7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
Formulários disponíveis: plate, tube, bar / rod
Temperamentos comuns: T73510, T73511, T74, T7451, T7452
Suporte ao processamento: Usinagem CNC, corte a laser, soldagem TIG/MIG, anodização, polimento, pintura eletrostática
Documentos de qualidade: Relatório MTC em cada pedido
7050 aluminum is a high-strength 7xxx series alloy built around zinc, magnesium, and copper, with zirconium for grain control. It is closely related to 7075 but performs better in thick sections because it is less sensitive to quench rate, so strength is retained deeper into the plate. The T7451 temper gives strong resistance to exfoliation and stress-corrosion cracking, which is why 7050 is a workhorse for aerospace structures such as bulkheads, fuselage frames, and wing skins. Linsy supplies 7050 in plate, tube, and bar with mill test certificates on every order.
Temperos disponíveis: T73510, T73511, T74, T7451, T7452
| Temperamento | Espessura (mm) | Largura (mm) | Comprimento (mm) |
|---|---|---|---|
| T73510, T73511, T74, T7451, T7452 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (corte sob medida) |
Temperos disponíveis: T73510, T73511, T7451, T7452
| Temperamento | Diâmetro externo (mm) | Parede (mm) | Comprimento (mm) |
|---|---|---|---|
| T73510, T73511, T7451, T7452 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Temperos disponíveis: T73510, T73511, T7451, T7452
| Temperamento | Diâmetro (mm) | Comprimento (mm) |
|---|---|---|
| T73510, T73511, T7451, T7452 | 3 – 300 | 500 – 12000 |
7050 aluminum (EN AW-7050, AlZn6CuMgZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Elemento | Porcentagem (%) |
|---|---|
| Si | 0,12 máximo |
| Fe | 0,15 máximo |
| Cu | 2.0 - 2.6 |
| Mn | 0,10 máximo |
| Mg | 1.9 – 2.6 |
| Cr | 0,04 máximo |
| Zn | 5.6 – 6.7 |
| Ti | 0,06 máximo |
| Zr | 0.08 – 0.15 |
| Outros (cada) | 0.05 |
| Outros (total) | 0.15 |
| Al | Equilíbrio |
| Temperamento | Resistência à tração (MPa) | Resistência ao escoamento (MPa) | Alongamento (%) | Resistência ao cisalhamento (MPa) |
|---|---|---|---|---|
| T7451 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
| T73510 / T73511 | 490 – 570 | 390 – 500 | 3.8 – 5.9 | 290 – 330 |
Values are typical for the overaged T7451 / T7351x tempers; confirm exact figures with the mill certificate.
Less quench-sensitive than 7075, so plate stays strong through its depth.
Overaged tempers resist cracking in aggressive service.
O endurecimento por precipitação proporciona a resistência especificada.
Generally supplied as a machined or formed part, not a welded assembly.
Linsy CNC-machines and laser-cuts 7050, then anodizes or paints for corrosion protection. Welding is not recommended; design parts as machined or formed components.
A Linsy é uma fornecedora de alumínio sediada em Shenzhen com mais de 20 anos de experiência. Nosso sistema de qualidade é certificado pelas normas ISO 9001, ISO 14001 e ISO 45001. Cada pedido é enviado com um certificado de ensaio de fábrica (MTC). Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação. O prazo de entrega típico para personalização é de 10 a 60 dias, dependendo do tempero, tamanho e quantidade.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
7050 is less sensitive to quench rate, so it keeps strength better in thick plate, and its overaged tempers resist stress corrosion far better than 7075-T6.
T7451 is the standard for aerospace plate where corrosion resistance matters; T73510/T73511 for extruded sections.
No, it is not a welding grade. Plan for machined or bonded assemblies.
Cada pedido é enviado com um MTC, e relatórios de testes de terceiros SGS estão disponíveis mediante solicitação.
Pedidos personalizados de alumínio geralmente são enviados em 10 a 60 dias, dependendo da liga, tempero, tamanho e quantidade. Estoque ou tamanhos padrão podem ser mais rápidos — pergunte à nossa equipe.
Sim. Cada pedido inclui um MTC. Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação.
Sim. Oferecemos usinagem CNC, corte a laser, soldagem, anodização, polimento e pintura eletrostática a pó, para que as peças possam ser entregues em um estado mais próximo ao acabado.
Envie sua liga, têmpera, dimensões, quantidade e norma exigida. Nossa equipe confirmará a disponibilidade, o prazo de entrega e o preço.