Lega di alluminio 6082

What Is 6082 Aluminum Alloy?

6082 (EN AW-6082, AlSi1MgMn) is a heat-treatable 6000-series aluminum alloy with magnesium and silicon as the main alloying elements, plus manganese for strength and corrosion resistance. It offers a strong combination of medium-to-high strength, good corrosion resistance, and excellent extrudability, which makes it one of the most widely used structural aluminum alloys.

Compared with 6061, 6082 generally provides higher strength in thicker sections while remaining weldable and formable in the appropriate tempers. It is commonly supplied in O, T4, T6, and T651 tempers across sheet, plate, bar, tube, and extruded profiles.

Available 6082 Aluminum Products

Forma	Tempra comuni	Intervallo dimensionale tipico
Lamiera e Bobina	O, F, T4, T6, T651, H112	Spessore 0,5–150 mm; Larghezza 500–2600 mm; Lunghezza 500–12000 mm
Piatto	O, T651, H112	Thickness 6–200 mm; Width up to 2600 mm; Length up to 12000 mm
Barra (tonda/quadra/piatta)	O, T6, T651, H112	Diametro/lato 6–400 mm; Lunghezza 1000–6000 mm
Tubo (tondo/quadro)	O, T6, T651	Diametro esterno 10–400 mm; Spessore parete 1–40 mm; Lunghezza 1000–6000 mm
Filo	O, T4, T6, T651	0,8–30 mm
Spessore parete	T4, T6, T651	In base al disegno fornito dal cliente

6082 Aluminum Sheet & Coil

Supplied in O, T4, T6, T651, and H112. Thin gauges are offered as coil; thicker material is cut to plate or sheet lengths. Custom widths and lengths are available.

6082 Aluminum Plate

Plate in T651 and H112 is used where higher section thickness and flatness control are required for machining and structural parts.

6082 Aluminum Bar

Round, square, and flat bars in T6/T651 and H112 for machining, fixtures, and structural components.

6082 Aluminum Tube

Round and square tubes for frameworks, transport, and fluid-handling structures where weldability matters.

6082 Aluminum Wire

Drawn wire in O/T4/T6/T651 for welding consumables, rivets, and fasteners.

Altre forme (profilo / personalizzato)

Extruded profiles produced to customer drawings in T4, T6, and T651.

6082 Specifications & Equivalent Designations

Denominazione	Valore
EN AW	EN AW-6082 (AlSi1MgMn)
UNS	A96082
ASTM	B221 (extruded), B209 (sheet/plate), B211 (bar/rod)
IT	EN 573, EN 485, EN 755
GB/T	3190, 3880, 6892
1000–6000 mm o bobina	O, T4, T6, T651, H112

Chemical Composition of 6082 Aluminum

Elemento	Composizione (wt%)
Si	0.70 – 1.30
Fe	0,50 max
Cu	0,10 max
Mn	0.40 – 1.00
Mg	0.60 – 1.20
Cr	0,25 max
Zn	Famiglia
Ti	0,15 max
Altri (ciascuno)	0,05 max
Altri (totale)	0,15 max
Al	Resto

Proprietà meccaniche in base al trattamento termico

The values below are typical reference figures for 6082 and should be confirmed against the ordered standard and Linsy’s mill data.

Temperamento	Resistenza alla trazione (MPa)	Resistenza allo snervamento (MPa)	Allungamento (%, min)
O	120	65	22
T4	205	110	16
T6	310	270	10
T651	310	270	10

Guida alla scelta della tempra

• O (annealed): maximum formability and lowest strength; choose for deep forming.
• T4: solution heat treated and naturally aged; good formability with moderate strength.
• T6 / T651: solution heat treated and artificially aged (T651 is stress-relieved); highest standard strength for structural use.
• H112: strain-hardened for plate/extrusion with relaxed property control; general structural use.

Key Characteristics of 6082 Aluminum

Forza-peso

6082 delivers strong specific strength, especially in T6/T651, making it suitable for load-bearing structures.

Resistenza alla corrosione

Good general corrosion resistance; in aggressive marine environments consider cladding or appropriate surface treatment.

Formability & Weldability

Readily formed in O/T4 and weldable by TIG/MIG. Welded zones are softer than the base temper and should be accounted for in design.

