en polvo para que las piezas puedan entregarse más cerca de su forma final.
Envíe su aleación, temple, dimensiones, cantidad y norma requerida. Nuestro equipo confirmará disponibilidad, plazo de entrega y precio.
Ventajas de Linsy
Linsy Aluminum es un proveedor líder de productos de procesamiento de aluminio, que presta servicio a diversas industrias, como la aeroespacial, la ingeniería general, la automoción, la marina, la construcción naval y otras aplicaciones industriales especializadas.
Nos comprometemos a mantener los más altos estándares de calidad y responsabilidad medioambiental, como demuestran nuestras certificaciones: ISO 9001:2008， ISO 14001:2004 y SGS.