5356 Alüminyum Alaşım

What Is 5356 Aluminum Alloy Aluminum?

5356 Aluminum Alloy (AlMg5CrTiMn) is a non-heat-treatable aluminum-magnesium (5xxx) alloy. Its strength comes from magnesium in solid solution and strain hardening, not heat treatment. It offers good corrosion resistance—especially in marine and industrial environments—and welds well, which makes it a common choice for structures exposed to water, chemicals, or cycling loads.

Available 5356 Aluminum Alloy Aluminum Products

5356 Aluminum Alloy is supplied in several forms and tempers. Standard size ranges are below; other dimensions can be discussed with our team.

Levha ve Plaka

Öğe	Range
Kalınlık	0.5 – 150 mm
Genişlik	1000 – 3000 mm
Uzunluk	1000 – 6000 mm
Common tempers	O, H22

Bar (Round / Flat / Square)

Öğe	Range
Diameter / side	6 – 400 mm
Uzunluk	1000 – 6000 mm
Common tempers	O, H22

Tube & Pipe

Öğe	Range
Outer diameter	6 – 400 mm
Wall thickness	0.5 – 40 mm
Uzunluk	1000 – 6000 mm
Common tempers	O, H22

Wire & Coil

Öğe	Range
Çap	0.8 – 12 mm
Bobin ağırlığı	10 – 500 kg
Size tolerance	± 0.05 mm
Common tempers	O, H22

Spesifikasyonlar ve Eşdeğer Tanımlamalar

Standart	Tanımlama
AA (USA)	5356 Alüminyum Alaşım
EN AW	AlMg5CrTiMn
Seri	5000 (Al-Mg, non-heat-treatable)

Kimyasal Bileşim

Element	Ağırlık %
Si	0,25 maks.
Fe	0,40 maks
Cu	0,10 maks.
Mn	0.05 - 0.20
Mg	4.5 - 5.5
Cr	0.05 - 0.20
Zn	0,10 maks.
Ti	0.06 - 0.20
Al	Denge

Values are typical AA composition ranges; confirm against the ordered specification and the supplied MTC.

Temperlere Göre Mekanik Özellikler

Temper	Tensile (MPa)	Yield (MPa)	Uzama (%)	Brinell
O	290	130	18	65
H22	320	200	12	75

Mechanical values are representative room-temperature typicals for plate, sheet, or bar and should be confirmed against the ordered thickness and the supplied MTC.

Temper Seçim Kılavuzu

• O (annealed): softest, best formability and corrosion resistance; for deep drawing and welding.
• H1xx / H2xx / H3xx: strain-hardened tempers with increasing strength and decreasing ductility.
• H116 / H321: stabilized tempers for marine plate with good exfoliation-corrosion resistance.

Choose the softest temper that meets the strength need to keep forming and welding straightforward.

Temel Özellikler

Welding filler alloy

One of the most common 5xxx filler metals for MIG and TIG welding of 5xxx and 6xxx base alloys.

Strength and ductility

Higher magnesium gives good strength and elongation compared with 4043/4045 fillers.

Anodized appearance

Produces a clear to slightly gray anodized finish that can match many base alloys.

Uygulamalar

• MIG and TIG welding wire
• Denizcilik bileşenleri (gövdeler, güverteler, tanklar)
• Yapısal çerçeveler ve basınçlı kaplar
• Bicycle, automotive, and trailer parts
• Aluminum scaffolding and piping

İşleme ve Yüzey Kaplama Notları

5356 Aluminum Alloy is a non-heat-treatable 5xxx alloy, so strength comes from strain hardening (H-tempers), not heat treatment. It cuts, drills, and welds well with standard aluminum tooling.

• Kesme: CNC machining, laser cutting, and sawing are supported.
• Kaynak: TIG and MIG welding with matching or compatible 5xxx filler.
• Forming: good cold formability in O and soft H-tempers.
• Yüzey Kaplaması: mill finish, anodizing, polishing, powder coating, or PVC film protection.

Note: anodized color of 5xxx alloys can differ slightly from 6xxx alloys; confirm the finish on a sample if color match matters.

Kalite Belgeleri ve Denetim

Every 5086 order ships with a Mill Test Certificate (MTC) that reports the actual chemical analysis and mechanical results for the supplied material. Third-party SGS or equivalent test reports can be arranged on request for project or tender requirements.

• MTC (EN 10204 3.1 or 3.2) with every order
• Dimensional inspection against the agreed tolerance
• Surface and visual check before packing
• Material traceability by heat / lot number

Why Choose Linsy for 5356 Aluminum Alloy

Linsy Aluminum is a Shenzhen-based aluminum supplier with more than 20 years of experience serving marine, transport, and general engineering customers. We supply 1000–8000 series material in plate, bar, tube, wire, coil, profile, and block forms.

• ISO 9001, ISO 14001, and ISO 45001 certified management systems
• MTC with every order and SGS test reports available on request
• CNC machining, laser cutting, welding, and surface finishing support
• Typical custom lead time 10–60 days, with low minimum order quantities

For a quote, share your alloy, temper, dimensions, quantity, and any certificate requirements.

İlgili Kaynaklar

• 5356 Aluminum Specifications Guide
• 5083 Marine-Grade Aluminum
• 5052 Alüminyum Alaşım
• Welding Filler Selection

5356 Aluminum Alloy Aluminum FAQ

Is 5356 heat treatable?

No. 5356 is a non-heat-treatable 5xxx alloy; it is most often used as welding filler metal.

5356 vs 4043 filler?

5356 (5xxx, higher Mg) gives higher strength and better color match on anodized parts; 4043 (4xxx, Si) flows more easily but is lower strength and darker after anodizing.

What base alloys can 5356 weld?

It is widely used to weld 5xxx and 6xxx series aluminum where higher joint strength is needed.

Genel Sipariş SSS

Tipik teslim süresi nedir?

Custom sizes are usually produced within 10–60 days depending on alloy, temper, and quantity. Confirm the schedule when you request a quote.

Do you provide mill test certificates?

Yes. An MTC is provided with every order, and third-party test reports can be arranged on request.

What surface finishes are available?

Mill finish, anodizing, polishing, powder coating, and PVC film are available depending on the form.

Minimum sipariş miktarı nedir?

We support low MOQs for custom requests. Share your required size and quantity for a quote.