6061 Aluminum Round Bar is a versatile heat-treatable 6xxx alloy offering an excellent strength-to-weight ratio, good weldability, and corrosion resistance. Commonly supplied in T6, it suits structural, machined, and transport parts.
Moduli disponibili: round bar
Temperamenti comuni: O / T4 / T6 / T651 / T6511
Supporto per l'elaborazione: CNC machining / welding / anodizing / cutting
Documenti di qualità: Rapporto MTC allegato a ogni ordine
6061 Aluminum Round Bar is made from 6061, one of the most widely used heat-treatable aluminum alloys. Its balanced mix of magnesium and silicon gives good strength after the T6/T651 aging treatment while keeping the material easy to machine and weld.
In T6 condition it delivers strong structural performance, which is why it appears across architecture, transport, and general engineering.
| Parametro | Typical Range |
|---|---|
| Diametro | 6–400 mm |
| Lunghezza | up to 6000 mm (cut to size) |
| Tempre | O, T4, T6, T651, T6511 |
| Normative | ASTM B211, ASTM B221, EN 755, GB/T 3191 |
Large diameters and custom lengths can be reviewed on enquiry.
| Sistema di Designazione | Equivalente |
|---|---|
| AA 6061 | EN AW-6061 |
| UNS A96061 | ISO Al-Mg1SiCu |
Norme comuni: ASTM B221, ASTM B211, EN 755, GB/T 6892.
| Elemento | Composizione (wt%) |
|---|---|
| Si | 0.40–0.80 |
| Fe | 0.70 max |
| Cu | 0.15–0.40 |
| Mn | 0,15 max |
| Mg | 0.80–1.20 |
| Cr | 0.04–0.35 |
| Zn | 0,25 max |
| Ti | 0,15 max |
| Altri (ciascuno) | 0,05 max |
| Altri (totale) | 0,15 max |
| Al | Bilanciamento (resto) |
I valori seguenti sono tipici per prodotti estrusi o trafilati e devono essere confermati dal certificato di prova del laminatoio per la specifica tempra e sezione.
| Temperamento | Resistenza alla trazione (MPa) | Resistenza allo snervamento (MPa) | Allungamento (%) |
|---|---|---|---|
| O | 124 | 55 | 25 |
| T4 | 207 | 110 | 18 |
| T6 | 310 | 276 | 12 |
| T651 | 310 | 276 | 12 |
T651/T6511 round bar is a workshop favorite for turned and milled parts.
T6 temper delivers strong, dimensionally stable stock for precision work.
Used for shafts, spindles, and fixtures where consistency matters.
Performs well indoors and in mild outdoor or marine-adjacent service.
Le seguenti guide trattano la selezione, il confronto delle tempra e le note di lavorazione per questa lega. Confermare gli URL attivi prima della pubblicazione — sostituire eventuali riferimenti esterni con link ai blog di proprietà di Linsy ove disponibili.
Yes. It is supplied in O, T4, T6, T651, and T6511 tempers.
T651 or T6511 is preferred for machining because stress relief minimizes warping after cutting.
Typical range is 6–400 mm; custom sizes can be reviewed on enquiry.
Il MOQ dipende dalla forma e dalla tempra. Sezioni e tempra standard possono partire da poche centinaia di chilogrammi; ordini con dimensioni personalizzate o tempra speciale vengono valutati caso per caso.
Per le tempra disponibili a magazzino, i tempi di consegna sono generalmente di 10–30 giorni. Estrusioni personalizzate o condizioni di trattamento termico possono richiedere fino a 60 giorni. Confermare con il nostro team vendite all'indirizzo enquiry.
Sì. Offriamo taglio, lavorazione CNC, saldatura, anodizzazione e lucidatura. Fornite i vostri disegni o l'elenco delle dimensioni con la richiesta.
Ogni ordine viene spedito con un MTC. Rapporti di prova SGS o di altri enti terzi possono essere organizzati su richiesta.