2017 (AlCu4MgSi) is a heat-treatable 2xxx-series aluminum alloy valued for its high strength, good machinability, and moderate corrosion resistance. As the US equivalent of the Chinese 2A11 standard, 2017 is widely specified for rivets, fasteners, and structural components in aerospace and general engineering — especially where formability in the O temper and strength after T4 heat treatment are both required.
Verfügbare Formulare: sheet / plate / bar / tube / wire
Häufige Temperamente: O / T3 / T4 / T351 / T42 / T451
Unterstützung bei der Bearbeitung: CNC machining / cold forming / drilling / anodizing
Qualitätsdokumente: MTC-Bericht bei jeder Bestellung
2017 aluminum alloy (UNS A92017, EN AW-2017) is a copper-based, heat-treatable alloy in the 2xxx series. Its nominal composition — approximately 3.5–4.5% Cu, 0.4–1.0% Mn, 0.4–0.8% Mg, and 0.2–0.8% Si — gives it a combination of strength and machinability that makes it a practical choice for forged and machined structural parts.
In the annealed (O) condition, 2017 exhibits good ductility for cold-forming operations such as riveting. After solution heat treatment and natural aging (T4), it develops tensile strength up to approximately 390 MPa — comparable to many higher-strength aerospace alloys, though with somewhat lower corrosion resistance than 2xxx alloys containing higher magnesium.
2017 is the direct US equivalent of the Chinese 2A11 (GB/T 3190) and Russian D1 alloy designations. It is sometimes referred to as AlCu4MgSi under the ISO designation system.
Linsy Aluminum supplies 2017 alloy across a range of product forms and tempers. All products can be cut to custom dimensions; typical lead times for custom sizes are 10–60 days.
| Formular | Temperament | Dicke (mm) | Breite (mm) | Länge (mm) |
|---|---|---|---|---|
| Blatt | O, T3, T351, T4, T42, T451 | 0.3–6.0 | 500–2200 | 1000–6000 |
| Platte | O, T3, T351, T4, T42, T451 | 6.0–200 | 500–2200 | 1000–6000 |
| Dimensions can be customized to project requirements | ||||
| Formular | Temperament | Diameter / Thickness (mm) | Länge (mm) |
|---|---|---|---|
| Round bar | O, T3, T351, T4, T42, T451 | 3–500 | 1000–6000 |
| Flat bar | O, T3, T351, T4, T42, T451 | 3–200 (thickness) | 1000–6000 |
| Square bar | O, T3, T351, T4, T42, T451 | 3–200 | 1000–6000 |
| Dimensions can be customized to project requirements | |||
| Formular | Temperament | Äußerer Durchmesser (mm) | Innendurchmesser (mm) | Länge (mm) |
|---|---|---|---|---|
| Round tube | O, T3, T351, T4, T42, T451 | 6–350 | 4–320 | 1000–6000 |
| Vierkantrohr | O, T3, T351, T4, T42, T451 | 10–200 (side) | — | 1000–6000 |
| Dimensions can be customized to project requirements | ||||
| Temperament | Durchmesser (mm) | Min. Weight/Coil | Toleranz |
|---|---|---|---|
| O, T3, T4, T351 | 0.8–12 | 50 kg | ±0.02 mm |
| Dimensions can be customized to project requirements | |||
| Spezifikation | Bezeichnung |
|---|---|
| UNS | A92017 |
| DE | EN AW-2017 |
| ISO (AlCu4MgSi) | 2017 |
| Chinese (GB/T 3190) | 2A11 |
| Russian (GOST) | D1 |
| AA (US) | 2017 |
Per ASTM B209 / EN 573-3, the nominal composition of 2017 aluminum alloy:
| Element | Inhalt (%) |
|---|---|
| Si | 0.20–0.80 |
| Fe | 0,70 max. |
| Cu | 3.50–4.50 |
| Mn | 0.40–1.00 |
| Mg | 0.40–0.80 |
| Cr | 0,10 max |
| Zn | 0,25 max |
| Ti | 0,15 max |
| Andere, jeweils | 0,05 max |
| Sonstige, insgesamt | 0,15 max |
| Al | Bilanz |
Typical mechanical properties for 2017 aluminum alloy in common tempers (values are approximate and vary with product form and thickness; verify against mill certificates for specific orders):
| Temperament | UTS (MPa) | Yield (MPa) | Dehnung A50 (%) | Typische Verwendung |
|---|---|---|---|---|
| O | ≤220 | ≤110 | 18–22 | Cold forming, riveting |
| T3 | 380–390 | 220–245 | 12–15 | Aerospace rivets, fasteners |
| T4 | 380–390 | 220–245 | 12–15 | Structural parts, machined components |
| T351 | 370–390 | 220–245 | 12–15 | Stress-relieved plate/bar for precision machining |
| T42 | 370–390 | 215–240 | 12–15 | User-solution-treated from O temper |
| T451 | 370–390 | 215–240 | 12–15 | Stress-relieved, user heat-treated |
Choosing the right temper for 2017 depends on the balance between formability and strength your application demands:
Anmerkung: 2017 is not recommended for welding. If weldability is a priority, consider 5052 or 6061 as alternatives.
