7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
Formulaires disponibles : tôle / plaque, tube, barre / tige, fil
Tempéraments courants : T4, T6, T651
Assistance technique : Usinage CNC, découpe laser, soudage TIG/MIG, anodisation, polissage, revêtement par poudre
Documents relatifs à la qualité : Rapport MTC joint à chaque commande
7014 aluminum is a high-strength, heat-treatable 7xxx series alloy built around zinc and magnesium, with small manganese and zirconium additions for grain control. It delivers a strong combination of tensile strength, toughness, and corrosion resistance, which is why it is widely specified for aerospace structural parts. 7014 responds well to heat treatment and can be supplied in sheet, plate, tube, bar, and wire. When welding is required, qualified procedures should be confirmed with our technical team. Linsy supplies 7014 in a range of tempers with mill test certificates provided on every order.
États disponibles : T4, T6, T651
| Tempérer | Épaisseur (mm) | Largeur (mm) | Longueur (mm) |
|---|---|---|---|
| T4, T6, T651 | 0.5 – 150 | 500 – 2600 | 500 – 16000 (découpe sur mesure) |
États disponibles : T4, T6, T651
| Tempérer | Diamètre extérieur (mm) | Paroi (mm) | Longueur (mm) |
|---|---|---|---|
| T4, T6, T651 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
États disponibles : T4, T6, T651
| Tempérer | Diamètre (mm) | Longueur (mm) |
|---|---|---|
| T4, T6, T651 | 3 – 300 | 500 – 12000 |
États disponibles : T6
| Diamètre (mm) | Poids de la bobine | Tolérance |
|---|---|---|
| 0.8 – 30 | 50 kg minimum | ± 0,02 mm |
7014 aluminum (EN AW-7014, AlZn5.7Mg2.7Mn) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Élément | Pourcentage (%) |
|---|---|
| Si | 0,50 max |
| Fe | 0,50 max |
| Cu | 0,10 max |
| Mn | 0,10 max |
| Mg | 2.2 – 3.3 |
| Cr | 0.05 – 0.30 |
| Zn | 5.2 – 6.2 |
| Ti | 0,15 max |
| Zr | 0,10 max |
| Autres (chacun) | 0.05 |
| Autres (total) | 0.15 |
| Al | Équilibre |
| Tempérer | Résistance à la traction (MPa) | Limite d'élasticité (MPa) | Élongation (%) | Résistance au cisaillement (MPa) |
|---|---|---|---|---|
| T6 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
| T651 | 480 – 520 | 360 – 420 | 11 – 20 | 280 – 380 |
Les valeurs sont typiques pour la condition indiquée. Un tiret (—) signifie que la valeur n'était pas disponible dans les données source ; veuillez confirmer avec le certificat d'essai en usine. Les valeurs marquées d'un astérisque sont des estimations en attente de vérification — voir le rapport d'audit.
T6 temper reaches 480–520 MPa ultimate tensile strength while staying light.
Better fracture toughness than many higher-zinc 7xxx grades, suited to airframe loads.
Satisfactory in internal structures; exterior use should be clad or anodized.
Responds strongly to precipitation hardening for tailored strength.
Weldable with care;confirm a qualified procedure and post-weld heat treatment with our team.
Linsy machines 7014 on CNC centers and cuts it with fiber laser. For corrosion protection, anodizing or painting is recommended on exposed surfaces. Welding should use a qualified procedure with filler selected for the service environment; post-weld heat treatment can be discussed with our engineers.
Linsy est un fournisseur d'aluminium basé à Shenzhen avec plus de 20 ans d'expérience. Notre système qualité est certifié ISO 9001, ISO 14001 et ISO 45001. Chaque commande est expédiée avec un certificat d'essai en usine (MTC). Des rapports d'essais tiers SGS sont disponibles sur demande. Le délai de livraison typique pour les commandes personnalisées est de 10 à 60 jours selon l'état, les dimensions et la quantité.
Pour une lecture plus approfondie sur la sélection et la fabrication des alliages 7xxx, consultez nos guides sur la sélection des alliages d'aluminium et le soudage des alliages de la série 7000. (Liens internes à connecter aux articles publiés du blog Linsy.)
Common tempers are T4, T6, and T651. T651 is stress-relieved for reduced distortion during machining. Tell us your application and we will recommend a temper.
It can be welded with a qualified procedure, but strength in the heat-affected zone drops. We recommend confirming the welding process and any post-weld treatment with our technical team before production.
7014 offers slightly lower peak strength than 7075 but generally better toughness, making it a good choice for airframe structures where damage tolerance matters.
Every order ships with a mill test certificate (MTC). SGS third-party test reports are available on request.
Les commandes d'aluminium personnalisées sont généralement expédiées sous 10 à 60 jours selon l'alliage, l'état, les dimensions et la quantité. Les tailles standard ou en stock peuvent être plus rapides — demandez à notre équipe.
Oui. Chaque commande comprend un MTC. Des rapports d'essais tiers SGS sont disponibles sur demande.
Oui. Nous fournissons l'usinage CNC, la découpe laser, le soudage, l'anodisation, le polissage et le revêtement par poudre afin que les pièces puissent être livrées plus proches de leur forme finie.
Envoyez votre alliage, état, dimensions, quantité et norme requise. Notre équipe confirmera la disponibilité, le délai de livraison et le prix.
Avantages pour Linsy
Linsy Aluminum est un fournisseur de premier plan de produits de transformation de l'aluminium, au service de diverses industries, notamment l'aérospatiale, l'ingénierie générale, l'automobile, la marine, la construction navale et d'autres applications industrielles spécialisées.
Nous nous engageons à respecter les normes les plus strictes en matière de qualité et de responsabilité environnementale, comme en témoignent nos certifications : ISO 9001:2008， ISO 14001:2004 et SGS.