7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
Mevcut formlar: sheet / plate, tube, bar / rod, wire
Yaygın temperler: T4, T6, T651
İşleme desteği: CNC işleme, lazer kesim, TIG/MIG kaynağı, eloksal, parlatma, toz boya
Kalite belgeleri: Her siparişle birlikte MTC raporu
7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
Mevcut temperler: T4, T6, T651
| Temper | Kalınlık (mm) | Genişlik (mm) | Uzunluk (mm) |
|---|---|---|---|
| T4, T6, T651 | 0.5 – 150 | 500 – 2600 | 500 – 16000 (boydan boya kesilmiş) |
Mevcut temperler: T4, T6, T651
| Temper | Dış Çap (mm) | Et Kalınlığı (mm) | Uzunluk (mm) |
|---|---|---|---|
| T4, T6, T651 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Mevcut temperler: T4, T6, T651
| Temper | Çap (mm) | Uzunluk (mm) |
|---|---|---|
| T4, T6, T651 | 3 – 300 | 500 – 12000 |
Mevcut temperler: T6
| Çap (mm) | Bobin ağırlığı | Tolerans |
|---|---|---|
| 0.8 – 30 | Min 50 kg | ± 0,02 mm |
7014 aluminum (EN AW-7014, AlZn5.7Mg2.7Mn) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Element | Yüzde (%) |
|---|---|
| Si | 0.50 max |
| Fe | 0.50 max |
| Cu | 0,10 maks. |
| Mn | 0,10 maks. |
| Mg | 2.2 – 3.3 |
| Cr | 0.05 – 0.30 |
| Zn | 5.2 – 6.2 |
| Ti | 0,15 maks. |
| Zr | 0,10 maks. |
| Diğerleri (her biri) | 0.05 |
| Diğerleri (toplam) | 0.15 |
| Al | Denge |
| Temper | Çekme Dayanımı (MPa) | Akma Dayanımı (MPa) | Uzama (%) | Kesme Dayanımı (MPa) |
|---|---|---|---|---|
| T6 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
| T651 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
Değerler belirtilen durum için tipiktir. Uzun çizgi (—), kaynak verilerinde değerin bulunmadığı anlamına gelir; fabrika sertifikası ile teyit edin. Yıldızlı değerler, doğrulama bekleyen tahminlerdir — denetim raporuna bakın.
T6 temper reaches 480–520 MPa ultimate tensile strength while staying light.
Better fracture toughness than many higher-zinc 7xxx grades, suited to airframe loads.
Satisfactory in internal structures; exterior use should be clad or anodized.
Responds strongly to precipitation hardening for tailored strength.
Weldable with care;confirm a qualified procedure and post-weld heat treatment with our team.
Linsy machines 7014 on CNC centers and cuts it with fiber laser. For corrosion protection, anodizing or painting is recommended on exposed surfaces. Welding should use a qualified procedure with filler selected for the service environment; post-weld heat treatment can be discussed with our engineers.
Linsy, Shenzhen merkezli, 20 yılı aşkın deneyime sahip bir alüminyum tedarikçisidir. Kalite sistemimiz ISO 9001, ISO 14001 ve ISO 45001 ile sertifikalıdır. Her sipariş, bir fabrika test sertifikası (MTC) ile gönderilir. Talep üzerine SGS üçüncü taraf test raporları mevcuttur. Tipik özel teslim süresi, temper, boyut ve miktara bağlı olarak 10–60 gündür.
7xxx seçimi ve imalatı hakkında daha derinlemesine bilgi için, alüminyum alaşımı seçimi ve 7000 serisi alaşımların kaynağı konulu rehberlerimize bakın. (Yayınlanan Linsy blog makalelerine bağlanacak dahili bağlantılar.)
Common tempers are T4, T6, and T651. T651 is stress-relieved for reduced distortion during machining. Tell us your application and we will recommend a temper.
It can be welded with a qualified procedure, but strength in the heat-affected zone drops. We recommend confirming the welding process and any post-weld treatment with our technical team before production.
7014 offers slightly lower peak strength than 7075 but generally better toughness, making it a good choice for airframe structures where damage tolerance matters.
Every order ships with a mill test certificate (MTC). SGS third-party test reports are available on request.
Özel alüminyum siparişleri, alaşım, temper, boyut ve miktara bağlı olarak genellikle 10–60 gün içinde gönderilir. Stok veya standart boyutlar daha hızlı olabilir — ekibimize sorun.
Evet. Her sipariş bir MTC içerir. Talep üzerine SGS üçüncü taraf test raporları mevcuttur.
Evet. CNC işleme, lazer kesim, kaynak, eloksal, parlatma ve toz boya sağlıyoruz, böylece parçalar bitmiş forma daha yakın teslim edilebilir.
Alaşım, temper, boyutlar, miktar ve gerekli standardı gönderin. Ekibimiz stok durumunu, teslim süresini ve fiyatlandırmayı teyit edecektir.
Linsy Avantajları
Linsy Alüminyum, havacılık, genel mühendislik, otomotiv, denizcilik, gemi yapımı ve diğer özel endüstriyel uygulamalar dahil olmak üzere çeşitli endüstrilere hizmet veren lider bir alüminyum işleme ürünleri tedarikçisidir.
Sertifikalarımızın da gösterdiği gibi, en yüksek kalite ve çevresel sorumluluk standartlarını sürdürmeye kararlıyız: ISO 9001:2008 ， ISO 14001:2004 ve SGS.