6951 aluminum is a heat-treatable 6000-series alloy developed as a brazing-sheet core material for radiators and heat exchangers. Its balanced silicon and magnesium content gives good strength after brazing while resisting core erosion during vacuum or controlled-atmosphere brazing. Linsy supplies 6951 as sheet, coil, tube, bar, and wire in O, T4, and T6 tempers.
Moduli disponibili: sheet / coil, tube, bar / rod, wire
Temperamenti comuni: T6, T4, O
Supporto per l'elaborazione: Lavorazione CNC, taglio laser, saldatura TIG/MIG, anodizzazione, lucidatura, verniciatura a polvere
Documenti di qualità: Rapporto MTC allegato a ogni ordine
6951 is commonly used as the core layer of clad brazing sheet, paired with a cladding alloy such as 4343 or 4045 on one or both faces. During the brazing cycle the cladding melts and flows to seal joints, while the 6951 core keeps the assembly strong and formable. It is widely specified in automotive and HVAC heat exchangers.
| Parametro | Spessore |
|---|---|
| Spessore | 0,3 – 150 mm |
| Larghezza | 500 – 2600 mm |
| Lunghezza | 500 – 16000 mm |
| Tempre | O, T4, T6, T651 |
| Parametro | Spessore |
|---|---|
| Diametro esterno | 6 – 300 mm |
| Spessore della parete | 0,5 – 40 mm |
| Lunghezza | fino a 12000 mm |
| Tempre | Stati di fornitura comuni |
| Parametro | Spessore |
|---|---|
| Diametro | 3 – 300 mm |
| Lunghezza | fino a 12000 mm |
| Tempre | Stati di fornitura comuni |
| Parametro | Spessore |
|---|---|
| Diametro | 0.8 – 30 mm |
| Peso della bobina | min 50 kg |
| Tempre | O, T6 |
| Denominazione | Riferimento |
|---|---|
| 6–400 mm | A96951 |
| EN AW | EN AW-6951 |
| Norme comuni | ASTM B209, ASTM B210, EN 573, GB/T 3190 |
| Serie | 6000 (Al-Mg-Si brazing core) |
| Elemento | Contenuto (wt%) |
|---|---|
| Silicio (Si) | 0.20 – 0.50 |
| Ferro (Fe) | 0,80 max |
| Rame (Cu) | 0.15 – 0.40 |
| Manganese (Mn) | 0,10 max |
| Magnesio (Mg) | 0,40 – 0,80 |
| Cromo (Cr) | 0,05 – 0,20 |
| Zinco (Zn) | Famiglia |
| Titanio (Ti) | 0,15 max |
| Altri, ciascuno | 0,05 max |
| Altri, totale | 0,15 max |
| Alluminio (Al) | Equilibrio |
| Temperamento | Resistenza a trazione (MPa) | Snervamento (MPa) | Allungamento (%) |
|---|---|---|---|
| T6 | 270 – 310 | 230 – 270 | 8 – 12 |
| T4 | 200 – 240 | 120 – 160 | 14 – 18 |
| O | ≤ 160 | ≤ 70 | ≥ 18 |
Soft core for maximum formability before brazing; often the as-clad supplied condition.
Solution heat treated and naturally aged; good forming plus moderate strength.
Peak strength after artificial aging; used where the core must carry load after brazing.
Engineered to survive vacuum and controlled-atmosphere brazing with low core erosion.
Good heat transfer for compact cooling systems.
Resists atmospheric and chemical attack for long service life.
Forms into fins, manifolds, and intricate heat-exchanger shapes.
6951 is normally supplied as clad brazing sheet (core plus 4343/4045 cladding) for furnace brazing. It forms well and can be welded where cladding is absent, but the brazing cladding must be protected from contamination. Anodizing is possible but less common than for decorative 6xxx alloys.
Ogni ordine viene spedito con un Certificato di Prova del Materiale (MTC) che registra la composizione e i risultati meccanici. Il nostro sistema di qualità è certificato secondo ISO 9001, ISO 14001 e ISO 45001. Rapporti di prova SGS di terze parti possono essere organizzati su richiesta. L'ispezione copre dimensioni, condizioni superficiali e verifica meccanica per tempra.
Linsy Aluminum is a Shenzhen-based aluminum manufacturer with more than 20 years of experience supplying the 1000 to 8000 series in plate, bar, tube, wire, coil, profile, and block forms. For 6951 aluminum, we support both off-the-shelf ranges and made-to-order dimensions.
See the blog articles linked below for deeper background, and contact our team for a tailored quote on 6951 aluminum.
Almost always as the core of clad brazing sheet, with a lower-melting cladding alloy such as 4343 or 4045 on one or both faces. Specify cladding when requesting a quote.
3003 is a non-heat-treatable brazing core with lower strength; 6951 is heat-treatable and stronger after brazing, suiting higher-pressure exchangers.
O or T4 are common as-supplied conditions because they form easily before the braze cycle; T6 cores are used where post-braze strength matters.
Dimensioni e trattamenti personalizzati vengono solitamente spediti entro 10-60 giorni. Confermare la finestra esatta quando si richiede un preventivo, poiché dipende dalla lega, dal trattamento, dalle dimensioni e dalla quantità ordinata.
Il MOQ è flessibile e valutato caso per caso. Piccoli lotti e prototipi possono spesso essere accolti; produzioni più grandi o standard sono più economiche. Comunicare le dimensioni e la quantità richieste per un preventivo definitivo.
Ogni ordine viene spedito con un Certificato di Prova in Fabbrica (MTC). Le certificazioni ISO 9001, ISO 14001 e ISO 45001 si applicano al nostro sistema di gestione. Rapporti di prova di terze parti SGS possono essere organizzati su richiesta.
Sì. Forniamo lavorazioni CNC, taglio laser, saldatura TIG/MIG e trattamenti superficiali tra cui anodizzazione, lucidatura, verniciatura a polvere e protezione con film in PVC.
Inviare lega/trattamento, forma richiesta, dimensioni, quantità ed eventuali requisiti di lavorazione o certificazione. Il nostro team restituirà un preventivo con tempi di consegna e condizioni di spedizione.
Vantaggi Linsy
Linsy Aluminum è un fornitore leader di prodotti per la lavorazione dell'alluminio, che serve diversi settori, tra cui quello aerospaziale, dell'ingegneria generale, automobilistico, marittimo, navale e altre applicazioni industriali specializzate.
Ci impegniamo a mantenere i più alti standard di qualità e responsabilità ambientale, come dimostrano le nostre certificazioni: ISO 9001:2008, ISO 14001:2004 e SGS.