Stop aluminium 5356

What Is 5356 Aluminum Alloy Aluminum?

5356 Aluminum Alloy (AlMg5CrTiMn) is a non-heat-treatable aluminum-magnesium (5xxx) alloy. Its strength comes from magnesium in solid solution and strain hardening, not heat treatment. It offers good corrosion resistance—especially in marine and industrial environments—and welds well, which makes it a common choice for structures exposed to water, chemicals, or cycling loads.

Available 5356 Aluminum Alloy Aluminum Products

5356 Aluminum Alloy is supplied in several forms and tempers. Standard size ranges are below; other dimensions can be discussed with our team.

Sheet & Plate

Pozycja	Zakres
Grubość	0.5 – 150 mm
Szerokość	1000 – 3000 mm
Długość	1000 – 6000 mm
Typowe stany	O, H22

Bar (Round / Flat / Square)

Pozycja	Zakres
Diameter / side	6 – 400 mm
Długość	1000 – 6000 mm
Typowe stany	O, H22

Tube & Pipe

Pozycja	Zakres
Średnica zewnętrzna	6 – 400 mm
Grubość ścianki	0.5 – 40 mm
Długość	1000 – 6000 mm
Typowe stany	O, H22

Wire & Coil

Pozycja	Zakres
Średnica	0.8 – 12 mm
Coil weight	10 – 500 kg
Size tolerance	± 0.05 mm
Typowe stany	O, H22

Dane techniczne i odpowiedniki oznaczeń

Standard	Oznaczenie
AA (USA)	Stop aluminium 5356
EN AW	AlMg5CrTiMn
Seria	5000 (Al-Mg, non-heat-treatable)

Skład chemiczny

Element	Waga %
Si	0,25 maks
Fe	maks. 0,40
Cu	0,10 maks
Mn	0.05 - 0.20
Mg	4.5 - 5.5
Cr	0.05 - 0.20
Zn	0,10 maks
Ti	0.06 - 0.20
Al	Równowaga

Values are typical AA composition ranges; confirm against the ordered specification and the supplied MTC.

Właściwości mechaniczne w zależności od stanu utwardzenia

Temperament	Tensile (MPa)	Yield (MPa)	Wydłużenie (%)	Brinell
O	290	130	18	65
H22	320	200	12	75

Mechanical values are representative room-temperature typicals for plate, sheet, or bar and should be confirmed against the ordered thickness and the supplied MTC.

Przewodnik po doborze hartowania

• O (annealed): softest, best formability and corrosion resistance; for deep drawing and welding.
• H1xx / H2xx / H3xx: strain-hardened tempers with increasing strength and decreasing ductility.
• H116 / H321: stabilized tempers for marine plate with good exfoliation-corrosion resistance.

Choose the softest temper that meets the strength need to keep forming and welding straightforward.

Kluczowe cechy charakterystyczne

Welding filler alloy

One of the most common 5xxx filler metals for MIG and TIG welding of 5xxx and 6xxx base alloys.

Strength and ductility

Higher magnesium gives good strength and elongation compared with 4043/4045 fillers.

Anodized appearance

Produces a clear to slightly gray anodized finish that can match many base alloys.

Zastosowania

• MIG and TIG welding wire
• Komponenty morskie (kadłuby, pokłady, zbiorniki)
• Ramy konstrukcyjne i zbiorniki ciśnieniowe
• Bicycle, automotive, and trailer parts
• Aluminum scaffolding and piping

Uwagi dotyczące obróbki i wykończenia powierzchni

5356 Aluminum Alloy is a non-heat-treatable 5xxx alloy, so strength comes from strain hardening (H-tempers), not heat treatment. It cuts, drills, and welds well with standard aluminum tooling.

• Cięcie: CNC machining, laser cutting, and sawing are supported.
• Spawanie: TIG and MIG welding with matching or compatible 5xxx filler.
• Formowanie: good cold formability in O and soft H-tempers.
• Wykończenie powierzchni: mill finish, anodizing, polishing, powder coating, or PVC film protection.

Note: anodized color of 5xxx alloys can differ slightly from 6xxx alloys; confirm the finish on a sample if color match matters.

Dokumentacja jakości i kontrola jakości

Every 5086 order ships with a Mill Test Certificate (MTC) that reports the actual chemical analysis and mechanical results for the supplied material. Third-party SGS or equivalent test reports can be arranged on request for project or tender requirements.

• MTC (EN 10204 3.1 or 3.2) with every order
• Dimensional inspection against the agreed tolerance
• Surface and visual check before packing
• Material traceability by heat / lot number

Why Choose Linsy for 5356 Aluminum Alloy

Linsy Aluminum is a Shenzhen-based aluminum supplier with more than 20 years of experience serving marine, transport, and general engineering customers. We supply 1000–8000 series material in plate, bar, tube, wire, coil, profile, and block forms.

• ISO 9001, ISO 14001, and ISO 45001 certified management systems
• MTC with every order and SGS test reports available on request
• CNC machining, laser cutting, welding, and surface finishing support
• Typical custom lead time 10–60 days, with low minimum order quantities

For a quote, share your alloy, temper, dimensions, quantity, and any certificate requirements.

Powiązane materiały

• 5356 Aluminum Specifications Guide
• 5083 Marine-Grade Aluminum
• Stop aluminium 5052
• Welding Filler Selection

5356 Aluminum Alloy Aluminum FAQ

Is 5356 heat treatable?

No. 5356 is a non-heat-treatable 5xxx alloy; it is most often used as welding filler metal.

5356 vs 4043 filler?

5356 (5xxx, higher Mg) gives higher strength and better color match on anodized parts; 4043 (4xxx, Si) flows more easily but is lower strength and darker after anodizing.

What base alloys can 5356 weld?

It is widely used to weld 5xxx and 6xxx series aluminum where higher joint strength is needed.

Najczęściej zadawane pytania dotyczące zamówień ogólnych

Jaki jest typowy czas realizacji zamówienia?

Custom sizes are usually produced within 10–60 days depending on alloy, temper, and quantity. Confirm the schedule when you request a quote.

Czy dostarczacie świadectwa badań hutniczych?

Yes. An MTC is provided with every order, and third-party test reports can be arranged on request.

What surface finishes are available?

Mill finish, anodizing, polishing, powder coating, and PVC film are available depending on the form.

Jaka jest minimalna wielkość zamówienia?

We support low MOQs for custom requests. Share your required size and quantity for a quote.