Applicazioni comuni

• Bridges, trusses, towers, and pylons
• Railway and transport structures, truck frames
• Marine and shipbuilding components
• Machined parts, fixtures, and wear plates
• Componenti strutturali automobilistici

Note sulla lavorazione e sulla finitura superficiale

Lavorazione meccanica

6082 machines well in the soft (O) and solution-heat-treated tempers; T6/T651 tempers are stronger and can work-harden at the cutting edge, so sharp tooling and appropriate feeds are recommended.

Saldatura

6082 is generally weldable using TIG or MIG processes with matching or 4043/5356 filler, depending on the service requirement. Welded zones lose some strength compared with the base temper — design accordingly for structural use.

Formatura e trattamento termico

La formatura è ottimale nelle condizioni O o T4. La resistenza finale viene sviluppata dal trattamento specificato; non ritrattare termicamente senza confermare la risposta della lega.

Finitura superficiale

Finiture comuni includono anodizzazione, lucidatura e verniciatura a polvere. La qualità dell'anodizzazione dipende dalla preparazione superficiale, quindi confermare i requisiti di finitura prima della produzione.

Documenti di qualità e ispezione

Every 6082 order ships with a Mill Test Certificate (MTC) that reports the actual chemical composition and mechanical properties against the ordered specification. We can also arrange:

• Third-party inspection and SGS test reports on request.
• Dimension and surface inspection records for critical tolerances.
• Material certificates aligned to ASTM, EN, GB, or JIS as required.

Please confirm the required standard and any additional documentation when placing the order.

Why Choose Linsy for 6082 Aluminum

Linsy opera con una base produttiva a Shenzhen con oltre 20 anni di esperienza nella fornitura di semilavorati in alluminio a acquirenti B2B globali. Gestiamo le serie dalla 1000 alla 8000 e supportiamo sia dimensioni standard di magazzino che misure su ordinazione.

• Gamma di materiali: 1000–8000 series, including 6082 in the tempers listed above.
• Supporto per l'elaborazione: Lavorazione CNC, taglio laser, saldatura TIG/MIG e sbavatura su disegno.
• Finitura superficiale: Anodizzazione, lucidatura, verniciatura a polvere e finiture spazzolate su richiesta.
• Sistema di qualità: Le operazioni seguono ISO 9001, ISO 14001 e ISO 45001.
• Documentazione: Un MTC (Certificato di collaudo del materiale) viene emesso con ogni ordine; rapporti di ispezione SGS di terze parti possono essere organizzati quando richiesto.

Risorse correlate

• Guida completa all'alluminio 6082-T6

6082 Aluminum FAQ

Is 6082 the same as 6061?

No. Both are 6000-series structural alloys, but 6082 has higher manganese and typically higher strength in thicker sections, while 6061 is more common in North America and easier to source in some tempers.

Can 6082 be welded?

Yes. It welds well with TIG/MIG using appropriate filler. Note that welded zones are softer than the surrounding T6 material.

What lead time should I expect?

Stock items ship in 10–30 days; custom sizes and tempers typically 30–60 days depending on specification.

Domande frequenti generali sugli ordini

Qual è il tempo di consegna standard?

Gli articoli standard in magazzino vengono solitamente spediti entro 10–30 giorni. Dimensioni, tempere o finiture superficiali personalizzate richiedono generalmente 30–60 giorni, in base alle specifiche e al volume dell'ordine.

Fornite certificati di prova del materiale?

Sì. Ogni ordine viene spedito con un certificato di collaudo del materiale (MTC) che riporta la composizione chimica e le proprietà meccaniche secondo lo standard ordinato.

Potete fornire dimensioni e tempra personalizzate?

Sì. Forniamo dimensioni standard e su misura per lamiere, lastre, barre, tubi e profilati, e possiamo organizzare tempere specifiche su richiesta.

Quali standard di qualità seguite?

Le operazioni seguono le norme ISO 9001, ISO 14001 e ISO 45001. Il materiale può essere fornito secondo le specifiche ASTM, EN, GB o JIS, a seconda delle esigenze.

Come vengono imballati i prodotti per l'esportazione?

Viene utilizzato un imballaggio standard per esportazione marittima con protezione dall'umidità; eventuali requisiti specifici vengono confermati al momento dell'ordine.