5082-O/H18/H38 Filo di alluminio

What Is 5082 Aluminum Wire?

5082 aluminum wire is drawn from the same AlMg4.5 alloy used for 5082 sheet and plate, but delivered as coiled or spooled wire. Being non-heat-treatable, its strength is set by the temper: O is soft and formable, H18 is strain-hardened to a medium level, and H38 is the strongest of the three. The wire keeps the alloy’s good corrosion resistance and weldability, making it useful for rivets, fasteners, and welded assemblies.

Note that 5082 wire is distinct from aluminum welding filler wire (such as 5356); 5082 wire is supplied for mechanical and forming use rather than as a welding consumable, though it can be used where its composition is acceptable to the procedure.

Available 5082 Aluminum Wire Products

Linsy draws 5082 wire in the following ranges. Other diameters and coil formats can be negotiated.

5082 Aluminum Wire — Diameter & Packaging

Parametro	Typical Range	Note
Diametro	0.8 – 12 mm	Other sizes on request
Diameter tolerance	± 0.05 mm	Tighter tolerance available
Tempers	O, H18, H38
Coil / spool weight	10 – 500 kg	Custom pack per enquiry
Standards	ASTM B211, ASTM B221, EN 755-2, GB/T 3191

Specifiche e denominazioni equivalenti

Barra e Tondino	Denominazione
6–400 mm	5082 / A95082
IT	EN AW-5082 (AlMg4.5)
Common standards	ASTM B211, ASTM B221, EN 755-2, GB/T 3191

Composizione chimica

Composition follows the AA 5082 specification. Values are weight percent, balance aluminium.

Elemento	Contenuto (%)
Silicio (Si)	Famiglia
Ferro (Fe)	0.35 max
Rame (Cu)	0,15 max
Manganese (Mn)	0.15 – 0.35
Magnesio (Mg)	4.00 – 5.00
Cromo (Cr)	0,15 max
Zinco (Zn)	0,25 max
Titanio (Ti)	0,10 max
Others (each / total)	0.05 / 0.15
Alluminio (Al)	Equilibrio

Proprietà meccaniche in base al trattamento termico

Typical room-temperature properties for 5082 wire. Values are indicative and should be confirmed against the ordered specification and diameter.

Temperamento	Resistenza alla trazione (MPa)	Resistenza allo snervamento (MPa)	Allungamento (%)
O	275	125	22
H18	380	330	10
H38	400	350	9

Guida alla scelta della tempra

• O – Soft and formable; for rivets, deep drawing, and complex forming.
• H18 – Medium strength with good spring character; general fasteners and formed parts.
• H38 – Highest strength of the three; structural and high-load wire applications.

Caratteristiche principali

Good Strength-to-Weight

Strain-hardened 5082 wire reaches useful tensile strengths while staying light.

Resistenza alla corrosione

Retains the alloy’s seawater and industrial-atmosphere corrosion resistance.

Formability & Weldability

O temper forms readily; the alloy welds well with 5xxx fillers where welding is required.

Dimensional Control

Drawn to tight diameter tolerances and supplied on coils or spools for automated feeding.

Applicazioni

• Rivets and structural fasteners
• Automotive and transport body components
• Welded fabricated assemblies
• Industrial wire products and formed parts
• Pressure-vessel and marine fittings

Note sulla lavorazione e sulla finitura superficiale

• Drawing & straightening: Supplied as coil, spool, or straightened cut lengths.
• Formazione: O temper is best for riveting and bending; H tempers need verified bend radii.
• parti strutturali leggere e decorative MIG/TIG with 5xxx filler where the wire is part of a welded assembly.
• Surface: Mill (bright drawn) finish; PVC or paper interleave available for spooled wire.

Documenti di qualità e ispezione

Every 5082 wire coil ships with a Mill Test Certificate (MTC) covering chemical composition and mechanical properties. SGS or third-party test reports are available on request. Linsy’s production is managed under ISO 9001, ISO 14001, and ISO 45001 systems.

Why Choose Linsy for 5082 Wire

Linsy is a Shenzhen-based aluminum supplier with more than 20 years of experience across the 1000-8000 series. For 5082 wire we offer in-house drawing, straightening, spooling, and cut-to-length, with typical custom lead times of 10-60 days depending on diameter and quantity. MTC is supplied with every order.

Risorse correlate

For deeper technical background on 5082 and related alloys, see the following resources from Linsy’s knowledge library:

• 5xxx Series Aluminum Alloys: A Buyer’s Guide – how to select the right Al-Mg alloy for your project
• 5082 vs 5083 Aluminum: Strength and Corrosion Compared – which medium-Mg grade fits your application
• Aluminum Wire & Rod: Forms, Tempers, and Uses – selecting wire diameter and temper for fasteners and forming
• Understanding Aluminum Temper Designations: O, H, and T – what temper codes mean and how to choose the right one

5082 Aluminum Wire FAQ

What tempers are available for 5082 wire?

Common tempers are O (soft), H18 (medium strength), and H38 (highest strength of the three).

Is 5082 wire the same as 5356 welding wire?

No. 5082 wire is supplied for mechanical and forming use; 5356 is a dedicated welding filler alloy with a different composition. Use the filler specified by your welding procedure.

What diameters can Linsy supply?

Typical diameters are 0.8-12 mm, with tolerances around ±0.05 mm. Other sizes can be quoted on request.

Can 5082 wire be anodized?

It can be anodized, but 5xxx alloys produce a grey tone; powder coating is often preferred for appearance.

Qual è il tempo di consegna standard?

Typical custom lead time is 10-60 days depending on diameter, temper, and quantity.

Domande frequenti generali sugli ordini

Qual è la quantità minima d'ordine?

MOQs depend on diameter and coil format. Smaller stock sizes may have lower MOQs; fully custom sizes are quoted per enquiry.

Fornite certificati di prova del laminatoio?

Yes. An MTC is supplied with every order, and SGS or third-party inspection reports can be arranged on request.

Which certifications does Linsy hold?

Production is managed under ISO 9001, ISO 14001, and ISO 45001 systems. Material can be supplied to ASTM, EN, GB, and JIS standards on request.

Can you supply cut lengths or spools?

Yes. 5082 wire is available as coil, spool, or straightened cut-to-length pieces.