7068 aluminum is an ultra-high-strength 7xxx series alloy, often cited as the strongest commercial aluminum alloy with tensile strength around 700 MPa — comparable to some soft steels. It was originally developed as a higher-strength successor to 7075 for ordnance and defense, and now serves aerospace, automotive, medical, and sporting-goods applications where strength-to-weight is critical. Linsy supplies 7068 in plate, tube, bar, and wire with mill test certificates on every order.
Formulaires disponibles : plate, tube, bar / rod, wire
Tempéraments courants : T651, T6511
Assistance technique : Usinage CNC, découpe laser, soudage TIG/MIG, anodisation, polissage, revêtement par poudre
Documents relatifs à la qualité : Rapport MTC joint à chaque commande
7068 aluminum is an ultra-high-strength 7xxx series alloy, often cited as the strongest commercial aluminum alloy with tensile strength around 700 MPa — comparable to some soft steels. It was originally developed as a higher-strength successor to 7075 for ordnance and defense, and now serves aerospace, automotive, medical, and sporting-goods applications where strength-to-weight is critical. Linsy supplies 7068 in plate, tube, bar, and wire with mill test certificates on every order.
États disponibles : T651, T6511
| Tempérer | Épaisseur (mm) | Largeur (mm) | Longueur (mm) |
|---|---|---|---|
| T651, T6511 | 0.5 – 200 | 500 – 2600 | 500 – 16000 (découpe sur mesure) |
États disponibles : T651, T6511
| Tempérer | Diamètre extérieur (mm) | Paroi (mm) | Longueur (mm) |
|---|---|---|---|
| T651, T6511 | 6 – 300 | 0.5 – 40 | 500 – 12000 |
États disponibles : T651, T6511
| Tempérer | Diamètre (mm) | Longueur (mm) |
|---|---|---|
| T651, T6511 | 3 – 300 | 500 – 12000 |
États disponibles : T651, T6511
| Diamètre (mm) | Poids de la bobine | Tolérance |
|---|---|---|
| 0.8 – 30 | 50 kg minimum | ± 0,02 mm |
7068 aluminum (EN AW-7068, AlZn8MgCu) is supplied to common wrought-alloy specifications. Typical standards by form: ASTM B209 (sheet and plate), ASTM B221 (extruded tube, bar, and profiles), ASTM B211 (bar and rod), ASTM B247 (forging stock), and ASTM B313 (welded tube). Always confirm the exact specification and temper with our team for your order.
| Élément | Pourcentage (%) |
|---|---|
| Si | 0,12 max |
| Fe | 0,15 max |
| Cu | 1.6 – 2.4 |
| Mn | 0,10 max |
| Mg | 2.2 – 3.0 |
| Cr | 0,05 max |
| Zn | 7.3 – 8.3 |
| Ti | 0,10 max |
| Zr | 0.05 – 0.15 |
| Autres (chacun) | 0.05 |
| Autres (total) | 0.15 |
| Al | Équilibre |
| Tempérer | Résistance à la traction (MPa) | Limite d'élasticité (MPa) | Élongation (%) | Résistance au cisaillement (MPa) |
|---|---|---|---|---|
| T651 / T6511 | 710 | 683 | 8 – 9 | 365 |
Values are typical for the T651 condition (~700 MPa ultimate). Confirm exact figures with the mill certificate; verify the Mn limit (AA 7068 may allow up to 0.30 max).
Ultimate tensile around 700 MPa, near some steels.
Top choice where mass must be minimized.
Better than 7075 in many service environments.
Supplied as machined or formed parts.
Linsy machines and laser-cuts 7068 and applies anodizing or painting for corrosion protection. Welding is not recommended.
Linsy est un fournisseur d'aluminium basé à Shenzhen avec plus de 20 ans d'expérience. Notre système qualité est certifié ISO 9001, ISO 14001 et ISO 45001. Chaque commande est expédiée avec un certificat d'essai en usine (MTC). Des rapports d'essais tiers SGS sont disponibles sur demande. Le délai de livraison typique pour les commandes personnalisées est de 10 à 60 jours selon l'état, les dimensions et la quantité.
For deeper reading on 7xxx selection and fabrication, see our guides on aluminum alloy selection, welding 7000-series alloys, and aircraft-grade tempers. (Internal links to be connected to published Linsy blog articles.)
Around 700 MPa ultimate tensile in T651 — the strongest of the common aluminum alloys, comparable to some soft steels.
It is stronger, with similar corrosion behavior, but less widely stocked. Choose 7068 when you need maximum strength.
No, it is a machined-part alloy.
Chaque commande est expédiée avec un MTC, et des rapports d'essais tiers SGS sont disponibles sur demande.
Les commandes d'aluminium personnalisées sont généralement expédiées sous 10 à 60 jours selon l'alliage, l'état, les dimensions et la quantité. Les tailles standard ou en stock peuvent être plus rapides — demandez à notre équipe.
Oui. Chaque commande comprend un MTC. Des rapports d'essais tiers SGS sont disponibles sur demande.
Oui. Nous fournissons l'usinage CNC, la découpe laser, le soudage, l'anodisation, le polissage et le revêtement par poudre afin que les pièces puissent être livrées plus proches de leur forme finie.
Envoyez votre alliage, état, dimensions, quantité et norme requise. Notre équipe confirmera la disponibilité, le délai de livraison et le prix.
Avantages pour Linsy
Linsy Aluminum est un fournisseur de premier plan de produits de transformation de l'aluminium, au service de diverses industries, notamment l'aérospatiale, l'ingénierie générale, l'automobile, la marine, la construction navale et d'autres applications industrielles spécialisées.
Nous nous engageons à respecter les normes les plus strictes en matière de qualité et de responsabilité environnementale, comme en témoignent nos certifications : ISO 9001:2008， ISO 14001:2004 et SGS.