7021 aluminum is a high-strength, weldable 7xxx series alloy primarily alloyed with zinc and magnesium, with a copper addition for strength. It is engineered for structural applications that demand high strength, good weldability, and reasonable corrosion resistance. While not as strong as 7075, 7021 offers a better balance of weldability and strength, making it a preferred choice for welded structures in transport and aerospace. Linsy supplies 7021 as sheet, tube, bar, and wire with mill test certificates on every order.
Dostępne formularze: sheet / plate, tube, bar / rod, wire
Typowe temperamenty: T6, T651
Wsparcie w zakresie przetwarzania: Obróbka CNC, cięcie laserowe, spawanie TIG/MIG, anodowanie, polerowanie, malowanie proszkowe
Dokumenty dotyczące jakości: Raport MTC dołączany do każdego zamówienia
7021 aluminum is a high-strength, weldable 7xxx series alloy primarily alloyed with zinc and magnesium, with a copper addition for strength. It is engineered for structural applications that demand high strength, good weldability, and reasonable corrosion resistance. While not as strong as 7075, 7021 offers a better balance of weldability and strength, making it a preferred choice for welded structures in transport and aerospace. Linsy supplies 7021 as sheet, tube, bar, and wire with mill test certificates on every order.
Dostępne tempry: T6, T651
| Temperament | Grubość (mm) | Szerokość (mm) | Długość (mm) |
|---|---|---|---|
| T6, T651 | 0.5 – 150 | 500 – 2600 | 500 – 16000 (cięcie na wymiar) |
Dostępne tempry: T6, T651
| Temperament | Średnica zewnętrzna (mm) | Grubość ścianki (mm) | Długość (mm) |
|---|---|---|---|
| T6, T651 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Dostępne tempry: T6, T651
| Temperament | Średnica (mm) | Długość (mm) |
|---|---|---|
| T6, T651 | 3 – 300 | 500 – 12000 |
Dostępne tempry: T6, T651
| Średnica (mm) | Coil weight | Tolerance |
|---|---|---|
| 0.8 – 30 | Co najmniej 50 kg | ± 0,02 mm |
7021 aluminum (EN AW-7021, AlZn5.5Mg1.5) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Element | Procent (%) |
|---|---|
| Si | maks. 0,40 |
| Fe | 0,50 maks. |
| Cu | 1.2 - 2.0 |
| Mn | 0.10 – 0.40 |
| Mg | 1.2 - 1.8 |
| Cr | 0.10 – 0.25 |
| Zn | 5.0 - 6.0 |
| Ti | 0,10 maks |
| Zr | 0,10 maks |
| Inni (każdy) | 0.05 |
| Inne (łącznie) | 0.15 |
| Al | Równowaga |
| Temperament | Wytrzymałość na rozciąganie (MPa) | Granica plastyczności (MPa) | Wydłużenie (%) | Wytrzymałość na ścinanie (MPa) |
|---|---|---|---|---|
| T6 | 470 | 420 | 10 | 150 – 340 |
| T651 | 470 | 420 | 10 | 150 – 340 |
Values are typical for the indicated condition. An em dash (—) means the value was not available in the source data; confirm with the mill certificate. Asterisked values are estimates pending verification — see the audit report.
Stronger than 7020 while remaining weldable for fabricated structures.
Suitable for load-bearing welded assemblies.
Adequate for internal and coated external service.
Wydzieleniowe utwardzanie zapewnia określoną wytrzymałość.
Linsy laser-cuts and CNC-machines 7021, and welds it with qualified MIG/TIG procedures. For exterior service, anodizing or painting is recommended. Post-weld heat treatment can be discussed with our engineers to recover strength.
Linsy to dostawca aluminium z siedzibą w Shenzhen, posiadający ponad 20-letnie doświadczenie. Nasz system jakości jest certyfikowany zgodnie z normami ISO 9001, ISO 14001 i ISO 45001. Każde zamówienie jest wysyłane ze świadectwem kontroli hutniczej (MTC). Raporty z badań stron trzecich SGS są dostępne na żądanie. Typowy czas realizacji zamówienia niestandardowego wynosi 10–60 dni, w zależności od tempera, rozmiaru i ilości.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection and welding 7000-series alloys. (Internal links to be connected to published Linsy blog articles.)
7021 is stronger and still weldable, but 7020 generally has the edge in weldability and corrosion. Choose 7021 when you need more strength in a welded build.
T6 and T651 are the standard tempers. T651 reduces residual stress for machining.
Każde zamówienie jest wysyłane ze świadectwem kontroli hutniczej (MTC), a raporty z badań stron trzecich SGS są dostępne na żądanie.
Custom orders typically ship in 10–60 days depending on temper, size, and quantity.
Niestandardowe zamówienia aluminium są zazwyczaj wysyłane w ciągu 10–60 dni, w zależności od stopu, tempera, rozmiaru i ilości. Towar z magazynu lub standardowe rozmiary mogą być dostępne szybciej — zapytaj nasz zespół.
Tak. Każde zamówienie zawiera MTC. Raporty z badań stron trzecich SGS są dostępne na żądanie.
Tak. Oferujemy obróbkę CNC, cięcie laserowe, spawanie, anodowanie, polerowanie i malowanie proszkowe, dzięki czemu części mogą być dostarczone w formie bliższej gotowemu produktowi.
Prześlij swój stop, temper, wymiary, ilość i wymaganą normę. Nasz zespół potwierdzi dostępność, czas realizacji i cenę.
Zalety Linsy
Linsy Aluminium jest wiodącym dostawcą produktów do obróbki aluminium, obsługującym różne branże, w tym lotnictwo, inżynierię ogólną, motoryzację, przemysł morski, stoczniowy i inne specjalistyczne zastosowania przemysłowe.
Dążymy do utrzymania najwyższych standardów jakości i odpowiedzialności za środowisko, o czym świadczą nasze certyfikaty: ISO 9001:2008， ISO 14001:2004 oraz SGS.