5383 aluminum is a high-strength, non-heat-treatable Mg-Mn alloy developed as an improved alternative to 5083, offering higher weld-joint strength and good resistance to exfoliation and stress corrosion cracking. Supplied mainly in H116 and H321 tempers, it is engineered for demanding marine, shipbuilding, and transport structures where payload and structural integrity are critical.
이용 가능한 양식: 시트 / 플레이트 / 코일 / 봉 / 튜브 / 압출 프로파일
흔히 나타나는 기질: O, H111, H112, H116, and H321
처리 지원: CNC 가공 / 레이저 절단 / 연마 / 양극 산화 처리
품질 관련 문서: 모든 주문 시 MTC 보고서 제공
5383 is a non-heat-treatable wrought aluminum alloy in the 5xxx (Al-Mg) family, formulated with roughly 4.5 to 5 percent magnesium plus manganese. It was developed as a higher-strength successor to 5083, delivering improved weld-joint strength and better resistance to exfoliation and stress corrosion cracking. Because it is strain-hardened rather than heat-treated, its properties come from cold work in the H tempers.
Linsy supplies 5383 in the forms most used for marine and transport structures. The tempers most commonly supplied are O, H111, H112, H116, and H321. 아래 치수는 일반적인 범위이며, 기타 크기는 요청 시 협의 가능합니다.
5383 sheet and coil are supplied in thicknesses from 0.5 mm to 12 mm, widths up to 2600 mm, and lengths up to 6000 mm or cut to size. H116 and H321 are the standard shipbuilding tempers.
5383 plate is available from 6 mm up to 120 mm thick, with standard widths up to 3000 mm. Thick plate is typically ordered in H321 or H116 for hull and deck structures.
Round, flat, and square bars are produced in diameters or side lengths from 6 mm to 300 mm, commonly in H111, H112, or O temper.
5383 seamless and welded tube can be supplied in outer diameters from 6 mm to 400 mm with wall thicknesses from 0.5 mm to 40 mm. Marine and pressure-service tempers are H116 or H321.
Extruded angles, channels, and custom profiles are available on request, normally in H111 or H112 temper.
5383 is identified by the following common standards and designations.
| 표준 | 명칭 |
|---|---|
| AA | 5383 |
| UNS | A95383 |
| EN AW | EN AW-5383 |
| Common name | AlMg4.5Mn (approx.) |
The typical composition of 5383 aluminum is listed below in weight percent, with aluminum as the balance.
| 요소 | 구성 (%) |
|---|---|
| 실리콘(Si) | 0.40 최대 |
| 철(Fe) | 0.40 최대 |
| 구리(Cu) | 최대 0.10 |
| 망간(Mn) | 0.40 – 1.00 |
| 마그네슘(Mg) | 4.0 – 5.2 |
| 크롬(Cr) | 0.05 – 0.25 |
| 아연(Zn) | 0.15 – 0.50 |
| 티타늄(Ti) | 최대 0.15 |
| 기타 각각 | 0.05 |
| 기타 합계 | 0.15 |
| 알루미늄(Al) | 잔액 |
아래 값은 압연 및 압출 제품의 일반적인 값이며, 주문된 특정 템퍼 및 두께에 대한 밀 시험 성적서로 확인해야 합니다.
| 성질 | 인장 강도(MPa) | 항복 강도(MPa) | 연신율 (%) |
|---|---|---|---|
| O | 290 – 340 | 145 min | 16 |
| H111 | 290 min | 145 min | 14 |
| H112 | 290 min | 145 min | 12 |
| H116 | 340 min | 240 min | 12 |
| H321 | 340 min | 240 min | 12 |
Choose H116 or H321 for welded marine structures where corrosion resistance and strength after welding matter most. O and H111 suit general fabrication and forming, while H112 is used for extruded and less-critical structural parts.
5383 was designed so welded joints retain more strength than those made with 5083, an important advantage for hull and tank fabrication.
It resists seawater, exfoliation, and stress corrosion cracking well, which is why it is favored in shipbuilding.
As a high-magnesium 5xxx grade it is stronger than 5083 in the same temper, while remaining workable.
In O and H111 tempers it forms and bends reasonably well; highly strain-hardened tempers are less formable.
5383 welds well with MIG and TIG processes using matching or compatible 5xxx fillers; post-weld heat treatment is not used because the alloy is not heat-treatable. It can be cut, drilled, and CNC machined, and is supplied laser-cut or sawn to size. Note that 5xxx alloys anodize to a darker gray tone rather than a bright finish, so anodizing is rarely specified for 5383.
Linsy는 모든 선적에 대해 밀 시험 성적서(MTC)를 제공하며, 해당되는 경우 EN 10204 3.1에 따른 화학 성분 및 기계적 특성을 문서화합니다. 제3자 검사 및 SGS 재료 시험 보고서는 요청 시 준비 가능합니다. 생산은 ISO 9001(품질), ISO 14001(환경) 및 ISO 45001(산업 안전 보건) 시스템 하에 관리됩니다.
Linsy Aluminum operates a production and processing base with over 20 years of experience across the 1xxx to 8xxx aluminum series. For 5383, we supply sheet, plate, bar, tube, and extruded profiles with optional CNC machining, laser cutting, and surface finishing such as anodizing and polishing. Every order is shipped with a mill test certificate (MTC), and production follows ISO 9001, ISO 14001, and ISO 45001 management systems. Custom dimensions and tempers can be arranged, with typical lead times of 10 to 60 days depending on the specification.
5383 has a slightly higher magnesium content and is formulated so welded joints are stronger, while corrosion resistance is comparable. It is often chosen when weld efficiency is critical.
No. It is a non-heat-treatable 5xxx alloy; its strength comes from strain hardening in the H tempers.
H116 and H321 are the standard marine tempers for plate and sheet in shipbuilding.
It can, but it produces a darker gray finish than the bright trim grades such as 5457 or 5657, so anodizing is uncommon for this alloy.
최소 주문 수량은 형태와 템퍼에 따라 달라집니다. 표준 재고 품목은 보통 수백 킬로그램부터 시작하며, 맞춤형 사이즈는 문의 시 견적이 제공됩니다.
표준 사양은 일반적으로 10일에서 60일 이내에 공급 가능합니다. 맞춤형 템퍼나 치수는 더 오래 걸릴 수 있으며, 각 견적 시 납기를 확인해 드립니다.
모든 주문에 대해 밀 테스트 인증서(MTC)가 포함됩니다. 생산은 ISO 9001, ISO 14001 및 ISO 45001 시스템 인증을 보유하고 있으며, SGS 또는 제3자 시험 보고서는 요청 시 제공 가능합니다.
네. Linsy는 절단 맞춤, 맞춤형 치수 및 선택된 템퍼를 지원합니다. 견적을 위해 도면이나 사양을 보내주시기 바랍니다.
제품은 운송 중 표면 손상을 방지하기 위해 포장되며, 수출 기준의 해상 운송용 포장이 제공됩니다.
린시의 장점
린시 알루미늄은 항공우주, 일반 엔지니어링, 자동차, 해양, 조선 및 기타 특수 산업 분야를 포함한 다양한 산업 분야에 서비스를 제공하는 알루미늄 가공 제품의 선도적인 공급업체입니다.
당사는 인증에서 알 수 있듯이 최고 수준의 품질과 환경적 책임을 유지하기 위해 최선을 다하고 있습니다: ISO 9001:2008, ISO 14001:2004 및 SGS.