7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
Formularios disponibles: plate, tube, bar / rod, wire
Temperamentos habituales: F, H112, O, T6, T651, T7451, T77, T7751
Asistencia técnica: Mecanizado CNC, corte por láser, soldadura TIG/MIG, anodizado, pulido, recubrimiento en polvo
Documentos de calidad: Informe MTC con cada pedido
7055 aluminum is one of the highest-strength 7xxx series alloys, with very high zinc plus copper, magnesium, and zirconium. It was developed to exceed 7050 and 7075 in compression strength and fatigue performance, especially in thick sections, and is used for the most demanding aerospace structures. The T7751 temper provides an excellent balance of strength and corrosion resistance. Linsy supplies 7055 in plate, tube, bar, and wire with mill test certificates on every order. Composition values below follow the AA standard and should be confirmed against the mill certificate.
Templetes disponibles: F, O, T6, T651, T7451, H112
| Temple | Espesor (mm) | Anchura (mm) | Longitud (mm) |
|---|---|---|---|
| F, O, T6, T651, T7451, H112 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (corte a medida) |
Templetes disponibles: T77, T7751
| Temple | Diámetro exterior (mm) | Pared (mm) | Longitud (mm) |
|---|---|---|---|
| T77, T7751 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Templetes disponibles: T77, T7751
| Temple | Diámetro (mm) | Longitud (mm) |
|---|---|---|
| T77, T7751 | 3 – 300 | 500 – 12000 |
Templetes disponibles: T77, T7751
| Diámetro (mm) | Peso de la bobina | Tolerancia |
|---|---|---|
| 0.8 – 30 | Mín. 50 kg | ± 0,02 mm |
7055 aluminum (EN AW-7055, AlZn8MgCuZr) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Elemento | Porcentaje (%) |
|---|---|
| Si | 0,10 máx. |
| Fe | 0,15 máx. |
| Cu | 2.0 - 2.6 |
| Mn | 0,05 máx. |
| Mg | 1.8 - 2.3 |
| Cr | 0,04 máx. |
| Zn | 7.6 - 8.4 |
| Ti | 0,06 máx. |
| Zr | 0.08 - 0.25 |
| Otros (cada uno) | 0.05 |
| Otros (total) | 0.15 |
| Al | Saldo |
| Temple | Resistencia a la tracción (MPa) | Límite elástico (MPa) | Alargamiento (%) | Resistencia al cizallamiento (MPa) |
|---|---|---|---|---|
| T7751 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
| T6 / T651 | 570 – 600 | 520 – 550 | 10 – 12 | 150 – 340 |
Values are typical for the T7751 / T6 tempers. Composition was corrected to AA 7055 limits (see audit report) and must be confirmed with the mill certificate.
Exceeds 7050 and 7075 in compression and fatigue.
Holds up under cyclic load in thick sections.
Overaging balances strength and corrosion.
Supplied as machined or formed parts.
Linsy CNC-machines and laser-cuts 7055, then anodizes or paints for corrosion protection. Welding is not recommended.
Linsy es un proveedor de aluminio con sede en Shenzhen con más de 20 años de experiencia. Nuestro sistema de calidad está certificado según ISO 9001, ISO 14001 e ISO 45001. Cada pedido se envía con un certificado de prueba de fábrica (MTC). Los informes de pruebas de terceros SGS están disponibles bajo solicitud. El plazo de entrega típico para pedidos personalizados es de 10 a 60 días, según el temple, tamaño y cantidad.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
Yes. 7055 is among the strongest commercial 7xxx alloys, with higher compression and fatigue strength, especially in thick sections.
T7751 offers the best balance of strength and stress-corrosion resistance.
No, it is not a welding grade; design as machined or formed parts.
Cada pedido se envía con un MTC, y los informes de pruebas de terceros SGS están disponibles bajo solicitud.
Los pedidos personalizados de aluminio suelen enviarse en 10 a 60 días, según la aleación, temple, tamaño y cantidad. Las existencias o tamaños estándar pueden ser más rápidos — consulte a nuestro equipo.
Sí. Cada pedido incluye un MTC. Los informes de pruebas de terceros SGS están disponibles bajo solicitud.
Sí. Proporcionamos mecanizado CNC, corte por láser, soldadura, anodizado, pulido y recubrimiento en polvo para que las piezas puedan entregarse más cerca de su forma final.
Envíe su aleación, temple, dimensiones, cantidad y norma requerida. Nuestro equipo confirmará disponibilidad, plazo de entrega y precio.
Ventajas de Linsy
Linsy Aluminum es un proveedor líder de productos de procesamiento de aluminio, que presta servicio a diversas industrias, como la aeroespacial, la ingeniería general, la automoción, la marina, la construcción naval y otras aplicaciones industriales especializadas.
Nos comprometemos a mantener los más altos estándares de calidad y responsabilidad medioambiental, como demuestran nuestras certificaciones: ISO 9001:2008， ISO 14001:2004 y SGS.