6082 알루미늄 와이어 (EN AW-6082) is a heat-treatable 6000-series wire known for strong specific strength, good corrosion resistance, and high fatigue performance. Supplied in O, T4, T6, and T651 tempers with diameters from 0.8–30 mm, it is used for welding wire, rivets, fasteners, and highly stressed structural components. Linsy provides 6082 wire with an MTC on every coil and export-grade packaging.
이용 가능한 양식: wire / spool / coil
흔히 나타나는 기질: O / T4 / T6 / T651
처리 지원: drawing / straightening / spooling
품질 관련 문서: 모든 주문 시 MTC 보고서 제공
6082 aluminum wire (EN AW-6082, AlSi1MgMn) is a heat-treatable 6000-series wire valued for its strength, corrosion resistance, and good fatigue performance. With added manganese, it holds structural integrity better than 6061 in demanding applications, and is commonly drawn in O, T4, T6, and T651 tempers.
It serves as welding wire, rivets, fasteners, and feedstock for stressed structural components where a light, strong, and weldable material is required.
| 양식 | 일반적인 템퍼 | 일반적인 치수 범위 |
|---|---|---|
| Wire (drawn) | O, T4, T6, T651 | Diameter 0.8–30 mm |
| Spool / Coil | O, T4, T6, T651 | Min 50 kg per coil; tolerance per spec |
Wire is supplied on spools or coils with a minimum of 50 kg per coil. Diameter tolerance follows the agreed specification (for example ASTM B211 or EN 755-2). Custom diameters and tempers can be discussed at order.
| 명칭 | 가치 |
|---|---|
| EN AW | EN AW-6082 |
| UNS | A96082 |
| Common standards | ASTM B211, ASTM B221, AWS A5.10, EN 755-2, GB/T 3191 |
| 분노 | O, T4, T6, T651 |
| 지름 | 0.8–30 mm |
| 요소 | 조성 (중량%) |
|---|---|
| Si | 0.70 – 1.30 |
| Fe | 0.50 최대 |
| Cu | 최대 0.10 |
| Mn | 0.40 – 1.00 |
| Mg | 0.60 – 1.20 |
| Cr | 최대 0.25 |
| Zn | 0.20 최대 |
| Ti | 최대 0.15 |
| 기타(각) | 최대 0.05 |
| 기타(합계) | 최대 0.15 |
| Al | 나머지 |
Typical reference values for 6082 wire; confirm against the ordered standard and Linsy’s mill data.
| 성질 | 인장 강도(MPa) | 항복 강도(MPa) | 연신율 (%, 최소) |
|---|---|---|---|
| O | 120 | 65 | 22 |
| T4 | 205 | 110 | 16 |
| T6 | 310 | 270 | 10 |
| T651 | 310 | 270 | 10 |
Higher manganese gives 6082 strong performance in cyclic-load applications versus 6061.
Good in atmospheric and many industrial environments.
Suitable as welding wire with compatible filler; produces sound joints for structural assemblies.
6082 machines well in the soft (O) and solution-heat-treated tempers; T6/T651 tempers are stronger and can work-harden at the cutting edge, so sharp tooling and appropriate feeds are recommended.
6082 is generally weldable using TIG or MIG processes with matching or 4043/5356 filler, depending on the service requirement. Welded zones lose some strength compared with the base temper — design accordingly for structural use.
성형은 O 또는 T4 상태에서 가장 잘 수행됩니다. 최종 강도는 지정된 템퍼에 의해 발현됩니다. 합금의 반응을 확인하지 않고 재열처리하지 마십시오.
일반적인 마감 처리에는 아노다이징, 연마 및 분체 코팅이 포함됩니다. 아노다이징 품질은 표면 처리에 따라 달라지므로, 생산 전에 마감 요구 사항을 확인하십시오.
Every 6082 wire order ships with an MTC reporting chemical composition and mechanical properties. Third-party SGS reports can be arranged on request. Confirm the required standard (ASTM, EN, GB) when ordering.
Linsy는 20년 이상의 경험을 가진 선전 생산 기지를 운영하며 글로벌 B2B 구매자에게 알루미늄 반제품을 공급하고 있습니다. 1000계열부터 8000계열까지 취급하며, 표준 재고 치수와 주문 제작 치수를 모두 지원합니다.
O, T4, T6, and T651, with T6/T651 preferred for high-strength fasteners and welding wire.
Typically 0.8–30 mm, with custom sizes available on request.
Yes. It welds well by TIG/MIG and is used as welding wire for structural aluminum assemblies.
표준 재고 품목은 일반적으로 10~30일 이내에 배송됩니다. 맞춤형 치수, 템퍼 또는 표면 마감은 사양과 주문량에 따라 일반적으로 30~60일이 소요됩니다.
예. 모든 주문에는 주문된 표준에 따른 화학 성분 및 기계적 특성을 보고하는 MTC가 함께 발송됩니다.
예. 당사는 시트, 플레이트, 바, 튜브 및 프로파일의 표준 및 주문 제작 치수를 공급하며, 요청 시 특정 템퍼를 준비할 수 있습니다.
운영은 ISO 9001, ISO 14001 및 ISO 45001을 따릅니다. 재료는 필요에 따라 ASTM, EN, GB 또는 JIS 사양으로 공급될 수 있습니다.
습기 보호 기능이 있는 표준 해상 운송용 수출 포장이 사용되며, 특정 요구 사항은 주문 시 확인됩니다.
린시의 장점
린시 알루미늄은 항공우주, 일반 엔지니어링, 자동차, 해양, 조선 및 기타 특수 산업 분야를 포함한 다양한 산업 분야에 서비스를 제공하는 알루미늄 가공 제품의 선도적인 공급업체입니다.
당사는 인증에서 알 수 있듯이 최고 수준의 품질과 환경적 책임을 유지하기 위해 최선을 다하고 있습니다: ISO 9001:2008, ISO 14001:2004 및 SGS.