7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
Formulaires disponibles : plate, tube, bar / rod
Tempéraments courants : T73510, T73511, T74, T7451, T7452
Assistance technique : Usinage CNC, découpe laser, soudage TIG/MIG, anodisation, polissage, revêtement par poudre
Documents relatifs à la qualité : Rapport MTC joint à chaque commande
7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
États disponibles : T73510, T73511, T74, T7451, T7452
| Tempérer | Épaisseur (mm) | Largeur (mm) | Longueur (mm) |
|---|---|---|---|
| T73510, T73511, T74, T7451, T7452 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (découpe sur mesure) |
États disponibles : T73510, T73511, T7451, T7452
| Tempérer | Diamètre extérieur (mm) | Paroi (mm) | Longueur (mm) |
|---|---|---|---|
| T73510, T73511, T7451, T7452 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
États disponibles : T73510, T73511, T7451, T7452
| Tempérer | Diamètre (mm) | Longueur (mm) |
|---|---|---|
| T73510, T73511, T7451, T7452 | 3 – 300 | 500 – 12000 |
7050 aluminum (EN AW-7050, AlZn6CuMgZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Élément | Pourcentage (%) |
|---|---|
| Si | 0,12 max |
| Fe | 0,15 max |
| Cu | 2.0 - 2.6 |
| Mn | 0,10 max |
| Mg | 1.9 – 2.6 |
| Cr | 0,04 max |
| Zn | 5.6 – 6.7 |
| Ti | 0,06 max |
| Zr | 0.08 – 0.15 |
| Autres (chacun) | 0.05 |
| Autres (total) | 0.15 |
| Al | Équilibre |
| Tempérer | Résistance à la traction (MPa) | Limite d'élasticité (MPa) | Élongation (%) | Résistance au cisaillement (MPa) |
|---|---|---|---|---|
| T7451 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
| T73510 / T73511 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
Values are typical for the overaged T7451 / T7351x tempers; confirm exact figures with the mill certificate.
Less quench-sensitive than 7075, so plate stays strong through its depth.
Overaged tempers resist cracking in aggressive service.
Le durcissement par précipitation confère la résistance spécifiée.
Generally supplied as a machined or formed part, not a welded assembly.
Linsy CNC-machines and laser-cuts 7050, then anodizes or paints for corrosion protection. Welding is not recommended; design parts as machined or formed components.
Linsy est un fournisseur d'aluminium basé à Shenzhen avec plus de 20 ans d'expérience. Notre système qualité est certifié ISO 9001, ISO 14001 et ISO 45001. Chaque commande est expédiée avec un certificat d'essai en usine (MTC). Des rapports d'essais tiers SGS sont disponibles sur demande. Le délai de livraison typique pour les commandes personnalisées est de 10 à 60 jours selon l'état, les dimensions et la quantité.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
7050 is less sensitive to quench rate, so it keeps strength better in thick plate, and its overaged tempers resist stress corrosion far better than 7075-T6.
T7451 is the standard for aerospace plate where corrosion resistance matters; T73510/T73511 for extruded sections.
No, it is not a welding grade. Plan for machined or bonded assemblies.
Chaque commande est expédiée avec un MTC, et des rapports d'essais tiers SGS sont disponibles sur demande.
Les commandes d'aluminium personnalisées sont généralement expédiées sous 10 à 60 jours selon l'alliage, l'état, les dimensions et la quantité. Les tailles standard ou en stock peuvent être plus rapides — demandez à notre équipe.
Oui. Chaque commande comprend un MTC. Des rapports d'essais tiers SGS sont disponibles sur demande.
Oui. Nous fournissons l'usinage CNC, la découpe laser, le soudage, l'anodisation, le polissage et le revêtement par poudre afin que les pièces puissent être livrées plus proches de leur forme finie.
Envoyez votre alliage, état, dimensions, quantité et norme requise. Notre équipe confirmera la disponibilité, le délai de livraison et le prix.
Avantages pour Linsy
Linsy Aluminum est un fournisseur de premier plan de produits de transformation de l'aluminium, au service de diverses industries, notamment l'aérospatiale, l'ingénierie générale, l'automobile, la marine, la construction navale et d'autres applications industrielles spécialisées.
Nous nous engageons à respecter les normes les plus strictes en matière de qualité et de responsabilité environnementale, comme en témoignent nos certifications : ISO 9001:2008， ISO 14001:2004 et SGS.