Lega di alluminio 6106 (EN AW-6106, AlMgSiMn) is a medium-strength 6000-series grade with good extrudability, corrosion resistance, and weldability. It is widely used for automotive, rail, marine, and architectural structures that need light yet durable material. Linsy supplies 6106 as sheet, bar, tube, wire, and extruded profile in O/T4/T6 with made-to-order sizes and an MTC on every order.
Moduli disponibili: sheet / coil / bar / tube / wire / profile
Temperamenti comuni: O / T4 / T6
Supporto per l'elaborazione: CNC machining / extrusion / welding / anodizing
Documenti di qualità: Rapporto MTC allegato a ogni ordine
6106 (EN AW-6106, AlMgSiMn) is a medium-strength 6000-series alloy with magnesium, silicon, and manganese. It offers a favorable balance of extrudability, corrosion resistance, weldability, and moderate strength, which suits structural and transportation components that need to be light yet durable.
| Forma | Common Tempers | Typical Size Range |
|---|---|---|
| Lamiera e Bobina | Stati di fornitura comuni | Thickness 0.5–150 mm; Width 500–2600 mm; Length 500–12000 mm |
| Bar (Round/Square/Flat) | Stati di fornitura comuni | Diameter/side 6–400 mm; Length 1000–6000 mm |
| Tube (Round/Square) | Stati di fornitura comuni | OD 10–400 mm; Wall 1–40 mm; Length 1000–6000 mm |
| Filo | Stati di fornitura comuni | 0.8–30 mm |
| Spessore parete | T4, T6 | In base al disegno fornito dal cliente |
Formed and cut parts in O, T4, and T6.
Round, square, and flat bars for machined and structural use.
Round and square tubes for frameworks and transport structures.
Drawn wire for welding and assembly.
Extruded profiles to drawing in T4 and T6.
| Denominazione | Valore |
|---|---|
| EN AW | EN AW-6106 (AlMgSiMn) |
| UNS | A96106 |
| 1000–6000 mm o bobina | Stati di fornitura comuni |
| Key property | Extrusion-friendly medium strength |
| Standards | ASTM B221, EN 755, GB/T 3190 |
| Elemento | Composizione (wt%) |
|---|---|
| Si | 0.40 – 0.80 |
| Fe | 0,50 max |
| Cu | 0,10 max |
| Mn | 0,15 max |
| Mg | 0.60 – 1.00 |
| Cr | 0,10 max |
| Zn | 0,10 max |
| Ti | 0,10 max |
| Altri (ciascuno) | 0,05 max |
| Altri (totale) | 0,15 max |
| Al | Resto |
Typical reference values; confirm against the ordered standard and Linsy’s mill data.
| Temperamento | Resistenza alla trazione (MPa) | Resistenza allo snervamento (MPa) | Elongation (%, min) |
|---|---|---|---|
| O | 110 | 60 | 22 |
| T4 | 200 | 120 | 16 |
| T6 | 260 | 220 | 10 |
Good die fill and surface quality make 6106 well suited to complex profiles.
Good corrosion resistance and readily weldable for transport and structural assemblies.
Sits between soft 6xxx grades and high-strength structural 6082.
6106 machines well in the soft (O) and solution-heat-treated tempers; T6/T651 tempers are stronger and can work-harden at the cutting edge, so sharp tooling and appropriate feeds are recommended.
6106 is generally weldable using TIG or MIG processes with matching or 4043/5356 filler, depending on the service requirement. Welded zones lose some strength compared with the base temper — design accordingly for structural use.
Forming is best done in the O or T4 condition. Final strength is developed by the specified temper; do not re-heat-treat without confirming the alloy’s response.
Common finishes include anodizing, polishing, and powder coating. Anodizing quality depends on surface preparation, so confirm finish requirements before production.
Every 6106 order ships with an MTC. Third-party SGS reports can be arranged on request. Confirm the required standard (ASTM, EN, GB) when ordering.
Linsy operates a Shenzhen production base with over 20 years of experience supplying aluminum semis to global B2B buyers. We handle the 1000 through 8000 series and support both standard stock sizes and made-to-order dimensions.
Automotive, rail, marine, and architectural structures needing a light, weldable, medium-strength alloy.
6106 offers higher strength and is more extrusion-oriented, while 6063 is the classic architectural/decoration grade.
O, T4, and T6, with T6 giving the highest strength.
Standard stock items usually ship within 10–30 days. Custom sizes, tempers, or surface finishes typically require 30–60 days, depending on specification and order volume.
Yes. Every order ships with an MTC reporting chemical composition and mechanical properties per the ordered standard.
Yes. We supply standard and made-to-order dimensions across sheet, plate, bar, tube, and profile, and can arrange specific tempers on request.
Operations follow ISO 9001, ISO 14001, and ISO 45001. Material can be supplied to ASTM, EN, GB, or JIS specifications as required.
Standard seaworthy export packaging with moisture protection is used; specific requirements are confirmed at order.
Vantaggi Linsy
Linsy Aluminum è un fornitore leader di prodotti per la lavorazione dell'alluminio, che serve diversi settori, tra cui quello aerospaziale, dell'ingegneria generale, automobilistico, marittimo, navale e altre applicazioni industriali specializzate.
Ci impegniamo a mantenere i più alti standard di qualità e responsabilità ambientale, come dimostrano le nostre certificazioni: ISO 9001:2008, ISO 14001:2004 e SGS.