7053 aluminum is a high-strength 7xxx series alloy with high zinc and copper content, developed for demanding structural use where strength and durability matter. It offers tensile levels above many common aerospace grades and is specified for aircraft structures and heavy-duty components that must hold up under sustained stress. Linsy supplies 7053 in plate, tube, bar, and wire with mill test certificates on every order.
Formulários disponíveis: plate, tube, bar / rod, wire
Temperamentos comuns: T7451, T77, T7751
Suporte ao processamento: Usinagem CNC, corte a laser, soldagem TIG/MIG, anodização, polimento, pintura eletrostática
Documentos de qualidade: Relatório MTC em cada pedido
7053 aluminum is a high-strength 7xxx series alloy with high zinc and copper content, developed for demanding structural use where strength and durability matter. It offers tensile levels above many common aerospace grades and is specified for aircraft structures and heavy-duty components that must hold up under sustained stress. Linsy supplies 7053 in plate, tube, bar, and wire with mill test certificates on every order.
Temperos disponíveis: T7451
| Temperamento | Espessura (mm) | Largura (mm) | Comprimento (mm) |
|---|---|---|---|
| T7451 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (corte sob medida) |
Temperos disponíveis: T7451
| Temperamento | Diâmetro externo (mm) | Parede (mm) | Comprimento (mm) |
|---|---|---|---|
| T7451 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Temperos disponíveis: T7451
| Temperamento | Diâmetro (mm) | Comprimento (mm) |
|---|---|---|
| T7451 | 3 – 300 | 500 – 12000 |
Temperos disponíveis: T77, T7751
| Diâmetro (mm) | Peso da bobina | Tolerância |
|---|---|---|
| 0.8 – 30 | Mínimo de 50 kg | ± 0,02 mm |
7053 aluminum (EN AW-7053, AlZn6.5Mg1.3Cu) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Elemento | Porcentagem (%) |
|---|---|
| Si | 0,15 máximo |
| Fe | 0,15 máximo |
| Cu | 2.0 - 2.6 |
| Mn | 0,30 máx |
| Mg | 1.9 – 2.6 |
| Cr | 0,10 máximo |
| Zn | 5.6 – 6.7 |
| Ti | 0,10 máximo |
| Zr | 0.08 – 0.15 |
| Outros (cada) | 0.05 |
| Outros (total) | 0.15 |
| Al | Equilíbrio |
| Temperamento | Resistência à tração (MPa) | Resistência ao escoamento (MPa) | Alongamento (%) | Resistência ao cisalhamento (MPa) |
|---|---|---|---|---|
| T7451 | 550 – 580 | 480 – 510 | 10 – 12 | 150 – 340 |
| T77 / T7751 | 550 – 580 | 480 – 510 | 10 – 12 | 150 – 340 |
Values are typical for the overaged T7451 / T7751 tempers. The wide shear range in the source should be confirmed with the mill certificate.
Tensile above many common aerospace alloys.
Overaged tempers suit demanding service.
Precipitation hardened to specification.
Supplied as machined or formed parts.
Linsy machines and laser-cuts 7053 and applies anodizing or painting for corrosion protection. Welding is not recommended.
A Linsy é uma fornecedora de alumínio sediada em Shenzhen com mais de 20 anos de experiência. Nosso sistema de qualidade é certificado pelas normas ISO 9001, ISO 14001 e ISO 45001. Cada pedido é enviado com um certificado de ensaio de fábrica (MTC). Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação. O prazo de entrega típico para personalização é de 10 a 60 dias, dependendo do tempero, tamanho e quantidade.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
Aircraft and heavy-duty structural parts where strength above common grades is required.
Plate in T7451; wire and extrusions in T77 / T7751 overaged tempers.
No, it is a machined-part alloy rather than a welding grade.
Cada pedido é enviado com um MTC, e relatórios de testes de terceiros SGS estão disponíveis mediante solicitação.
Pedidos personalizados de alumínio geralmente são enviados em 10 a 60 dias, dependendo da liga, tempero, tamanho e quantidade. Estoque ou tamanhos padrão podem ser mais rápidos — pergunte à nossa equipe.
Sim. Cada pedido inclui um MTC. Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação.
Sim. Oferecemos usinagem CNC, corte a laser, soldagem, anodização, polimento e pintura eletrostática a pó, para que as peças possam ser entregues em um estado mais próximo ao acabado.
Envie sua liga, têmpera, dimensões, quantidade e norma exigida. Nossa equipe confirmará a disponibilidade, o prazo de entrega e o preço.
Vantagens da Linsy
A Linsy Aluminum é uma fornecedora líder de produtos de processamento de alumínio, atendendo a diversos setores, incluindo aeroespacial, engenharia geral, automotivo, marítimo, construção naval e outras aplicações industriais especializadas.
Temos o compromisso de manter os mais altos padrões de qualidade e responsabilidade ambiental, conforme demonstrado por nossas certificações: ISO 9001:2008， ISO 14001:2004 e SGS.