5657 aluminum is a non-heat-treatable 5xxx alloy with about 1 percent magnesium, known for its excellent anodizing characteristics. It combines good corrosion resistance with moderate strength and is particularly popular where surface finish and aesthetic appeal are important, such as architectural trim, building facades, and consumer product casings.
Mevcut formlar: levha / plaka / bobin / çubuk / boru / ekstrüde profil
Yaygın temperler: O, H25, H28, and H38
İşleme desteği: CNC işleme / lazer kesim / parlatma / eloksal
Kalite belgeleri: Her siparişle birlikte MTC raporu
5657 is a non-heat-treatable 5xxx alloy with about 1 percent magnesium, developed for high-quality anodized surfaces. It provides an excellent anodizing response, good corrosion resistance, and moderate strength, and is widely used for decorative and architectural finishes.
Linsy supplies 5657 mainly as sheet and coil for anodized decorative finishes, with bar and profiles available on request. The tempers most commonly supplied are O, H25, H28, and H38. Aşağıdaki boyutlar tipik aralıklardır; talep üzerine diğer boyutlar görüşülebilir.
5657 is supplied primarily as thin-gauge sheet and coil in thicknesses from 0.3 mm to 4 mm, widths up to 2000 mm, and lengths up to 6000 mm or cut to size.
Thick plate is not a standard 5657 product; thin rolled coil and sheet are the typical forms. Other gauges can be discussed on request.
Round, flat, and square bars can be produced in diameters or side lengths from 6 mm to 200 mm, normally in O or H25.
5657 tube can be supplied in outer diameters from 6 mm to 200 mm with wall thicknesses from 0.5 mm to 20 mm, usually in O or H25 temper.
Extruded and drawn profiles for trim are available on request.
5657 is identified by the following common standards and designations.
| Standart | Tanımlama |
|---|---|
| AA | 5657 |
| UNS | A95657 |
| EN AW | EN AW-AlMg1 |
The typical composition of 5657 aluminum is listed below in weight percent, with aluminum as the balance.
| Element | Kompozisyon (%) |
|---|---|
| Silisyum (Si) | 0,25 maks. |
| Demir (Fe) | 0,40 maks |
| Bakır (Cu) | 0,10 maks. |
| Manganez (Mn) | 0.15 – 0.35 |
| Magnezyum (Mg) | 0,8 – 1,2 |
| Krom (Cr) | 0,05 maks. |
| Çinko (Zn) | 0,10 maks. |
| Titanyum (Ti) | 0.03 max |
| Diğerleri her biri | 0.05 |
| Diğerleri toplam | 0.15 |
| Alüminyum (Al) | Denge |
Aşağıdaki değerler haddelenmiş ve ekstrüde ürünler için tipiktir ve sipariş edilen spesifik temper ve kalınlık için fabrika test sertifikası ile teyit edilmelidir.
| Temper | Çekme Dayanımı (MPa) | Akma Dayanımı (MPa) | Uzama (%) |
|---|---|---|---|
| O | 115 – 160 | 45 min | 18 |
| H25 | 180 – 220 | 150 min | 8 |
| H28 | 215 – 260 | 180 min | 5 |
| H38 | 230 – 270 | 200 min | 4 |
Choose O or H25 for bright decorative trim that is formed before anodizing; H28 and H38 give higher strength for anodized parts that are not heavily formed.
5657 is valued for a clear, consistent, and attractive anodized finish, its main selection reason.
Corrosion behavior is good for interior and architectural exposure.
In O and H25 tempers it forms and bends well for panels and trim.
Strength is moderate; the grade is chosen for appearance more than load capacity.
5657 is most often supplied for anodizing and polishing; surface preparation before finishing is important. It can be cut, bent, and CNC machined. It is non-heat-treatable, so no solution heat treatment is involved.
Linsy, her sevkiyatta, geçerli olduğu durumlarda EN 10204 3.1'e göre kimyasal bileşim ve mekanik özellikleri belgeleyen bir fabrika test sertifikası (MTC) sağlar. Talep üzerine üçüncü taraf muayenesi ve SGS malzeme test raporları düzenlenebilir. Üretim, ISO 9001 (kalite), ISO 14001 (çevre) ve ISO 45001 (iş sağlığı ve güvenliği) sistemleri altında yönetilir.
Linsy Aluminum operates a production and processing base with over 20 years of experience across the 1xxx to 8xxx aluminum series. For 5657, we supply sheet, plate, bar, tube, and extruded profiles with optional CNC machining, laser cutting, and surface finishing such as anodizing and polishing. Every order is shipped with a mill test certificate (MTC), and production follows ISO 9001, ISO 14001, and ISO 45001 management systems. Custom dimensions and tempers can be arranged, with typical lead times of 10 to 60 days depending on the specification.
Its low magnesium content and clean composition give a uniform, bright anodized surface that higher-magnesium grades cannot achieve.
No. It is a non-heat-treatable 5xxx alloy; tempers are O and H-strain-hardened only.
5005 is the most common anodizing grade; 5657 and 5457 are selected for brighter or formed decorative trim. Confirm the exact spec with our team.
Yes for architectural trim, though in aggressive marine environments a higher-magnesium grade may be preferred for corrosion reasons.
Minimum sipariş miktarları, forma ve tempere bağlıdır. Standart stok kalemleri genellikle birkaç yüz kilogramdan başlarken, özel ebatlar her talep için fiyatlandırılır.
Standart spesifikasyonlar genellikle 10 ila 60 gün içinde temin edilebilir. Özel temperler veya ebatlar daha uzun sürebilir; her teklifle birlikte bir tarih onaylarız.
Her siparişe bir fabrika test sertifikası (MTC) dahildir. Üretim, ISO 9001, ISO 14001 ve ISO 45001 sistem sertifikalarına sahiptir ve talep üzerine SGS veya üçüncü taraf test raporları tedarik edilebilir.
Evet. Linsy, kesilmiş ölçü, özel ebatlar ve seçili temperleri destekler. Teklif için çiziminizi veya spesifikasyonunuzu paylaşın.
Ürünler, nakliye sırasında yüzey hasarını önlemek için paketlenir; ihracat standartlarına uygun deniz yoluyla nakliyeye uygun ambalaj mevcuttur.
Linsy Avantajları
Linsy Alüminyum, havacılık, genel mühendislik, otomotiv, denizcilik, gemi yapımı ve diğer özel endüstriyel uygulamalar dahil olmak üzere çeşitli endüstrilere hizmet veren lider bir alüminyum işleme ürünleri tedarikçisidir.
Sertifikalarımızın da gösterdiği gibi, en yüksek kalite ve çevresel sorumluluk standartlarını sürdürmeye kararlıyız: ISO 9001:2008 ， ISO 14001:2004 ve SGS.