6061 Aluminum Flat Bar is a versatile heat-treatable 6xxx alloy offering an excellent strength-to-weight ratio, good weldability, and corrosion resistance. Commonly supplied in T6, it suits structural, machined, and transport parts.
Mevcut formlar: flat bar
Yaygın temperler: O / T4 / T6 / T651 / T6511
İşleme desteği: CNC machining / welding / anodizing / cutting
Kalite belgeleri: Her siparişle birlikte MTC raporu
6061 Aluminum Flat Bar is made from 6061, one of the most widely used heat-treatable aluminum alloys. Its balanced mix of magnesium and silicon gives good strength after the T6/T651 aging treatment while keeping the material easy to machine and weld.
In T6 condition it delivers strong structural performance, which is why it appears across architecture, transport, and general engineering.
| Parameter | Typical Range |
|---|---|
| Kalınlık | 3–200 mm |
| Genişlik | 10–600 mm |
| Uzunluk | up to 6000 mm (cut to size) |
| Tempers | O, T4, T6, T651, T6511 |
| Standards | ASTM B221, EN 755, GB/T 6892 |
Custom thickness and width combinations can be reviewed on enquiry.
| Tanımlama Sistemi | Eşdeğer |
|---|---|
| AA 6061 | EN AW-6061 |
| UNS A96061 | ISO Al-Mg1SiCu |
Yaygın standartlar: ASTM B221, ASTM B211, EN 755, GB/T 6892.
| Element | Bileşim (ağırlıkça %) |
|---|---|
| Si | 0.40–0.80 |
| Fe | 0.70 max |
| Cu | 0.15–0.40 |
| Mn | 0,15 maks. |
| Mg | 0.80–1.20 |
| Cr | 0.04–0.35 |
| Zn | 0,25 maks. |
| Ti | 0,15 maks. |
| Diğerleri (her biri) | 0,05 maks. |
| Diğerleri (toplam) | 0,15 maks. |
| Al | Denge (kalan) |
Aşağıdaki değerler ekstrüde veya çekilmiş ürün için tipiktir ve belirli temper ve kesit için fabrika test sertifikası ile teyit edilmelidir.
| Temper | Çekme Dayanımı (MPa) | Akma Dayanımı (MPa) | Uzama (%) |
|---|---|---|---|
| O | 124 | 55 | 25 |
| T4 | 207 | 110 | 18 |
| T6 | 310 | 276 | 12 |
| T651 | 310 | 276 | 12 |
T6 flat bar carries real structural load at a fraction of steel’s weight.
Cuts and drills cleanly, ideal for CNC-produced brackets and parts.
Joins reliably by TIG/MIG; design around post-weld temper loss.
Handles atmospheric and mild marine exposure with optional anodizing.
Aşağıdaki kılavuzlar, bu alaşım için seçim, temper karşılaştırması ve işleme notlarını kapsar. Yayınlamadan önce canlı URL'leri doğrulayın — harici referansları mümkün olduğunda Linsy'ye ait blog bağlantılarıyla değiştirin.
Yes. It is supplied in O, T4, T6, T651, and T6511; T6/T651 are the structural tempers.
T651 is stress-relieved by stretching after aging, giving better dimensional stability and less warping after machining.
Yes. Standard and custom lengths are supplied cut to your dimension list.
Minimum sipariş miktarı, forma ve tempere bağlıdır. Standart kesitler ve temperler birkaç yüz kilogramdan başlayabilir; özel boyut veya özel temper siparişleri duruma göre değerlendirilir.
Stokta bulunan temperler için teslim süresi tipik olarak 10–30 gündür. Özel ekstrüzyon veya ısıl işlem görmüş koşullar 60 güne kadar sürebilir. Sorgulama sırasında satış ekibimizle teyit edin.
Evet. Kesme, CNC işleme, kaynak, anodizasyon ve parlatma hizmetleri sunuyoruz. Sorgulamanızla birlikte çizimlerinizi veya boyut listenizi sağlayın.
Her sipariş bir MTC ile sevk edilir. Talep üzerine SGS veya diğer üçüncü taraf test raporları düzenlenebilir.
Linsy Avantajları
Linsy Alüminyum, havacılık, genel mühendislik, otomotiv, denizcilik, gemi yapımı ve diğer özel endüstriyel uygulamalar dahil olmak üzere çeşitli endüstrilere hizmet veren lider bir alüminyum işleme ürünleri tedarikçisidir.
Sertifikalarımızın da gösterdiği gibi, en yüksek kalite ve çevresel sorumluluk standartlarını sürdürmeye kararlıyız: ISO 9001:2008 ， ISO 14001:2004 ve SGS.