7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
Formulários disponíveis: chapa / placa, tubo, barra / haste, fio
Temperamentos comuns: T4, T6, T651
Suporte ao processamento: Usinagem CNC, corte a laser, soldagem TIG/MIG, anodização, polimento, pintura eletrostática
Documentos de qualidade: Relatório MTC em cada pedido
7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
Temperos disponíveis: T4, T6, T651
| Temperamento | Espessura (mm) | Largura (mm) | Comprimento (mm) |
|---|---|---|---|
| T4, T6, T651 | 0.5 – 150 | 500 – 2600 | 500 – 16000 (corte sob medida) |
Temperos disponíveis: T4, T6, T651
| Temperamento | Diâmetro externo (mm) | Parede (mm) | Comprimento (mm) |
|---|---|---|---|
| T4, T6, T651 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Temperos disponíveis: T4, T6, T651
| Temperamento | Diâmetro (mm) | Comprimento (mm) |
|---|---|---|
| T4, T6, T651 | 3 – 300 | 500 – 12000 |
Temperos disponíveis: T6
| Diâmetro (mm) | Peso da bobina | Tolerância |
|---|---|---|
| 0.8 – 30 | Mínimo de 50 kg | ± 0,02 mm |
7014 aluminum (EN AW-7014, AlZn5.7Mg2.7Mn) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Elemento | Porcentagem (%) |
|---|---|
| Si | 0,50 máx |
| Fe | 0,50 máx |
| Cu | 0,10 máximo |
| Mn | 0,10 máximo |
| Mg | 2.2 – 3.3 |
| Cr | 0.05 – 0.30 |
| Zn | 5.2 – 6.2 |
| Ti | 0,15 máximo |
| Zr | 0,10 máximo |
| Outros (cada) | 0.05 |
| Outros (total) | 0.15 |
| Al | Equilíbrio |
| Temperamento | Resistência à tração (MPa) | Resistência ao escoamento (MPa) | Alongamento (%) | Resistência ao cisalhamento (MPa) |
|---|---|---|---|---|
| T6 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
| T651 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
Os valores são típicos para a condição indicada. Um travessão (—) indica que o valor não estava disponível nos dados de origem; confirme com o certificado de fábrica. Valores com asterisco são estimativas pendentes de verificação — consulte o relatório de auditoria.
T6 temper reaches 480–520 MPa ultimate tensile strength while staying light.
Better fracture toughness than many higher-zinc 7xxx grades, suited to airframe loads.
Satisfactory in internal structures; exterior use should be clad or anodized.
Responds strongly to precipitation hardening for tailored strength.
Weldable with care;confirm a qualified procedure and post-weld heat treatment with our team.
Linsy machines 7014 on CNC centers and cuts it with fiber laser. For corrosion protection, anodizing or painting is recommended on exposed surfaces. Welding should use a qualified procedure with filler selected for the service environment; post-weld heat treatment can be discussed with our engineers.
A Linsy é uma fornecedora de alumínio sediada em Shenzhen com mais de 20 anos de experiência. Nosso sistema de qualidade é certificado pelas normas ISO 9001, ISO 14001 e ISO 45001. Cada pedido é enviado com um certificado de ensaio de fábrica (MTC). Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação. O prazo de entrega típico para personalização é de 10 a 60 dias, dependendo do tempero, tamanho e quantidade.
Para leitura aprofundada sobre seleção e fabricação da série 7xxx, consulte nossos guias sobre seleção de ligas de alumínio e soldagem de ligas da série 7000. (Links internos a serem conectados a artigos publicados no blog da Linsy.)
Common tempers are T4, T6, and T651. T651 is stress-relieved for reduced distortion during machining. Tell us your application and we will recommend a temper.
It can be welded with a qualified procedure, but strength in the heat-affected zone drops. We recommend confirming the welding process and any post-weld treatment with our technical team before production.
7014 offers slightly lower peak strength than 7075 but generally better toughness, making it a good choice for airframe structures where damage tolerance matters.
Every order ships with a mill test certificate (MTC). SGS third-party test reports are available on request.
Pedidos personalizados de alumínio geralmente são enviados em 10 a 60 dias, dependendo da liga, tempero, tamanho e quantidade. Estoque ou tamanhos padrão podem ser mais rápidos — pergunte à nossa equipe.
Sim. Cada pedido inclui um MTC. Relatórios de testes de terceiros SGS estão disponíveis mediante solicitação.
Sim. Oferecemos usinagem CNC, corte a laser, soldagem, anodização, polimento e pintura eletrostática a pó, para que as peças possam ser entregues em um estado mais próximo ao acabado.
Envie sua liga, têmpera, dimensões, quantidade e norma exigida. Nossa equipe confirmará a disponibilidade, o prazo de entrega e o preço.