7021 aluminum is a high-strength, weldable 7xxx series alloy primarily alloyed with zinc and magnesium, with a copper addition for strength. It is engineered for structural applications that demand high strength, good weldability, and reasonable corrosion resistance. While not as strong as 7075, 7021 offers a better balance of weldability and strength, making it a preferred choice for welded structures in transport and aerospace. Linsy supplies 7021 as sheet, tube, bar, and wire with mill test certificates on every order.
Formularios disponibles: sheet / plate, tube, bar / rod, wire
Temperamentos habituales: T6, T651
Asistencia técnica: Mecanizado CNC, corte por láser, soldadura TIG/MIG, anodizado, pulido, recubrimiento en polvo
Documentos de calidad: Informe MTC con cada pedido
7021 aluminum is a high-strength, weldable 7xxx series alloy primarily alloyed with zinc and magnesium, with a copper addition for strength. It is engineered for structural applications that demand high strength, good weldability, and reasonable corrosion resistance. While not as strong as 7075, 7021 offers a better balance of weldability and strength, making it a preferred choice for welded structures in transport and aerospace. Linsy supplies 7021 as sheet, tube, bar, and wire with mill test certificates on every order.
Templetes disponibles: T6, T651
| Temple | Espesor (mm) | Anchura (mm) | Longitud (mm) |
|---|---|---|---|
| T6, T651 | 0.5 – 150 | 500 – 2600 | 500 – 16000 (corte a medida) |
Templetes disponibles: T6, T651
| Temple | Diámetro exterior (mm) | Pared (mm) | Longitud (mm) |
|---|---|---|---|
| T6, T651 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
Templetes disponibles: T6, T651
| Temple | Diámetro (mm) | Longitud (mm) |
|---|---|---|
| T6, T651 | 3 – 300 | 500 – 12000 |
Templetes disponibles: T6, T651
| Diámetro (mm) | Peso de la bobina | Tolerancia |
|---|---|---|
| 0.8 – 30 | Mín. 50 kg | ± 0,02 mm |
7021 aluminum (EN AW-7021, AlZn5.5Mg1.5) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), and ASTM B313 (welded tube). Forging stock follows ASTM B247. Always confirm the exact specification and temper with our team for your order.
| Elemento | Porcentaje (%) |
|---|---|
| Si | 0.40 máx. |
| Fe | 0,50 máx. |
| Cu | 1.2 - 2.0 |
| Mn | 0.10 – 0.40 |
| Mg | 1.2 - 1.8 |
| Cr | 0.10 – 0.25 |
| Zn | 5.0 - 6.0 |
| Ti | 0,10 máx. |
| Zr | 0,10 máx. |
| Otros (cada uno) | 0.05 |
| Otros (total) | 0.15 |
| Al | Saldo |
| Temple | Resistencia a la tracción (MPa) | Límite elástico (MPa) | Alargamiento (%) | Resistencia al cizallamiento (MPa) |
|---|---|---|---|---|
| T6 | 470 | 420 | 10 | 150 – 340 |
| T651 | 470 | 420 | 10 | 150 – 340 |
Los valores son típicos para la condición indicada. Una raya (—) significa que el valor no estaba disponible en los datos de origen; confirme con el certificado de fábrica. Los valores con asterisco son estimaciones pendientes de verificación — consulte el informe de auditoría.
Stronger than 7020 while remaining weldable for fabricated structures.
Suitable for load-bearing welded assemblies.
Adequate for internal and coated external service.
Precipitation hardening delivers the specified strength.
Linsy laser-cuts and CNC-machines 7021, and welds it with qualified MIG/TIG procedures. For exterior service, anodizing or painting is recommended. Post-weld heat treatment can be discussed with our engineers to recover strength.
Linsy es un proveedor de aluminio con sede en Shenzhen con más de 20 años de experiencia. Nuestro sistema de calidad está certificado según ISO 9001, ISO 14001 e ISO 45001. Cada pedido se envía con un certificado de prueba de fábrica (MTC). Los informes de pruebas de terceros SGS están disponibles bajo solicitud. El plazo de entrega típico para pedidos personalizados es de 10 a 60 días, según el temple, tamaño y cantidad.
Para lectura más profunda sobre selección y fabricación de la serie 7xxx, consulte nuestras guías sobre selección de aleaciones de aluminio y soldadura de aleaciones de la serie 7000. (Enlaces internos que se conectarán a artículos publicados del blog de Linsy).
7021 is stronger and still weldable, but 7020 generally has the edge in weldability and corrosion. Choose 7021 when you need more strength in a welded build.
T6 and T651 are the standard tempers. T651 reduces residual stress for machining.
Cada pedido se envía con un MTC, y los informes de pruebas de terceros SGS están disponibles bajo solicitud.
Custom orders typically ship in 10–60 days depending on temper, size, and quantity.
Los pedidos personalizados de aluminio suelen enviarse en 10 a 60 días, según la aleación, temple, tamaño y cantidad. Las existencias o tamaños estándar pueden ser más rápidos — consulte a nuestro equipo.
Sí. Cada pedido incluye un MTC. Los informes de pruebas de terceros SGS están disponibles bajo solicitud.
Sí. Proporcionamos mecanizado CNC, corte por láser, soldadura, anodizado, pulido y recubrimiento en polvo para que las piezas puedan entregarse más cerca de su forma final.
Envíe su aleación, temple, dimensiones, cantidad y norma requerida. Nuestro equipo confirmará disponibilidad, plazo de entrega y precio.
Ventajas de Linsy
Linsy Aluminum es un proveedor líder de productos de procesamiento de aluminio, que presta servicio a diversas industrias, como la aeroespacial, la ingeniería general, la automoción, la marina, la construcción naval y otras aplicaciones industriales especializadas.
Nos comprometemos a mantener los más altos estándares de calidad y responsabilidad medioambiental, como demuestran nuestras certificaciones: ISO 9001:2008， ISO 14001:2004 y SGS.