8009 alumínio (also referenced as FVS121 / AlFe8.7Si1.8V1.3) is a dispersion-strengthened 8000-series alloy built around a fine iron–silicon–vanadium intermetallic network rather than traditional age hardening. This gives it high strength that is retained at elevated temperatures, plus good fatigue resistance. Linsy supplies 8009 in O, T6, and T8 tempers across sheet, bar, and tube, with custom dimensions and MTC documentation for every order.
Formulários disponíveis: sheet / plate / bar / tube / wire
Temperamentos comuns: O / T6 / T8
Suporte ao processamento: CNC machining / laser cutting / polishing / anodizing
Documentos de qualidade: Relatório MTC em cada pedido
8009 is a powder-metallurgy-derived dispersion-strengthened alloy whose strength comes from a uniform dispersion of thermally stable Al–Fe–Si–V intermetallics. Unlike 2xxx/7xxx alloys, its strength does not collapse at moderately high service temperatures, making it attractive for aerospace and engine-adjacent structural parts. It is not a lithium-bearing alloy; its chemistry is iron–silicon–vanadium based.
As faixas típicas de produção estão listadas abaixo; dimensões personalizadas estão disponíveis mediante solicitação.
| Formulário | Temperamento | Dimensão | Faixa | Observação |
|---|---|---|---|---|
| Sheet & Coil | O, T6, T8 | Espessura | 0.5 – 100 mm | Custom widths/lengths |
| Placa | O, T6, T8 | Espessura | 6 – 150 mm | Quarto |
| Barra redonda | O, T6, T8 | Diâmetro | 6 – 300 mm | Corte sob medida |
| Tubo | O, T6, T8 | Diâmetro externo | 10 – 300 mm | Wall 1 – 30 mm |
| Fio | O, T6, T8 | Diâmetro | 0.8 – 30 mm | Coil weight ≥ 50 kg |
| Elemento | Composição (%) |
|---|---|
| Ferro (Fe) | 8.0 – 9.5 |
| Silício (Si) | 1.5 – 2.1 |
| Vanádio (V) | 1.0 – 1.6 |
| Cobre (Cu) | 0,05 máximo |
| Magnésio (Mg) | 0,05 máximo |
| Manganês (Mn) | 0,05 máximo |
| Zinco (Zn) | 0,05 máximo |
| Titânio (Ti) | 0,05 máximo |
| Outros (cada) | 0,05 máximo |
| Outros (total) | 0,15 máximo |
| Alumínio (Al) | Restante |
| Temperamento | Resistência à tração (MPa) | Resistência ao escoamento (MPa) | Alongamento (%) | Observação |
|---|---|---|---|---|
| O | 350 – 420 | 200 – 280 | 12 – 18 | Recozido |
| T6 | 520 – 590 | 460 – 540 | 7 – 11 | Peak strength |
| T8 | 540 – 600 | 480 – 550 | 6 – 10 | Cold-worked + aged |
The dispersed intermetallics resist coarsening, so strength holds up better than age-hardened alloys at elevated temperature.
Good fatigue performance supports rotating and cyclic-load aerospace components.
Generally good corrosion resistance; welding is possible but reduces the dispersion-strengthened benefit — confirm with engineering for critical parts.
8009 machines comparably to other high-strength aluminum grades. Because its strength derives from dispersion rather than precipitation, prolonged exposure above roughly 200–250°C should be reviewed with engineering. Standard anodizing and polishing are applicable.
Isolamento e revestimento de cabos.
O 8011 é adequado para corte longitudinal, estampagem profunda e laminação. Tratamentos de superfície, como revestimento ou impressão, são comuns para embalagens. Não é uma liga estrutural e não deve ser especificada onde se espera alta carga mecânica.
Certificação e Padrões:.
No. 8009 is an iron–silicon–vanadium dispersion-strengthened alloy, not an Al-Li alloy. Some sources confuse it with 8090; the chemistry here follows the AA 8009 (AlFeSiV) designation.
8009 keeps more strength at elevated temperature, while 7075 peaks higher at room temperature. Choice depends on service temperature and fatigue needs.
Welding is possible but softens the dispersion-strengthened structure; evaluate for non-critical joints or use mechanical fastening.
Tamanhos padrão geralmente estão disponíveis entre 10 e 60 dias, dependendo da liga, têmpera e volume do pedido. Confirme o prazo exato com nossa equipe de vendas ao solicitar um orçamento.
Sim. Cortamos conforme espessura, largura, comprimento, diâmetro e espessura de parede especificados pelo cliente, quando o processo de produção permitir.
Um relatório MTC é incluído em cada pedido. Relatórios adicionais de terceiros ou SGS podem ser providenciados mediante solicitação.
Opções comuns incluem acabamento de laminação, anodização, polimento e revestimentos especializados, sujeitos à liga e aplicação.
Vantagens da Linsy
A Linsy Aluminum é uma fornecedora líder de produtos de processamento de alumínio, atendendo a diversos setores, incluindo aeroespacial, engenharia geral, automotivo, marítimo, construção naval e outras aplicações industriais especializadas.
Temos o compromisso de manter os mais altos padrões de qualidade e responsabilidade ambiental, conforme demonstrado por nossas certificações: ISO 9001:2008， ISO 14001:2004 e SGS.