5356 is a high-magnesium 5xxx aluminum alloy (AlMg5CrTiMn), most widely used as a welding filler metal for MIG and TIG joining of 5xxx and 6xxx alloys. It offers good strength, ductility, and corrosion resistance, and is supplied in wire and sheet across O and H22 tempers.
Moduli disponibili: sheet / plate / bar / tube / wire / coil
Temperamenti comuni: O, H22
Supporto per l'elaborazione: CNC machining / laser cutting / welding / anodizing
Documenti di qualità: Rapporto MTC allegato a ogni ordine
5356 Aluminum Alloy (AlMg5CrTiMn) is a non-heat-treatable aluminum-magnesium (5xxx) alloy. Its strength comes from magnesium in solid solution and strain hardening, not heat treatment. It offers good corrosion resistance—especially in marine and industrial environments—and welds well, which makes it a common choice for structures exposed to water, chemicals, or cycling loads.
5356 Aluminum Alloy is supplied in several forms and tempers. Standard size ranges are below; other dimensions can be discussed with our team.
| Articolo | Spessore |
|---|---|
| Spessore | 0.5 – 150 mm |
| Larghezza | 1000 – 3000 mm |
| Lunghezza | 1000 – 6000 mm |
| 1000–6000 mm o bobina | O, H22 |
| Articolo | Spessore |
|---|---|
| Diameter / side | 6 – 400 mm |
| Lunghezza | 1000 – 6000 mm |
| 1000–6000 mm o bobina | O, H22 |
| Articolo | Spessore |
|---|---|
| Diametro esterno | 6 – 400 mm |
| Spessore della parete | 0.5 – 40 mm |
| Lunghezza | 1000 – 6000 mm |
| 1000–6000 mm o bobina | O, H22 |
| Articolo | Spessore |
|---|---|
| Diametro | 0.8 – 12 mm |
| Peso della bobina | 10 – 500 kg |
| Size tolerance | ± 0.05 mm |
| 1000–6000 mm o bobina | O, H22 |
| Standard | Denominazione |
|---|---|
| AA (USA) | Lega di alluminio 5356 |
| EN AW | AlMg5CrTiMn |
| Serie | 5000 (Al-Mg, non-heat-treatable) |
| Elemento | Peso % |
|---|---|
| Si | 0,25 max |
| Fe | 0,40 max |
| Cu | 0,10 max |
| Mn | 0.05 - 0.20 |
| Mg | 4.5 - 5.5 |
| Cr | 0.05 - 0.20 |
| Zn | 0,10 max |
| Ti | 0.06 - 0.20 |
| Al | Equilibrio |
Values are typical AA composition ranges; confirm against the ordered specification and the supplied MTC.
| Temperamento | Resistenza a trazione (MPa) | Snervamento (MPa) | Allungamento (%) | Brinell |
|---|---|---|---|---|
| O | 290 | 130 | 18 | 65 |
| H22 | 320 | 200 | 12 | 75 |
Mechanical values are representative room-temperature typicals for plate, sheet, or bar and should be confirmed against the ordered thickness and the supplied MTC.
Choose the softest temper that meets the strength need to keep forming and welding straightforward.
One of the most common 5xxx filler metals for MIG and TIG welding of 5xxx and 6xxx base alloys.
Higher magnesium gives good strength and elongation compared with 4043/4045 fillers.
Produces a clear to slightly gray anodized finish that can match many base alloys.
5356 Aluminum Alloy is a non-heat-treatable 5xxx alloy, so strength comes from strain hardening (H-tempers), not heat treatment. It cuts, drills, and welds well with standard aluminum tooling.
Note: anodized color of 5xxx alloys can differ slightly from 6xxx alloys; confirm the finish on a sample if color match matters.
Every 5086 order ships with a Mill Test Certificate (MTC) that reports the actual chemical analysis and mechanical results for the supplied material. Third-party SGS or equivalent test reports can be arranged on request for project or tender requirements.
Linsy Aluminum is a Shenzhen-based aluminum supplier with more than 20 years of experience serving marine, transport, and general engineering customers. We supply 1000–8000 series material in plate, bar, tube, wire, coil, profile, and block forms.
For a quote, share your alloy, temper, dimensions, quantity, and any certificate requirements.
No. 5356 is a non-heat-treatable 5xxx alloy; it is most often used as welding filler metal.
5356 (5xxx, higher Mg) gives higher strength and better color match on anodized parts; 4043 (4xxx, Si) flows more easily but is lower strength and darker after anodizing.
It is widely used to weld 5xxx and 6xxx series aluminum where higher joint strength is needed.
Custom sizes are usually produced within 10–60 days depending on alloy, temper, and quantity. Confirm the schedule when you request a quote.
Yes. An MTC is provided with every order, and third-party test reports can be arranged on request.
Mill finish, anodizing, polishing, powder coating, and PVC film are available depending on the form.
We support low MOQs for custom requests. Share your required size and quantity for a quote.
Vantaggi Linsy
Linsy Aluminum è un fornitore leader di prodotti per la lavorazione dell'alluminio, che serve diversi settori, tra cui quello aerospaziale, dell'ingegneria generale, automobilistico, marittimo, navale e altre applicazioni industriali specializzate.
Ci impegniamo a mantenere i più alti standard di qualità e responsabilità ambientale, come dimostrano le nostre certificazioni: ISO 9001:2008, ISO 14001:2004 e SGS.