6082 filo di alluminio (EN AW-6082) is a heat-treatable 6000-series wire known for strong specific strength, good corrosion resistance, and high fatigue performance. Supplied in O, T4, T6, and T651 tempers with diameters from 0.8–30 mm, it is used for welding wire, rivets, fasteners, and highly stressed structural components. Linsy provides 6082 wire with an MTC on every coil and export-grade packaging.
Moduli disponibili: wire / spool / coil
Temperamenti comuni: O / T4 / T6 / T651
Supporto per l'elaborazione: drawing / straightening / spooling
Documenti di qualità: Rapporto MTC allegato a ogni ordine
6082 aluminum wire (EN AW-6082, AlSi1MgMn) is a heat-treatable 6000-series wire valued for its strength, corrosion resistance, and good fatigue performance. With added manganese, it holds structural integrity better than 6061 in demanding applications, and is commonly drawn in O, T4, T6, and T651 tempers.
It serves as welding wire, rivets, fasteners, and feedstock for stressed structural components where a light, strong, and weldable material is required.
| Forma | Tempra comuni | Intervallo dimensionale tipico |
|---|---|---|
| Wire (drawn) | O, T4, T6, T651 | Diameter 0.8–30 mm |
| Spool / Coil | O, T4, T6, T651 | Min 50 kg per coil; tolerance per spec |
Wire is supplied on spools or coils with a minimum of 50 kg per coil. Diameter tolerance follows the agreed specification (for example ASTM B211 or EN 755-2). Custom diameters and tempers can be discussed at order.
| Denominazione | Valore |
|---|---|
| EN AW | EN AW-6082 |
| UNS | A96082 |
| Norme comuni | ASTM B211, ASTM B221, AWS A5.10, EN 755-2, GB/T 3191 |
| Tempre | O, T4, T6, T651 |
| Diametro | 0,8–30 mm |
| Elemento | Composizione (wt%) |
|---|---|
| Si | 0.70 – 1.30 |
| Fe | 0,50 max |
| Cu | 0,10 max |
| Mn | 0.40 – 1.00 |
| Mg | 0.60 – 1.20 |
| Cr | 0,25 max |
| Zn | Famiglia |
| Ti | 0,15 max |
| Altri (ciascuno) | 0,05 max |
| Altri (totale) | 0,15 max |
| Al | Resto |
Typical reference values for 6082 wire; confirm against the ordered standard and Linsy’s mill data.
| Temperamento | Resistenza alla trazione (MPa) | Resistenza allo snervamento (MPa) | Allungamento (%, min) |
|---|---|---|---|
| O | 120 | 65 | 22 |
| T4 | 205 | 110 | 16 |
| T6 | 310 | 270 | 10 |
| T651 | 310 | 270 | 10 |
Higher manganese gives 6082 strong performance in cyclic-load applications versus 6061.
Good in atmospheric and many industrial environments.
Suitable as welding wire with compatible filler; produces sound joints for structural assemblies.
6082 machines well in the soft (O) and solution-heat-treated tempers; T6/T651 tempers are stronger and can work-harden at the cutting edge, so sharp tooling and appropriate feeds are recommended.
6082 is generally weldable using TIG or MIG processes with matching or 4043/5356 filler, depending on the service requirement. Welded zones lose some strength compared with the base temper — design accordingly for structural use.
La formatura è ottimale nelle condizioni O o T4. La resistenza finale viene sviluppata dal trattamento specificato; non ritrattare termicamente senza confermare la risposta della lega.
Finiture comuni includono anodizzazione, lucidatura e verniciatura a polvere. La qualità dell'anodizzazione dipende dalla preparazione superficiale, quindi confermare i requisiti di finitura prima della produzione.
Every 6082 wire order ships with an MTC reporting chemical composition and mechanical properties. Third-party SGS reports can be arranged on request. Confirm the required standard (ASTM, EN, GB) when ordering.
Linsy opera con una base produttiva a Shenzhen con oltre 20 anni di esperienza nella fornitura di semilavorati in alluminio a acquirenti B2B globali. Gestiamo le serie dalla 1000 alla 8000 e supportiamo sia dimensioni standard di magazzino che misure su ordinazione.
O, T4, T6, and T651, with T6/T651 preferred for high-strength fasteners and welding wire.
Typically 0.8–30 mm, with custom sizes available on request.
Yes. It welds well by TIG/MIG and is used as welding wire for structural aluminum assemblies.
Gli articoli standard in magazzino vengono solitamente spediti entro 10–30 giorni. Dimensioni, tempere o finiture superficiali personalizzate richiedono generalmente 30–60 giorni, in base alle specifiche e al volume dell'ordine.
Sì. Ogni ordine viene spedito con un certificato di collaudo del materiale (MTC) che riporta la composizione chimica e le proprietà meccaniche secondo lo standard ordinato.
Sì. Forniamo dimensioni standard e su misura per lamiere, lastre, barre, tubi e profilati, e possiamo organizzare tempere specifiche su richiesta.
Le operazioni seguono le norme ISO 9001, ISO 14001 e ISO 45001. Il materiale può essere fornito secondo le specifiche ASTM, EN, GB o JIS, a seconda delle esigenze.
Viene utilizzato un imballaggio standard per esportazione marittima con protezione dall'umidità; eventuali requisiti specifici vengono confermati al momento dell'ordine.
Vantaggi Linsy
Linsy Aluminum è un fornitore leader di prodotti per la lavorazione dell'alluminio, che serve diversi settori, tra cui quello aerospaziale, dell'ingegneria generale, automobilistico, marittimo, navale e altre applicazioni industriali specializzate.
Ci impegniamo a mantenere i più alti standard di qualità e responsabilità ambientale, come dimostrano le nostre certificazioni: ISO 9001:2008, ISO 14001:2004 e SGS.