Aluminium 8009 (also referenced as FVS121 / AlFe8.7Si1.8V1.3) is a dispersion-strengthened 8000-series alloy built around a fine iron–silicon–vanadium intermetallic network rather than traditional age hardening. This gives it high strength that is retained at elevated temperatures, plus good fatigue resistance. Linsy supplies 8009 in O, T6, and T8 tempers across sheet, bar, and tube, with custom dimensions and MTC documentation for every order.
Dostępne formularze: sheet / plate / bar / tube / wire
Typowe temperamenty: O / T6 / T8
Wsparcie w zakresie przetwarzania: obróbka CNC / cięcie laserowe / polerowanie / anodowanie
Dokumenty dotyczące jakości: Raport MTC dołączany do każdego zamówienia
8009 is a powder-metallurgy-derived dispersion-strengthened alloy whose strength comes from a uniform dispersion of thermally stable Al–Fe–Si–V intermetallics. Unlike 2xxx/7xxx alloys, its strength does not collapse at moderately high service temperatures, making it attractive for aerospace and engine-adjacent structural parts. It is not a lithium-bearing alloy; its chemistry is iron–silicon–vanadium based.
Typical production ranges are listed below; custom dimensions are available on request.
| Formularz | Temperament | Dimension | Zakres | Note |
|---|---|---|---|---|
| Blacha i krąg | O, T6, T8 | Grubość | 0.5 – 100 mm | Custom widths/lengths |
| Płyta | O, T6, T8 | Grubość | 6 – 150 mm | Quarto |
| Okrągły pręt | O, T6, T8 | Średnica | 6 – 300 mm | Cut to length |
| Rura | O, T6, T8 | Średnica zewnętrzna | 10 – 300 mm | Wall 1 – 30 mm |
| Drut | O, T6, T8 | Średnica | 0.8 – 30 mm | Coil weight ≥ 50 kg |
| Element | Skład (%) |
|---|---|
| Żelazo (Fe) | 8.0 – 9.5 |
| Krzem (Si) | 1.5 – 2.1 |
| Wanad (V) | 1.0 – 1.6 |
| Miedź (Cu) | 0.05 max |
| Magnez (Mg) | 0.05 max |
| Mangan (Mn) | 0.05 max |
| Cynk (Zn) | 0.05 max |
| Tytan (Ti) | 0.05 max |
| Inni (każdy) | 0.05 max |
| Inne (łącznie) | 0,15 maks |
| Aluminium (Al) | Reszta |
| Temperament | Wytrzymałość na rozciąganie (MPa) | Granica plastyczności (MPa) | Wydłużenie (%) | Note |
|---|---|---|---|---|
| O | 350 – 420 | 200 – 280 | 12 – 18 | Wyżarzony |
| T6 | 520 – 590 | 460 – 540 | 7 – 11 | Peak strength |
| T8 | 540 – 600 | 480 – 550 | 6 – 10 | Cold-worked + aged |
The dispersed intermetallics resist coarsening, so strength holds up better than age-hardened alloys at elevated temperature.
Good fatigue performance supports rotating and cyclic-load aerospace components.
Generally good corrosion resistance; welding is possible but reduces the dispersion-strengthened benefit — confirm with engineering for critical parts.
8009 machines comparably to other high-strength aluminum grades. Because its strength derives from dispersion rather than precipitation, prolonged exposure above roughly 200–250°C should be reviewed with engineering. Standard anodizing and polishing are applicable.
Every shipment is accompanied by an MTC report detailing chemical composition and mechanical test results. Third-party inspection and SGS test reports can be arranged on request. Incoming and outgoing inspection covers dimensions, surface condition, and mechanical properties.
Linsy operates a Shenzhen production base with over 20 years of aluminum manufacturing experience, supplying 1000–8000 series alloys to global B2B buyers. We support custom dimensions, tempers, and processing for both prototype and production volumes.
Engineering guides and specification references help with alloy selection and design. The external links below are provided for background reading and should be replaced with Linsy-owned content before publication (verify before use).
No. 8009 is an iron–silicon–vanadium dispersion-strengthened alloy, not an Al-Li alloy. Some sources confuse it with 8090; the chemistry here follows the AA 8009 (AlFeSiV) designation.
8009 keeps more strength at elevated temperature, while 7075 peaks higher at room temperature. Choice depends on service temperature and fatigue needs.
Welding is possible but softens the dispersion-strengthened structure; evaluate for non-critical joints or use mechanical fastening.
Standard sizes are usually available within 10–60 days depending on alloy, temper, and order volume. Confirm exact timing with our sales team when requesting a quote.
Yes. We cut to customer-specified thickness, width, length, diameter, and wall thickness where the production process allows.
An MTC report is included with every order. Additional third-party or SGS reports can be arranged on request.
Common options include mill finish, anodizing, polishing, and specialized coatings subject to alloy and application.