7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
Formulaires disponibles : plate, tube, bar / rod, wire
Tempéraments courants : F, H112, O, T6, T651, T7451, T77, T7751
Assistance technique : Usinage CNC, découpe laser, soudage TIG/MIG, anodisation, polissage, revêtement par poudre
Documents relatifs à la qualité : Rapport MTC joint à chaque commande
7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
États disponibles : F, O, T6, T651, T7451, H112
| Tempérer | Épaisseur (mm) | Largeur (mm) | Longueur (mm) |
|---|---|---|---|
| F, O, T6, T651, T7451, H112 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (découpe sur mesure) |
États disponibles : T77, T7751
| Tempérer | Diamètre extérieur (mm) | Paroi (mm) | Longueur (mm) |
|---|---|---|---|
| T77, T7751 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
États disponibles : T77, T7751
| Tempérer | Diamètre (mm) | Longueur (mm) |
|---|---|---|
| T77, T7751 | 3 – 300 | 500 – 12000 |
États disponibles : T77, T7751
| Diamètre (mm) | Poids de la bobine | Tolérance |
|---|---|---|
| 0.8 – 30 | 50 kg minimum | ± 0,02 mm |
7055 aluminum (EN AW-7055, AlZn8MgCuZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Élément | Pourcentage (%) |
|---|---|
| Si | 0,10 max |
| Fe | 0,15 max |
| Cu | 2.0 - 2.6 |
| Mn | 0,05 max |
| Mg | 1.8 - 2.3 |
| Cr | 0,04 max |
| Zn | 7.6 - 8.4 |
| Ti | 0,06 max |
| Zr | 0.08 - 0.25 |
| Autres (chacun) | 0.05 |
| Autres (total) | 0.15 |
| Al | Équilibre |
| Tempérer | Résistance à la traction (MPa) | Limite d'élasticité (MPa) | Élongation (%) | Résistance au cisaillement (MPa) |
|---|---|---|---|---|
| T7751 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
| T6 / T651 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
Values are typical for the T7751 / T6 tempers. Composition was corrected to AA 7055 limits (see audit report) and must be confirmed with the mill certificate.
Exceeds 7050 and 7075 in compression and fatigue.
Holds up under cyclic load in thick sections.
Overaging balances strength and corrosion.
Supplied as machined or formed parts.
Linsy CNC-machines and laser-cuts 7055, then anodizes or paints for corrosion protection. Welding is not recommended.
Linsy est un fournisseur d'aluminium basé à Shenzhen avec plus de 20 ans d'expérience. Notre système qualité est certifié ISO 9001, ISO 14001 et ISO 45001. Chaque commande est expédiée avec un certificat d'essai en usine (MTC). Des rapports d'essais tiers SGS sont disponibles sur demande. Le délai de livraison typique pour les commandes personnalisées est de 10 à 60 jours selon l'état, les dimensions et la quantité.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
Yes. 7055 is among the strongest commercial 7xxx alloys, with higher compression and fatigue strength, especially in thick sections.
T7751 offers the best balance of strength and stress-corrosion resistance.
No, it is not a welding grade; design as machined or formed parts.
Chaque commande est expédiée avec un MTC, et des rapports d'essais tiers SGS sont disponibles sur demande.
Les commandes d'aluminium personnalisées sont généralement expédiées sous 10 à 60 jours selon l'alliage, l'état, les dimensions et la quantité. Les tailles standard ou en stock peuvent être plus rapides — demandez à notre équipe.
Oui. Chaque commande comprend un MTC. Des rapports d'essais tiers SGS sont disponibles sur demande.
Oui. Nous fournissons l'usinage CNC, la découpe laser, le soudage, l'anodisation, le polissage et le revêtement par poudre afin que les pièces puissent être livrées plus proches de leur forme finie.
Envoyez votre alliage, état, dimensions, quantité et norme requise. Notre équipe confirmera la disponibilité, le délai de livraison et le prix.
Avantages pour Linsy
Linsy Aluminum est un fournisseur de premier plan de produits de transformation de l'aluminium, au service de diverses industries, notamment l'aérospatiale, l'ingénierie générale, l'automobile, la marine, la construction navale et d'autres applications industrielles spécialisées.
Nous nous engageons à respecter les normes les plus strictes en matière de qualité et de responsabilité environnementale, comme en témoignent nos certifications : ISO 9001:2008， ISO 14001:2004 et SGS.