6082 알루미늄 합금 (EN AW-6082, AlSi1MgMn) is a heat-treatable 6000-series structural grade supplied as sheet, plate, bar, tube, wire, and extruded profile. It combines good corrosion resistance with higher strength than 6061 in thicker sections, and is widely used for bridges, transport, marine, and machined parts. Linsy supplies 6082 in O, T4, T6, and T651 with made-to-order sizes and an MTC on every order.
이용 가능한 양식: 판재 / 플레이트 / 코일 / 봉 / 튜브 / 와이어 / 형재
흔히 나타나는 기질: O / T4 / T6 / T651 / H112
처리 지원: CNC 가공 / 레이저 절단 / 용접 / 아노다이징
품질 관련 문서: 모든 주문 시 MTC 보고서 제공
6082 (EN AW-6082, AlSi1MgMn) is a heat-treatable 6000-series aluminum alloy with magnesium and silicon as the main alloying elements, plus manganese for strength and corrosion resistance. It offers a strong combination of medium-to-high strength, good corrosion resistance, and excellent extrudability, which makes it one of the most widely used structural aluminum alloys.
Compared with 6061, 6082 generally provides higher strength in thicker sections while remaining weldable and formable in the appropriate tempers. It is commonly supplied in O, T4, T6, and T651 tempers across sheet, plate, bar, tube, and extruded profiles.
| 양식 | 일반적인 템퍼 | 일반적인 치수 범위 |
|---|---|---|
| 시트 및 코일 | O, F, T4, T6, T651, H112 | 두께 0.5–150 mm; 너비 500–2600 mm; 길이 500–12000 mm |
| 플레이트 | O, T651, H112 | Thickness 6–200 mm; Width up to 2600 mm; Length up to 12000 mm |
| 바 (원형/사각형/평면) | O, T6, T651, H112 | 직경/변 6–400 mm; 길이 1000–6000 mm |
| 튜브 (원형/사각형) | O, T6, T651 | 외경 10–400 mm; 벽 두께 1–40 mm; 길이 1000–6000 mm |
| 와이어 | O, T4, T6, T651 | 0.8–30 mm |
| 프로파일 / 압출 | T4, T6, T651 | 고객 도면에 따름 |
Supplied in O, T4, T6, T651, and H112. Thin gauges are offered as coil; thicker material is cut to plate or sheet lengths. Custom widths and lengths are available.
Plate in T651 and H112 is used where higher section thickness and flatness control are required for machining and structural parts.
Round, square, and flat bars in T6/T651 and H112 for machining, fixtures, and structural components.
Round and square tubes for frameworks, transport, and fluid-handling structures where weldability matters.
Drawn wire in O/T4/T6/T651 for welding consumables, rivets, and fasteners.
Extruded profiles produced to customer drawings in T4, T6, and T651.
| 명칭 | 가치 |
|---|---|
| EN AW | EN AW-6082 (AlSi1MgMn) |
| UNS | A96082 |
| ASTM | B221 (extruded), B209 (sheet/plate), B211 (bar/rod) |
| EN | EN 573, EN 485, EN 755 |
| GB/T | 3190, 3880, 6892 |
| 일반적인 템퍼 | O, T4, T6, T651, H112 |
| 요소 | 조성 (중량%) |
|---|---|
| Si | 0.70 – 1.30 |
| Fe | 0.50 최대 |
| Cu | 최대 0.10 |
| Mn | 0.40 – 1.00 |
| Mg | 0.60 – 1.20 |
| Cr | 최대 0.25 |
| Zn | 0.20 최대 |
| Ti | 최대 0.15 |
| 기타(각) | 최대 0.05 |
| 기타(합계) | 최대 0.15 |
| Al | 나머지 |
The values below are typical reference figures for 6082 and should be confirmed against the ordered standard and Linsy’s mill data.
| 성질 | 인장 강도(MPa) | 항복 강도(MPa) | 연신율 (%, 최소) |
|---|---|---|---|
| O | 120 | 65 | 22 |
| T4 | 205 | 110 | 16 |
| T6 | 310 | 270 | 10 |
| T651 | 310 | 270 | 10 |
6082 delivers strong specific strength, especially in T6/T651, making it suitable for load-bearing structures.
Good general corrosion resistance; in aggressive marine environments consider cladding or appropriate surface treatment.
Readily formed in O/T4 and weldable by TIG/MIG. Welded zones are softer than the base temper and should be accounted for in design.
6082 machines well in the soft (O) and solution-heat-treated tempers; T6/T651 tempers are stronger and can work-harden at the cutting edge, so sharp tooling and appropriate feeds are recommended.
6082 is generally weldable using TIG or MIG processes with matching or 4043/5356 filler, depending on the service requirement. Welded zones lose some strength compared with the base temper — design accordingly for structural use.
성형은 O 또는 T4 상태에서 가장 잘 수행됩니다. 최종 강도는 지정된 템퍼에 의해 발현됩니다. 합금의 반응을 확인하지 않고 재열처리하지 마십시오.
일반적인 마감 처리에는 아노다이징, 연마 및 분체 코팅이 포함됩니다. 아노다이징 품질은 표면 처리에 따라 달라지므로, 생산 전에 마감 요구 사항을 확인하십시오.
Every 6082 order ships with a Mill Test Certificate (MTC) that reports the actual chemical composition and mechanical properties against the ordered specification. We can also arrange:
Please confirm the required standard and any additional documentation when placing the order.
Linsy는 20년 이상의 경험을 가진 선전 생산 기지를 운영하며 글로벌 B2B 구매자에게 알루미늄 반제품을 공급하고 있습니다. 1000계열부터 8000계열까지 취급하며, 표준 재고 치수와 주문 제작 치수를 모두 지원합니다.
No. Both are 6000-series structural alloys, but 6082 has higher manganese and typically higher strength in thicker sections, while 6061 is more common in North America and easier to source in some tempers.
Yes. It welds well with TIG/MIG using appropriate filler. Note that welded zones are softer than the surrounding T6 material.
Stock items ship in 10–30 days; custom sizes and tempers typically 30–60 days depending on specification.
표준 재고 품목은 일반적으로 10~30일 이내에 배송됩니다. 맞춤형 치수, 템퍼 또는 표면 마감은 사양과 주문량에 따라 일반적으로 30~60일이 소요됩니다.
예. 모든 주문에는 주문된 표준에 따른 화학 성분 및 기계적 특성을 보고하는 MTC가 함께 발송됩니다.
예. 당사는 시트, 플레이트, 바, 튜브 및 프로파일의 표준 및 주문 제작 치수를 공급하며, 요청 시 특정 템퍼를 준비할 수 있습니다.
운영은 ISO 9001, ISO 14001 및 ISO 45001을 따릅니다. 재료는 필요에 따라 ASTM, EN, GB 또는 JIS 사양으로 공급될 수 있습니다.
습기 보호 기능이 있는 표준 해상 운송용 수출 포장이 사용되며, 특정 요구 사항은 주문 시 확인됩니다.
린시의 장점
린시 알루미늄은 항공우주, 일반 엔지니어링, 자동차, 해양, 조선 및 기타 특수 산업 분야를 포함한 다양한 산업 분야에 서비스를 제공하는 알루미늄 가공 제품의 선도적인 공급업체입니다.
당사는 인증에서 알 수 있듯이 최고 수준의 품질과 환경적 책임을 유지하기 위해 최선을 다하고 있습니다: ISO 9001:2008, ISO 14001:2004 및 SGS.