7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
Verfügbare Formulare: Blech / Platte, Rohr, Stange / Stab, Draht
Häufige Temperamente: T4, T6, T651
Unterstützung bei der Bearbeitung: CNC-Bearbeitung, Laserschneiden, WIG/MIG-Schweißen, Eloxieren, Polieren, Pulverbeschichten
Qualitätsdokumente: MTC-Bericht bei jeder Bestellung
7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
Verfügbare Zustände: T4, T6, T651
| Temperament | Dicke (mm) | Breite (mm) | Länge (mm) |
|---|---|---|---|
| T4, T6, T651 | 0.5 – 150 | 500 – 2600 | 500 – 16000 (auf Maß geschnitten) |
Verfügbare Zustände: T4, T6, T651
| Temperament | Äußerer Durchmesser (mm) | Wand (mm) | Länge (mm) |
|---|---|---|---|
| T4, T6, T651 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Verfügbare Zustände: T4, T6, T651
| Temperament | Durchmesser (mm) | Länge (mm) |
|---|---|---|
| T4, T6, T651 | 3 – 300 | 500 – 12000 |
Verfügbare Zustände: T6
| Durchmesser (mm) | Gewicht der Spule | Toleranz |
|---|---|---|
| 0.8 – 30 | Mindestens 50 kg | ± 0,02 mm |
7014 aluminum (EN AW-7014, AlZn5.7Mg2.7Mn) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Element | Prozentsatz (%) |
|---|---|
| Si | 0,50 max. |
| Fe | 0,50 max. |
| Cu | 0,10 max |
| Mn | 0,10 max |
| Mg | 2.2 – 3.3 |
| Cr | 0.05 – 0.30 |
| Zn | 5.2 – 6.2 |
| Ti | 0,15 max |
| Zr | 0,10 max |
| Sonstige (jeweils) | 0.05 |
| Sonstige (insgesamt) | 0.15 |
| Al | Bilanz |
| Temperament | Zugfestigkeit (MPa) | Streckgrenze (MPa) | Dehnung (%) | Scherfestigkeit (MPa) |
|---|---|---|---|---|
| T6 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
| T651 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
Die Werte sind typisch für den angegebenen Zustand. Ein Gedankenstrich (—) bedeutet, dass der Wert in den Quelldaten nicht verfügbar war; bitte mit dem Werkszeugnis bestätigen. Mit Sternchen gekennzeichnete Werte sind Schätzwerte, die noch der Überprüfung bedürfen – siehe Prüfbericht.
T6 temper reaches 480–520 MPa ultimate tensile strength while staying light.
Better fracture toughness than many higher-zinc 7xxx grades, suited to airframe loads.
Satisfactory in internal structures; exterior use should be clad or anodized.
Responds strongly to precipitation hardening for tailored strength.
Weldable with care;confirm a qualified procedure and post-weld heat treatment with our team.
Linsy machines 7014 on CNC centers and cuts it with fiber laser. For corrosion protection, anodizing or painting is recommended on exposed surfaces. Welding should use a qualified procedure with filler selected for the service environment; post-weld heat treatment can be discussed with our engineers.
Linsy ist ein in Shenzhen ansässiger Aluminiumlieferant mit mehr als 20 Jahren Erfahrung. Unser Qualitätssystem ist nach ISO 9001, ISO 14001 und ISO 45001 zertifiziert. Jede Bestellung wird mit einem Werkszeugnis (MTC) versandt. SGS-Prüfberichte von Dritten sind auf Anfrage erhältlich. Die typische kundenspezifische Vorlaufzeit beträgt 10–60 Tage, abhängig von Zustand, Abmessung und Menge.
Für weiterführende Informationen zur Auswahl und Verarbeitung von 7xxx-Legierungen lesen Sie unsere Leitfäden zur Aluminiumlegierungsauswahl und zum Schweißen von 7000er-Serienlegierungen. (Interne Links zu veröffentlichten Linsy-Blogartikeln.)
Common tempers are T4, T6, and T651. T651 is stress-relieved for reduced distortion during machining. Tell us your application and we will recommend a temper.
It can be welded with a qualified procedure, but strength in the heat-affected zone drops. We recommend confirming the welding process and any post-weld treatment with our technical team before production.
7014 offers slightly lower peak strength than 7075 but generally better toughness, making it a good choice for airframe structures where damage tolerance matters.
Every order ships with a mill test certificate (MTC). SGS third-party test reports are available on request.
Kundenspezifische Aluminiumbestellungen werden in der Regel innerhalb von 10–60 Tagen versandt, abhängig von Legierung, Zustand, Abmessung und Menge. Lagerware oder Standardabmessungen können schneller gehen – fragen Sie unser Team.
Ja. Jede Bestellung enthält ein MTC. SGS-Prüfberichte von Dritten sind auf Anfrage erhältlich.
Ja. Wir bieten CNC-Bearbeitung, Laserschneiden, Schweißen, Eloxieren, Polieren und Pulverbeschichten an, sodass Teile in einem näher am Endzustand befindlichen Format geliefert werden können.
Senden Sie Ihre Legierung, Ihren Zustand, Ihre Abmessungen, Ihre Menge und die erforderliche Norm. Unser Team wird Verfügbarkeit, Vorlaufzeit und Preis bestätigen.
Linsy Vorteile
Linsy Aluminum ist ein führender Anbieter von Produkten für die Aluminiumverarbeitung und beliefert verschiedene Branchen wie die Luft- und Raumfahrt, den allgemeinen Maschinenbau, die Automobilindustrie, die Schifffahrt, den Schiffbau und andere spezialisierte industrielle Anwendungen.
Wir verpflichten uns, die höchsten Qualitäts- und Umweltstandards einzuhalten, was durch unsere Zertifizierungen belegt wird: ISO 9001:2008, ISO 14001:2004 und SGS.