7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
Formulários disponíveis: plate, tube, bar / rod, wire
Temperamentos comuns: F, H112, O, T6, T651, T7451, T77, T7751
Suporte ao processamento: Usinagem CNC, corte a laser, soldagem TIG/MIG, anodização, polimento, pintura eletrostática
Documentos de qualidade: Relatório MTC em cada pedido
7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
Temperos disponíveis: F, O, T6, T651, T7451, H112
| Temperamento | Espessura (mm) | Largura (mm) | Comprimento (mm) |
|---|---|---|---|
| F, O, T6, T651, T7451, H112 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (corte sob medida) |
Temperos disponíveis: T77, T7751
| Temperamento | Diâmetro externo (mm) | Parede (mm) | Comprimento (mm) |
|---|---|---|---|
| T77, T7751 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Temperos disponíveis: T77, T7751
| Temperamento | Diâmetro (mm) | Comprimento (mm) |
|---|---|---|
| T77, T7751 | 3 – 300 | 500 – 12000 |
Temperos disponíveis: T77, T7751
| Diâmetro (mm) | Peso da bobina | Tolerância |
|---|---|---|
| 0.8 – 30 | Mínimo de 50 kg | ± 0,02 mm |
7055 aluminum (EN AW-7055, AlZn8MgCuZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Elemento | Porcentagem (%) |
|---|---|
| Si | 0,10 máximo |
| Fe | 0,15 máximo |
| Cu | 2.0 - 2.6 |
| Mn | 0,05 máximo |
| Mg | 1.8 - 2.3 |
| Cr | 0,04 máximo |
| Zn | 7.6 - 8.4 |
| Ti | 0,06 máximo |
| Zr | 0.08 - 0.25 |
| Outros (cada) | 0.05 |
| Outros (total) | 0.15 |
| Al | Equilíbrio |
| Temperamento | Resistência à tração (MPa) | Resistência ao escoamento (MPa) | Alongamento (%) | Resistência ao cisalhamento (MPa) |
|---|---|---|---|---|
| T7751 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
| T6 / T651 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
Values are typical for the T7751 / T6 tempers. Composition was corrected to AA 7055 limits (see audit report) and must be confirmed with the mill certificate.
Exceeds 7050 and 7075 in compression and fatigue.
Holds up under cyclic load in thick sections.
Overaging balances strength and corrosion.
Supplied as machined or formed parts.
Linsy CNC-machines and laser-cuts 7055, then anodizes or paints for corrosion protection. Welding is not recommended.
A Linsy é uma fornecedora de alumínio sediada em Shenzhen com mais de 20 anos de experiência. Nosso sistema de qualidade é certificado pelas normas ISO 9001, ISO 14001 e ISO 45001. Cada pedido é enviado com um certificado de ensaio de fábrica (MTC). Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação. O prazo de entrega típico para personalização é de 10 a 60 dias, dependendo do tempero, tamanho e quantidade.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
Yes. 7055 is among the strongest commercial 7xxx alloys, with higher compression and fatigue strength, especially in thick sections.
T7751 offers the best balance of strength and stress-corrosion resistance.
No, it is not a welding grade; design as machined or formed parts.
Cada pedido é enviado com um MTC, e relatórios de testes de terceiros SGS estão disponíveis mediante solicitação.
Pedidos personalizados de alumínio geralmente são enviados em 10 a 60 dias, dependendo da liga, tempero, tamanho e quantidade. Estoque ou tamanhos padrão podem ser mais rápidos — pergunte à nossa equipe.
Sim. Cada pedido inclui um MTC. Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação.
Sim. Oferecemos usinagem CNC, corte a laser, soldagem, anodização, polimento e pintura eletrostática a pó, para que as peças possam ser entregues em um estado mais próximo ao acabado.
Envie sua liga, têmpera, dimensões, quantidade e norma exigida. Nossa equipe confirmará a disponibilidade, o prazo de entrega e o preço.
Vantagens da Linsy
A Linsy Aluminum é uma fornecedora líder de produtos de processamento de alumínio, atendendo a diversos setores, incluindo aeroespacial, engenharia geral, automotivo, marítimo, construção naval e outras aplicações industriais especializadas.
Temos o compromisso de manter os mais altos padrões de qualidade e responsabilidade ambiental, conforme demonstrado por nossas certificações: ISO 9001:2008， ISO 14001:2004 e SGS.