Stop aluminium 6101 (EN AW-6101) is a 6000-series, high-conductivity grade used for bus bars, electrical conductors, and power-distribution components. It combines good electrical performance with light weight, formability, and corrosion resistance, and is supplied as sheet, bar, tube, wire, and profile in O/T6/T61/T64/T65 tempers. Linsy provides 6101 with made-to-order sizes and an MTC on every order.
Dostępne formularze: blacha / zwój / pręt / rura / drut / profil
Typowe temperamenty: O / T6 / T61 / T64 / T65
Wsparcie w zakresie przetwarzania: CNC machining / bending / welding / cutting
Dokumenty dotyczące jakości: Raport MTC dołączany do każdego zamówienia
6101 (EN AW-6101) is a 6000-series aluminum alloy with magnesium and silicon, developed for high electrical conductivity while retaining useful strength and formability. It is a primary choice for bus bars, electrical conductors, and power-distribution components where weight savings and corrosion resistance matter.
Compared with general structural grades, 6101 is optimized for current-carrying performance, making it common in switchgear, rail traction, and automotive electrical systems.
| Formularz | Typowe temperamenty | Typowy zakres wymiarów |
|---|---|---|
| Blacha i krąg | T6, T61, T64, T65 | Grubość 0,5–150 mm; Szerokość 500–2600 mm; Długość 500–12000 mm |
| Pręt (okrągły / kwadratowy / płaski) | T6, T61, T64, T65 | Średnica/bok 6–400 mm; Długość 1000–6000 mm |
| Rura (okrągła / kwadratowa) | T6, T61, T64, T65 | Średnica zewnętrzna 10–400 mm; Grubość ścianki 1–40 mm; Długość 1000–6000 mm |
| Drut | T6, T61, T64, T65 | 0,8–30 mm |
| Profil / Wyciskanie | T6, T61 | Zgodnie z rysunkiem klienta |
Used for bus-bar strip and formed conductive parts in T6/T61/T64/T65.
Round, square, and flat bars for machined conductive components and connectors.
Tubes for bus-duct and structural-conductive assemblies.
Drawn wire for stranded conductors and welded assemblies.
Extruded profiles to drawing, commonly for bus-bar and rail applications.
| Oznaczenie | Wartość |
|---|---|
| EN AW | EN AW-6101 (AlMg0.6Si / AlMg0.6SiCu) |
| UNS | A96101 |
| Typowe stany | O, T6, T61, T64, T65 |
| Kluczowa właściwość | High electrical conductivity |
| Normy | ASTM B211, ASTM B221, EN 755, GB/T 3190 |
| Element | Skład (% wag.) |
|---|---|
| Si | 0.30 – 0.70 |
| Fe | 0,50 maks. |
| Cu | 0,10 maks |
| Mn | 0,10 maks |
| Mg | 0.35 – 0.80 |
| Cr | 0,10 maks |
| Zn | 0,10 maks |
| Ti | 0,10 maks |
| Inni (każdy) | 0.05 max |
| Inne (łącznie) | 0,15 maks |
| Al | Reszta |
Typical reference values; confirm against the ordered standard and Linsy’s mill data.
| Temperament | Wytrzymałość na rozciąganie (MPa) | Granica plastyczności (MPa) | Wydłużenie (%, min.) |
|---|---|---|---|
| O | 90 | 55 | 20 |
| T6 | 220 | 180 | 12 |
| T61 | 230 | 190 | 10 |
The defining property of 6101 — suitable for bus bars and conductors where weight and corrosion resistance are priorities.
Readily formed and weldable; joints should be designed considering local conductivity changes.
Good in most atmospheric and indoor electrical environments.
6101 machines well in the soft (O) and solution-heat-treated tempers; T6/T651 tempers are stronger and can work-harden at the cutting edge, so sharp tooling and appropriate feeds are recommended.
6101 is generally weldable using TIG or MIG processes with matching or 4043/5356 filler, depending on the service requirement. Welded zones lose some strength compared with the base temper — design accordingly for structural use.
Stop 6111 dobrze poddaje się obróbce skrawaniem w stanach miękkim (O) i po przesycaniu; stany T6/T651 są twardsze i mogą ulegać umocnieniu na krawędzi skrawającej, dlatego zaleca się stosowanie ostrych narzędzi i odpowiednich posuwów.
Spawanie.
Every 6101 order ships with an MTC reporting composition and properties. Conductivity testing can be arranged on request. Confirm the required standard (ASTM, EN, GB) when ordering.
Formowanie najlepiej wykonywać w stanie O lub T4. Ostateczna wytrzymałość jest uzyskiwana w określonym stanie; nie przeprowadzać ponownej obróbki cieplnej bez potwierdzenia reakcji stopu.
Mainly high-conductivity electrical applications such as bus bars, conductors, and welded electrical assemblies.
6101 is tuned for electrical conductivity, while 6061 is a more general structural alloy with higher strength.
O, T6, T61, T64, and T65, depending on the conductivity/strength balance required.
Standardowe pozycje magazynowe są zwykle wysyłane w ciągu 10–30 dni. Wymiary niestandardowe, stany lub wykończenia powierzchni zazwyczaj wymagają 30–60 dni, w zależności od specyfikacji i wielkości zamówienia.
Tak. Każde zamówienie jest wysyłane z MTC raportującym skład chemiczny i właściwości mechaniczne zgodnie z zamówioną normą.
Tak. Dostarczamy standardowe i wykonywane na wymiar wymiary dla blach, płyt, prętów, rur i profili, a na życzenie możemy zorganizować określone stany.
Działania są zgodne z ISO 9001, ISO 14001 oraz ISO 45001. Materiał może być dostarczany zgodnie ze specyfikacjami ASTM, EN, GB lub JIS na żądanie.
Stosowane jest standardowe opakowanie eksportowe przystosowane do transportu morskiego z zabezpieczeniem przed wilgocią; szczegółowe wymagania są potwierdzane przy zamówieniu.
Zalety Linsy
Linsy Aluminium jest wiodącym dostawcą produktów do obróbki aluminium, obsługującym różne branże, w tym lotnictwo, inżynierię ogólną, motoryzację, przemysł morski, stoczniowy i inne specjalistyczne zastosowania przemysłowe.
Dążymy do utrzymania najwyższych standardów jakości i odpowiedzialności za środowisko, o czym świadczą nasze certyfikaty: ISO 9001:2008， ISO 14001:2004 oraz SGS.