With Cu as the primary alloying element (~4%), 2017 achieves high strength in the T4 temper (UTS ~390 MPa) while maintaining good machinability. It machines readily with standard CNC tooling and produces clean chips — a practical advantage over softer alloys in high-volume machining runs.
2017 has moderate corrosion resistance — adequate for many indoor and protected structural applications, but less suitable than 5xxx or 6xxx alloys for prolonged exposure to marine or industrial atmospheres. Where corrosion is a concern, consider protective surface treatments (anodizing, painting) or switching to a 5xxx-series alloy.
In the O temper, 2017 offers good cold formability — it can be bent, headed, and riveted with standard tooling. After heat treatment (T3/T4), formability drops significantly; most forming should be completed before solution treatment.
2017 is not recommended for arc welding. The high copper content promotes hot cracking and reduces weld joint strength. Resistance welding (spot, seam) is possible with appropriate parameters. If welding is required, 5052, 5083, or 6061 are better choices.
2017 aluminum alloy is specified in industries that demand high strength from a machinable, heat-treatable material:
2017 alloy responds well to standard aluminum processing methods:
Every 2017 aluminum order from Linsy includes:
Linsy Aluminum is a Shenzhen-based factory with over 20 years of experience supplying aluminum products across the 1000–8000 series. For 2017 alloy specifically:
To discuss your 2017 aluminum requirements or request a quote, contact our sales team.
Both are 2xxx-series Cu-based alloys, but 2024 contains higher Mg (~1.5%) and achieves higher strength (~470 MPa UTS in T4). 2017 has slightly lower strength but better formability in the O temper, making it preferred for rivets and cold-headed fasteners.
2017 is not recommended for arc welding due to hot-cracking susceptibility from its high Cu content. Resistance welding (spot/seam) may be used with controlled parameters. For weldable alternatives in similar strength ranges, consider 6061-T6 or 5083.
T351 is recommended for precision-machined plate and bar — the stress-relief stretch after quenching provides dimensional stability during machining. T4 is acceptable when dimensional tolerance requirements are less stringent.
Yes. 2017 (AA/UNS designation) and 2A11 (Chinese GB/T 3190 designation) are equivalent alloys with the same nominal composition. The Russian equivalent is D1.
Mill finish, polished, anodized (darker tone than 6xxx alloys), and powder-coated. Anodizing quality is acceptable but not as bright as 6061 or 6063.
Contact our sales team for MOQ details — minimums vary by product form and temper.
Typical custom lead time is 10–60 days depending on product form, temper, and dimensions. Stock items may ship faster.
Yes. All product forms can be cut or produced to your specified dimensions. Provide your drawing or specification when requesting a quote.
Linsy operates under ISO 9001 (quality), ISO 14001 (environmental), and ISO 45001 (occupational health & safety) — an integrated management system covering all three areas.
Linsy Vorteile
Linsy Aluminum ist ein führender Anbieter von Produkten für die Aluminiumverarbeitung und beliefert verschiedene Branchen wie die Luft- und Raumfahrt, den allgemeinen Maschinenbau, die Automobilindustrie, die Schifffahrt, den Schiffbau und andere spezialisierte industrielle Anwendungen.
Wir verpflichten uns, die höchsten Qualitäts- und Umweltstandards einzuhalten, was durch unsere Zertifizierungen belegt wird: ISO 9001:2008, ISO 14001:2004 und SGS.